Systematic errors in the evaluation of uncorrected data from thermographic lock-in measurements
(2018)
Lock-in thermography (LT) is based on the correct evaluation of phase differences between the temperature oscillations at different surface regions of the object under test during periodic heating. Since the usual heating procedures contain a DC component, the actual heating pattern achieved is not harmonic. This causes systematic deviations when phase differences are determined by means of harmonic analysis, e.g. with FFT analysis. The resulting errors depend clearly on the ratio between DC and AC amplitude, which is demonstrated at simulated and experimentally recorded temperature transients. Further experimental LT data obtained by different oscillating energy inputs showed a variety of possible shapes of transients with different DC components.
Quantification of impact damages in CFRP and GFRP structures with thermography and ultrasonics
(2018)
The extent of damage caused by impacts in fibre reinforced composites depends on the energy of the impacts, on the velocity and the shape of the impacting body, on the material and structure of the composite and on the geometry of the structure. Here, mainly the thickness of the component is essential. The non-destructive evaluation of these damages can be carried out using both ultrasound and active thermography methods. A comparison of the detection sensitivity of these methods for the different damages is carried out in this paper depending on the fibre composite material used (CFRP and GFRP), the thickness of the material and the impact energy. The NDT methods used after the damage are supplemented by thermographic measurements with high temporal resolution, which were already recorded during the impact.
Low-velocity impact damages were monitored in-situ using an infrared camera before, during and after Impact load. Thermal images were recorded as a function of time at the front side (impact) as well as at the rear side of the plates using a high frame rate. In CFRP and GFRP specimens with different thicknesses and made of various types of fibers and matrix materials, different kind of damages were observed. The sizes of the heated areas being related to the damages and the amount of energy dissipated into heat was determined quantitatively as a function of impact energy and are a measure of the resistance of the different materials against impact load.