Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (52)
- Vortrag (18)
- Beitrag zu einem Tagungsband (10)
- Monografie (2)
- Beitrag zu einem Sammelband (2)
- Buchkapitel (1)
Sprache
- Englisch (85) (entfernen)
Schlagworte
- Fatigue strength (17)
- Fracture mechanics (16)
- Cyclic R-curve (11)
- Weldments (11)
- Fatigue crack propagation threshold (8)
- Short cracks (8)
- Additive Manufacturing (7)
- Additive manufacturing (6)
- Fatigue (6)
- Crack propagation (5)
Organisationseinheit der BAM
- 9 Komponentensicherheit (57)
- 9.4 Integrität von Schweißverbindungen (56)
- 8 Zerstörungsfreie Prüfung (10)
- 8.5 Röntgenbildgebung (10)
- 9.6 Additive Fertigung metallischer Komponenten (6)
- 5 Werkstofftechnik (5)
- 9.0 Abteilungsleitung und andere (5)
- 5.1 Mikrostruktur Design und Degradation (4)
- 5.5 Materialmodellierung (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (18)
An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens.
The net section limit load FY is a key input parameter for the accuracy of any
elastic-plastic flaw assessment procedure of the R6 type. Unfortunately available limit load
solutions are of variable quality since they have been obtained over decades by different
methods. As a consequence the results of the fracture analyses such as the critical load or
crack size are limited in their accuracy and are often significantly conservative. A further
problem is that common limit load solutions based on ligament yielding are inadequate in a
number of cases even for through crack configurations and should be replaced by some
kind of local yielding solutions. In the present paper a simple and straightforward reference
load definition is proposed instead of the limit load which strictly corresponds to a ligament
yielding parameter Lr = 1 in the R6 Routine and similar approaches such as SINTAP and
FITNET. This can be determined by finite element simulation for any geometry. In addition to
a previous study on thin wall notched plates the method is applied to plates containing
shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a
suitable extension and improvement of the existing methods.
The net section limit load FY necessary for assessment at static loading is a key input for the accuracy of any elasticplastic flaw assessment procedure of the R6 type. Unfortunately available limit load solutions are of variable quality since they have been obtained over decades by different methods. As a consequence the results of the fracture analyses such as the critical load or crack size are limited in their accuracy and are often significantly conservative. Further, common limit load solutions based on ligament yielding are inadequate in a number of cases even for through crack configurations and should be replaced by some kind of local yielding solutions. In the present paper a simple and straightforward reference load definition is proposed instead of the limit load which strictly corresponds to a ligament yielding parameter Lr = 1 in the R6 Routine and similar approaches such as the European SINTAP and FITNET methods. This can be determined by finite element simulation for any geometry. In addition to a previous study on thin wall notched plates the method is applied to plates containing shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a suitable extension and improvement of the existing methods.
The life extension of a component in service is of great importance in many engineering applications and it relies on the possibility of monitoring the material degradation during in-service loading. In this view, non-destructive testing is needed in order to be able to evaluate the material properties while keeping the component in service.
The present work focuses on a miniature mechanical test named small punch test, which has been employed on virgin and aged 1CrMoV steel in order to characterise its mechanical behaviour. A thorough experimental analysis has been carried out using classical and miniature mechanical tests and the results have been compared in order to evaluate the feasibility of the small punch test to the characterisation of an aged steel.
A numerical framework based on finite element simulations is also presented to support the findings of the experimental tests. Starting from the simulation of a typical load–displacement curve given by the small punch test, the elastic–plastic parameters have been identified and applied in the simulation of the tensile tests.
Experimental results and non-uniqueness of the mathematical problem associated to the identification of the material parameters are discussed.
Rotor disks for gas turbines are heavy components and are usually designed following a safe-life approach, where the low-cycle fatigue analysis is carried out referring to design life curves with suitable probabilistic margins. However, in the case of such a heavy component there is the possibility of rare occurrence of undetected defects or, better, the need to identify the defect acceptability for the different rotor regions (considering stress, temperature, mission profile).In order to carry out such calculations for a turbine rotor disk a software named AStrID (Assessment of the Structural Integrity of Disks) has been developed in close cooperation between Politecnico di Milano and Ansaldo Energia (AEN). This paper summarizes its background and some of the relevant features.
Design methodology of vessel produced by L PBF stainless steel using representative specimens
(2022)
This work presents the preliminary results of an ongoing project with a double objective: on the one hand, the characterisation of the mechanical properties against fatigue damage of an additively manufactured 316 stainless steel produced by laser powder bed-based (L-PBF) technology; on the other hand, the implementation of numerical simulation techniques able to predict the mechanical behaviour of the material in order to optimise and reduce the design costs of vessels used in the chemical sector. The current state of the work developed in this research framework allows showing the first batch of experimental results of crack propagation rate (FCGR) and high cycle fatigue (HCF) tests. The geometry of the vessels studied presents three clearly differentiated regions, either in terms of thickness (11-15 mm) or concerning the inclination of the walls to the direction of manufacturing (0º - 45º). The experimental campaign carried out so far allows identifying the differences in behaviour when comparing different extraction locations around the vessel. This is due to the variations in thermal cycles that the deposited material undergoes during the manufacturing process. Therefore, this causes variations in the microstructure which lead to changes in the response of the material. In this work, these differences are analysed qualitatively and quantitatively from the results of FCGR and HCF, thus allowing to locate the regions with the highest risk in terms of structural integrity against fatigue. This preliminary phase together with the numerical simulation of the additive manufacturing process are key to achieving a reliable description and modelling of the material. The latter will make it possible to address the priority aim of this project, involving the manufacture of independent samples whose properties are representative of the original material extracted from the reference vessels. It is, therefore, a comprehensive methodology for the design of additively manufactured components based on the localised fatigue mechanical properties of representative specimens.
The robust determination of the threshold against fatigue crack propagation DKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of DKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic DK– da/dN test data to calculate DKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating DKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density.
The largest percentage of component life under fatigue loading conditions is spent in the short crack regime and in the initial phase of long cracks. The use of Fracture Mechanics in the characterization of fatigue crack growth rate curves has proven to be a useful and adequate tool in the prediction of fatigue lifetimes as long as certain conditions are satisfied. All the above implies the need for a methodical and accurate procedure of assessment of the material response in order to achieve a reliable prediction of lifetime in components under safe conditions, based on the damage tolerance approach. It also highlights the need to analyse the response of increasingly reduced thicknesses, which, as time goes by, show greater differences with respect to those commonly studied and defined in standards and design guidelines, as well as to the experimental studies that can be found in the literature at present. Some examples of thin-walled components are turbine blades or certain additively manufactured parts where, additionally, variations in material properties can occur locally and should also be examined.