Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (43)
- Beitrag zu einem Tagungsband (27)
- Zeitschriftenartikel (20)
- Posterpräsentation (8)
- Beitrag zu einem Sammelband (3)
- Monografie (1)
Sprache
- Englisch (102) (entfernen)
Schlagworte
- Degradation (12)
- Residual strength (10)
- Slow burst test (10)
- Regulations (9)
- Acceptance rate (8)
- Composite (8)
- Hydrogen (8)
- Sample testing (8)
- Composite cylinders (7)
- Probabilistic (7)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (34)
- 3.0 Abteilungsleitung und andere (18)
- 3.5 Sicherheit von Gasspeichern (16)
- 5 Werkstofftechnik (3)
- 5.5 Materialmodellierung (3)
- 8 Zerstörungsfreie Prüfung (3)
- 8.6 Faseroptische Sensorik (2)
- 2 Prozess- und Anlagensicherheit (1)
- 2.1 Sicherheit von Energieträgern (1)
- 3.3 Sicherheit von Transportbehältern (1)
Eingeladener Vortrag
- nein (43)
Storage
(2018)
The whole conference focused on gaps in research concerning hydrogen and hydrogen safety. This presentation focus on storage aspects and shows the current gaps in research from the point of view of the authors. They have differences in background, from university via manufacturer and safety institute to hydrogen operating industry. The different purposes of storage are covered (onboard storage, stationary storage and transport of gases) as well as the different designs (steel to pure composite/plastic).
Existing standards for the approval of composite cylinders for the transport of compressed hydrogen are currently based on deterministic (ISO 11119-3) and semi-probabilistic (UN GTR No. 13) criteria. This paper analysis the capabilities of these procedures with respect to the evaluation of burst strength. Their characteristics are compared with the probabilistic approach developed at BAM. Based on Monte-Carlo simulations the available design range (mean value and scatter of burst strength) of all concepts are assessed. In addition, the probability of acceptance for potentially unsafe design types is determined.
The results show large areas of burst properties with a sufficient reliability which cannot be used for the design of composite cylinders, due to current approval criteria. On the other hand, existing standards allow the approval of potentially unsafe designs in case of a very high scatter regarding their burst strength.
It is also shown that existing design types are already designed to the limits of the available design area. A further weight and cost reduction of composite cylinders is therefore closely related to the approval criteria. An example based on UN GTR No. 13 shows how an approval criterion can be optimized by using statistical methods. The example shows that a reduced minimum burst pressure can be combined with a lower probability of acceptance for potentially unsafe design types.
The increasing amount of composite transport systems for hydrogen leads to new and therefore unknown potential hazards for general public. Due to lack of experience, risks of new technologies tend to be rated higher than existing familiar applications. An approach for probabilistic safety assessment of technologies or products requires the definition of minimal acceptable reliability levels. This ensures that the probability of a critical failure with a certain consequence is limited to an acceptable risk. But what is the acceptable risk and which risk results from specific probabilities of occurrence and consequences? This is always a very complex question. The following example is based on a probabilistic approach for safety assessment of composite cylinders developed at the BAM (Federal Institute for Materials Research and Testing).
The explosion of hydrogen gas storage cylinders on May 25, 1894, represents one of the most spectacular failure cases during the late industrialization period in Germany. With respect to modern applications to hydrogen storage as energy carrier, it has several times been referred to as precedent failure case for the whole industrial sector. The detailed investigation reports by Martens have thus gained interest in the last years, but also, because the publications in 1896 about his expertise already provided in September 1894 document one of the first and most comprehensive investigations which can be regarded as a nucleus for modern failure analysis.
After summarizing the newspaper reports in the introduction, the present contribution provides a review of Martens' reports targeted at the development of failure analyses and materials testing procedures as well as potential failure origins.
The strength of unidirectional elastic fibre composites is shown to depend on the loading rate as the viscoelastic nature of the matrix results in a fall in breaking load as the rate is reduced. The simulation of the accumulation of fibre breaks leading to failure, takes into account all physical phenomena involved fibre failure, including the stochastic nature of fibre strength, stress transfer through the matrix between reinforcements, interfacial debonding and the viscoelastic nature of the matrix. The kinetics of composite failure are seen to involve the initial formation of random fibre breaks which at higher loads coalesce into clusters of broken fibres. The rate at which this occurs depends on the viscoelastic properties of the matrix. These results have been shown to closely mirror the behaviour of carbon fibre composite pressure vessels.
Current standards governing the design, qualification and in-service inspection of carbon fibre composite cylinders do not facilitate to optimise cylinder design. The requirements have been adapted from standards for metallic cylinders and cannot easily quantify the degradation processes in composite materials. In this article, the results of hydraulic and hydrogen pressure cycle life tests performed on composite reinforced tanks with a metal liner (type 3) and with a high density polymer liner (type 4) are shown. Moreover, the degradation measured by means of residual strength of the tanks after the cycling tests have been compared. It has been found that the most critical aging for metal based composite cylinder is the gaseous cycling while type 4 designs seem to be more sensitive to hydraulic cycling at high temperature.
Fibre-reinforced plastics (FRP) especially carbon-fibre-reinforced polymer (CFRP) and glass-fibre-reinforced polymer (GFRP) are commonly used materials in high pressure vessels and storage units for automotive and aerospace purposes. Optical fibres are suitable to be integrated or directly applied to the surface of FRP components. Using optical fibres it is possible to monitor the distributed strain profiles and changes within the fatigue life of a pressure vessel to ensure the operational safety. Within artificial ageing experiments we used swept wavelength interferometry (SWI) based distributed strain sensing for the monitoring of commercial high-pressure composite cylinder. This artificial ageing was performed using test conditions of 503bar pressure load (service pressure 300 bar) and 89 °C for 100 h. The polyimide coated optical fibres were glued to the surface externally in circumferential and axial direction. Using distributed strain sensing (DSS) material expansion of over 0.5% were monitored with sub-centimetre spatial resolution. Within the circumferential direction we observed up to 10 % local fluctuation compared to the median strain caused by inhomogeneous material expansion, which could cause local material fatigue. In addition, we determined material degradation manifested itself as localized remaining material expansion and/or contraction. Results have been validated by other non-destructive methods like digital strip projection.
Degradation and damage analysis of composite pressure vessels via experimental modal analysis
(2023)
For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests.
Due to high specific stiffness a nd strength properties, fibre reinforced plastics are used more and more often for the construction of pressure vessels. Within a recent research project run by the Federal Institute for Materials Research and Testing (BAM), aging process of composite pressure vessels is investigated in order to be able to give more accurate lifetime predictions in the future. Focus is set on type III pressure vessels consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. In order to increase high-cycle fatigue, residual stresses are induced into the pressure vessel during manufacturing process. In particular, residual compressive stresses within the inner aluminium layer have been defined as a main parameter affecting fatigue strength. The aim is to identify and evaluate residual stresses of the pressure vessel by analysing its modal parameters. Through the set-up of a finite-element model potential capability and validity for the use of modal analysis is proven and evaluated, considering influences resulting from manufacturing deviations, too. In the following, a number of stress sensitive modes are defined. Based on these preliminary numerical investigations, a test bench is set up in order to measure pressure vessels via an experimental modal analysis. A final critical evaluation regarding the accuracy of the modal analysis is made by comparing experimental results with data obtained through simulations.