Single-walled carbon nanotubes (SWNT) and carbon nitride films are synthesized by a direct current (dc) arc discharge at slightly reduced pressure and by an inductively coupled r.f. plasma (ICP) at atmospheric pressure, respectively. By treatment with nitric acid SWNT are purified from by-products and characterized by scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), and Raman spectroscopy. ICP allows the deposition of carbon nitride films on steel substrate. The deposition of the films creates a relatively strong radial symmetric profile. The structure of the films are rather independent of the distance between substrate and plasma. Raman, Fourier transform infrared (FTIR), and energy dispersive X-ray (EDX) spectroscopy are used for analyzing the carbon nitride materials.
Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.
In this work we present the preparation of conductive polyethylene/carbon nanotube composites based on the segregated network concept. Attention has been focused on the effect of decreasing the amount of filler necessary to achieve low resistivity. Using high- and low-grade single-walled carbon nanotube materials we obtained conductive composites with a low percolation threshold of 0.5 wt.% for high-grade nanotubes, about 1 wt% for commercial nanotubes and 1.5 wt% for low-grade material. The higher percolation threshold for low-grade material is related to low effectiveness of other carbon fractions in the network formation. The electrical conductivity was measured as a function of the single-walled carbon nanotubes content in the polymer matrix and as a function of temperature. It was also found that processing parameters significantly influenced the electrical conductivity of the composites. Raman spectroscopy was applied to study single wall nanotubes in the conductive composites.
In 1996, R. T. K. Baker, and N. M. Rodriguez claimed to have synthesized a new type of carbon nanofiber material capable of storing large amounts of hydrogen at room temperature and pressures above 100 bar, thus making it a powerful candidate for a very efficient energy storage system in mobile applications. Consequently, many scientists all over the world tried to test and verify these findings, however, with partly inconsistent results. We present here for the first time independent hydrogen storage measurements for several types of nanofibers, both synthesized by our group following precisely the specifications given in the literature as well as original samples supplied by Rodriguez and Baker for this study. The hydrogen storage capacities at room temperature and pressures up to 140 bar were quantified independently by gravimetric and volumetric methods, respectively. No significant hydrogen storage capacity has been detected for all carbon nanofibers investigated.
We have developed a very fast and entirely gas-phase based purification technique for carbon nanotubes (CNT) that allows removing metal and metal oxide impurities with high effectiveness. CNT agglomerates from chemical vapor deposition (CVD) synthesis which contained carbon encapsulated catalysts were injected into an atmospheric plasma torch. Very high heating rates allow for quasi-instantaneous vaporization of catalyst particles. This way, metal vapors are hyposized to break mechanically instable encapsulations and effuse from incomplete ones faster than thermally induced graphitization stabilizes such particle encapsulations. The ash content of multi-walled (MW) CNT samples was reduced to less than 15% of the initial value within a few milliseconds. Also the metal content of single-walled (SW) CNT agglomerates was significantly reduced. Repeated injection of CNT agglomerates into the plasma torch resulted in higher-purity products of improved structural integrity and increased oxidation resistance.