- Baustoffe (2)
- Earth construction (2)
- Einpressmörtel (2)
- Grout mortar (2)
- Historical buildings (2)
- Historische Bauwerke (2)
- Hydraulic lime (2)
- Instandsetzung (2)
- Kalkhydrat (2)
- Lehmbau (2)
The purpose of this paper is to numerically simulate the in-plane behaviour of rammed earth walls under cyclic shear-compression tests. The experimental testing allowed obtaining the maximum horizontal loads, the displacement capacity and the level of non-linear behaviour of the respective loaddisplacement relationships as well as the failure modes. The calibration of the numerical model (finite element method) was carried out based on the experimental results. Within this framework, a micromodelling approach was considered. The behaviour of the rammed earth material was simulated using a total strain rotating crack model. A Mohr-Coulomb failure criterion was used to reproduce the behaviour of the interfaces between the layers.
Although the numerical results achieved a satisfactory agreement with the experimental results a sensitivity analysis of the parameters involved was performed. The sensitivity analysis aimed at determining which parameters of the model have a significant impact in the model’s results. As expected the sensitivity analysis pointed out that the sliding failure occurrence is mainly influenced by two parameters of the interface elements: the interface tensile strength fit and the friction angle u. Moreover the cohesion c and the layers thickness showed a limited effect on the shear behaviour. It should be noted that the results mentioned above are related to the cases where a significant level of vertical compressive stress r is employed.
The study presents the results from the development of a grouting material based on hydrated lime with addition of pozzolana, which is referred to as hydraulic lime, suitable for the repair of cracks in a variety of earthen building techniques. The goal was to develop a material also compatible with earthen structures exposed to dynamic loads. The grouting mortar was designed to be adaptable in strength properties and at the same time to have sufficient robustness for preparation and use on the construction site.
Results showed a satisfactory performance of the grout concerning fresh and hardened mortar properties as well as injectability.
Die Instandsetzung von Lehmbauwerken ist keine einfache Aufgabe. Der Baustoff Lehm hat vergleichsweise schwache mechanische Eigenschaften. Er ist außerdem anfällig gegenüber eindringendem Wasser, wobei er sehr schnell seinen Zusammenhalt verlieren kann, wenn gewisse Feuchtegehalte überschritten werden. Instandsetzungskonzepte für Bauwerke aus solchen Materialien stellen deshalb eine Herausforderung dar. Historische Lehmbauwerke zeigen oft Schäden in Form von starker Rissbildung, die durch statische oder dynamische Lasten hervorgerufen sein kann. Häufig werden solche Risse wegen mangelnder Fachkenntnis und / oder fehlender Techniken nur ungenügend instandgesetzt. Die Rissinstandsetzung mit Einpressmörteln birgt insbesondere für Lehmbaustoffe eine Herausforderung und erfordert spezifische Anforderungen an den Einpressmörtel, wie z. B. niedriger Wassergehalt, gutes Wasserrückhaltevermögen, niedriges Schwindmaß, an das instandzusetzende Material angepasste Festigkeit und E-Modul sowie eine gute Haftung am Lehmuntergrund. Zusätzlich müssen Einpressmörtel eine ausreichende Fließfähigkeit aufweisen, um kleine Risse und Hohlräume ohne Entmischung zu füllen. Deshalb muss das rheologische Verhalten des Einpressmörtels gut untersucht und kontrolliert werden, um die gewünschte Wirkung zu erzielen. Die Rissinstandsetzung bei Lehmbauwerken erfolgt traditionell durch manuelles Stopfen mit einem Mörtel. Natürlich können auf diese Weise nur Risse mit einer großen Breite verfüllt werden. Ein weiterer Nachteil ist, dass Risse, die durch dickere Wände verlaufen, nicht vollständig mit den für das Stopfen verwendeten Werkzeugen erreicht werden können. Kalkgebundene Einpressmörtel für Lehmbaustoffe werden gewöhnlich für die Wiederbefestigung von Putzen und weniger aus statisch-konstruktiven Gründen eingesetzt.
Aufgrund der Eigenschaften von Lehm, müssen Einpressmörtel auf Basis von hydraulischem Kalk nach EN 459-1 [4] wesentliche Anforderungen an eine Reihe von Eigenschaften erfüllen, die sich auf die Verträglichkeit, die Dauerhaftigkeit und insbesondere die Injektionsfähigkeit beziehen. Das Ziel der vorgestellten Untersuchungen war einen Einpressmörtel zu herzustellen, mit dem die strukturelle Kontinuität in Lehmmauerwerk oder anderen massiven Lehmwänden (Stampf- und Wellerlehm) durch Rissverpressung wiederhergestellt werden kann. Das Material bestand aus Kalkhydrat mit Zusätzen von Puzzolanen und Kalksteinfüller.
