Slow burst testing of samples as a method for quantification of composite cylinder degradation
(2014)
The current practise to focus periodic retesting of composite cylinders primarily on the hydraulic pressure test has to be evaluated as critical. The test itself always causes a certain amount of micro damage to the cylinders but does not necessarily deliver sufficient and evaluable information. Thus BAM Federal Institute of Materials Research and Testing (Germany) moves the focal point to a new approach for validation of composite cylinders, based on destructive sample tests parallel to operation. Statistical assessment of results of these destructive tests is employed for the estimation of remaining safe service life, based on reliability demands. The estimated service life is also used for the determination of re-test periods of the examined population of composite cylinders.
An essential aspect of this approach is the validation of current residual strength and its prediction at any point of service life. In cases of gas cylinders with very high cycle strength, residual strength cannot be quantified statistically by means of hydraulic load cycles. As a replacement, creep tests or burst tests may be employed. BAM suggests the 'slow burst test SBT' as a combination of these two test procedures. This is a compromise between the practicability of the (conventional) burst test and the practical relevance of sustained loads during service, to be tested in creep rupture tests. In this paper, a variety of 99 burst results of a cylinder design type used for breathing apparatus (CFRP with PE-liner) is evaluated. The influence of test procedure parameters and nature and intensity of artificial ageing on the test sample strength are analysed statistically. This leads to an evaluation of different procedures of artificial ageing and the recommendation to substitute conventional burst tests by slow burst tests for the assessment of composite pressure receptacles.
Featuring a detailed analysis of current approval requirements and the relevant safety assessment methods for gas cylinders in general and with main focus on composite cylinders for storing ompressed natural gas and hydrogen, this book demonstrates how current regulations and standards limit the ability to reduce cost and weight. Based on this data, it then highlights the potential offered by the proposed approval procedure based on probabilistic safety assessment.
After addressing the economic potential of probabilistic safety assessments, the book details working procedures and improving cycles and (slow) bursts as methods for assessing residual strength. It then discusses methods for statistically evaluating test data, as well as sample- size and distribution character considerations. A definition of sample strength is elaborated in terms of the performance sheets developed by the author. On this basis, it discusses safety as a property of service life and interpreted as an issue of degradation, and explores aspects of artificial aging for simulating the end-of-life reliability level. Lastly, the book considers control and inspection aspects: quality of production, degradation prediction using destructive sample tests parallel to operation, retesting periods and correcting for underand overestimates of safe lifetime.
Presented in schematic diagrams, illustrations and tables, this information enables manufacturers and operators to use this new approach in practice and supports the improvement of current regulations and standards.
Gas cylinders made of composite materials receive growing popularity in light-weight applications. Current standards are mostly based on safety determination relying on minimum amounts of endured load cycles and a minimum burst pressure of a small number of specimens. This paper investigates the possibilities of a probabilistic strength assessment for safety improvements as well as cost and weight savings. The probabilistic assessment is based on destructive testing of small sized samples. The influence of sample size on uncertainty of the assessment is analysed. Furthermore, methods for the assessment of in-service ageing (degradation) are discussed and displayed in performance charts.
The set of slides summarises the expectations of participants discussed during the opening session. Then the most important aspects of the presentations during the first two days are compiled. At the end the conclusions coming out of a joint discussion are presented. This show what participants expect BAM to do for implementation of the PA in near future.
The presentation shows the basics on the graphic comparison of deterministic regulations and probabilistic safety requirements. In doing so, unsafe but approvable areas in the BAM-SPC (sample performance chart) becomes obvious; as the area of not approveable but safe strength properties does.
Finally the semi-porbabilistic approach of GTR#13 (global technical regulation for hydrogen vehicles) is analysed. Relevant figures show again potential of saving material and unsafe areas in case of high scatter at end of life.
Degradation and damage analysis of composite pressure vessels via experimental modal analysis
(2023)
For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests.
Hydrogen is an attractive energy carrier that requires high effort for safe storage. For ensuring safety, storage cylinders must undergo a challenging approval process. Relevant standards and regulations for composite cylinders used for the transport of hydrogen and for its onboard storage are currently based on deterministic (e.g. ISO 11119-3) or to some respect semi-probabilistic criteria (UN GTR No. 13; with respect to burst strength).
This paper provides a systematic analysis of the load cycle properties resulting from these regulations and standards. Their characteristics are compared with the probabilistic approach of the Federal Institute for Materials Research and Testing BAM. The most important aspect of comparing different concepts is the rate for accepting designs with potentially unsafe or critical safety properties. This acceptance rate is analysed by operating Monte-Carlo simulations over the available range of production properties.
This presentation provides the main issue of a probabilistic based safety assessment.
It shows the differences in terms of survival rate between some current deterministic standards and the probabilistic approach.
It deals with three test procedures: slow burst test, cycle test and fire engulfment test.
This presentation shows the most important steps for developing the probabilistic approach PA with a lot of detailed information on test results. It discusses the necessitiy of performing a slow burst test, to which amount degradation can be accepted and how these interacts with aspects of costs etc.