In-plane shear behaviour of earthen materials panels strengthened with polyester fabric strips
(2016)
An experimental investigation was carried out to study the in-plane shear behaviour of earthen material Panels strengthened with polyester fabric strips. Strengthened panels were developed to exploit the strength potential of earthen materials and to solve its lack of tensile strength, significantly improving not only strength but also ductility. Three earthen materials were considered: cob, earth block masonry (EBM) and rammed earth (RE). As first approach the strengthening configuration, based on different adhesive materials, was tested only for cob panels. As part of the study the results of a big testing campaign of unstrengthened Panels were considered. Seven strengthened panels were tested in diagonal compression/shear.A unique reinforcement orientation was used. The results of these tests are presented in this paper, and include the load-displacement behaviours, crack patterns, failure modes. The results showed that the reinforcement was the most effective in EBM panels, with increase in strength and ductility observed. In RE and cob panels the reinforcement did not likely contribute significantly to the shear resistance, due to a lack of embedment length of the strips. Instead, in EBM it was likely that the vertical reinforcement acted in tension to restrain shear induced dilation and to restrain sliding.
Die Instandsetzung von Lehmbauwerken ist keine einfache Aufgabe. Der Baustoff Lehm hat vergleichsweise schwache mechanische Eigenschaften. Er ist außerdem anfällig gegenüber eindringendem Wasser, wobei er sehr schnell seinen Zusammenhalt verlieren kann, wenn gewisse Feuchtegehalte überschritten werden. Instandsetzungskonzepte für Bauwerke aus solchen Materialien stellen deshalb eine Herausforderung dar. Historische Lehmbauwerke zeigen oft Schäden in Form von starker Rissbildung, die durch statische oder dynamische Lasten hervorgerufen sein kann. Häufig werden solche Risse wegen mangelnder Fachkenntnis und / oder fehlender Techniken nur ungenügend instandgesetzt. Die Rissinstandsetzung mit Einpressmörteln birgt insbesondere für Lehmbaustoffe eine Herausforderung und erfordert spezifische Anforderungen an den Einpressmörtel, wie z. B. niedriger Wassergehalt, gutes Wasserrückhaltevermögen, niedriges Schwindmaß, an das instandzusetzende Material angepasste Festigkeit und E-Modul sowie eine gute Haftung am Lehmuntergrund. Zusätzlich müssen Einpressmörtel eine ausreichende Fließfähigkeit aufweisen, um kleine Risse und Hohlräume ohne Entmischung zu füllen. Deshalb muss das rheologische Verhalten des Einpressmörtels gut untersucht und kontrolliert werden, um die gewünschte Wirkung zu erzielen.
Die Rissinstandsetzung bei Lehmbauwerken erfolgt traditionell durch manuelles Stopfen mit einem Mörtel. Natürlich können auf diese Weise nur Risse mit einer großen Breite verfüllt werden. Ein weiterer Nachteil ist, dass Risse, die durch dickere Wände verlaufen, nicht vollständig mit den für das Stopfen verwendeten Werkzeugen erreicht werden können. Kalkgebundene Einpressmörtel für Lehmbaustoffe werden gewöhnlich für die Wiederbefestigung von Putzen und weniger aus statisch-konstruktiven Gründen eingesetzt Aufgrund der Eigenschaften von Lehm, müssen Einpressmörtel auf Basis von hydraulischem Kalk nach EN 459-1 wesentliche Anforderungen an eine Reihe von Eigenschaften erfüllen, die sich auf die Verträglichkeit, die Dauerhaftigkeit und insbesondere die Injektionsfähigkeit beziehen. Das Ziel der vorgestellten Untersuchungen war einen Einpressmörtel zu herzustellen, mit dem die strukturelle Kontinuität in Lehmmauerwerk oder anderen massiven Lehmwänden (Stampf- und Wellerlehm) durch Rissverpressung wiederhergestellt werden kann. Das Material bestand aus Kalkhydrat mit Zusätzen von Puzzolanen und Kalksteinfüller.
The repair of earthen structures is not an easy task. Earth as a construction material has comparatively weak mechanical properties. It is also susceptible towards liquid water, were it can lose cohesion very quickly if certain moisture contents are exceeded. Repair concepts of structures built with such materials are therefore challenging. Historical earthen structures often exhibit damages in form of extensive cracking, which may have been caused by static or dynamic loads. Frequently these cracks are insufficiently or inappropriately repaired because of lack of knowledge and / or technology. In particular, the behaviour of crack repair by grouting poses a challenge in earthen materials and demands specific requirements for the grouting mortar, such as low water content, good water retention, low shrinkage. Grouting materials require additional specifications such as compatible strengths and Young’s modulus as well as good adhesion to the earthen substrates. In addition, grouts have to be sufficiently flowable to fill small cracks and voids without segregation or bleeding. Therefore, the rheological behaviour has to be well understood and controlled to gain the desired effects.
The repair of cracks in earthen buildings is traditionally done by stuffing manually mortar into the gap. Naturally, this method is only usable for cracks with large widths. Another disadvantage is that cracks going through thicker walls cannot be completely reached by the tools used for stuffing the mortar into the crack. Lime based grouts for earthen materials were usually used for re-attachment of plasters but less for structural reasons. Due to the nature of earthen materials grouts based on formulated or hydraulic lime (according to the definition in EN 459-1) have to meet considerable demands on a variety of properties, which are related to compatibility, durability and in particular to the ability of being injected. The goal of this study was to create a grout, which can be used to re-establish structural continuity in cracked earthen masonry or other massive earth walls (rammed earth and cob) with the focus on grouting cracks. The grout material was based on hydrated lime (calcium hydroxide) with additions of pozzolana and lime stone filler.