Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (79)
- Vortrag (52)
- Beitrag zu einem Tagungsband (18)
- Beitrag zu einem Sammelband (13)
- Posterpräsentation (12)
- Buchkapitel (2)
- Forschungsbericht (1)
Sprache
- Englisch (113)
- Deutsch (61)
- Mongolisch (3)
Schlagworte
- Glass (26)
- Sintering (20)
- Crystallization (10)
- LTCC (9)
- Foaming (7)
- Glas (7)
- Sintern (7)
- Viscosity (7)
- Water content (5)
- Crystal growth (4)
Organisationseinheit der BAM
The internal friction of hydrated soda-lime-silica glasses with total water content (CW ) up to 1.9 wt. % was studied by dynamic mechanical analysis (DMA) using temperature-frequency sweeps from 723 K to 273 K and from 1 s-1 to 50 s-1. Total water content and concentrations of H2O molecules (CH2O ) and OH groups (COH) in the DMA specimens were determined by infrared spectroscopy. For low water contents (CW ≈ COH < 0.25 wt. %) two discrete internal friction peaks below the glass transition (α relaxation) were assigned to the low-temperature motion of alkali ions (γ relaxation) and cooperative movements of dissimilar mobile species under participation of OH at higher temperature (βOH relaxation). For large water contents (CW > 1 wt. %), where significant amounts of molecular water are evident (CH2O > 0.15 wt. %), however, internal friction spectra change unexpectedly: the βOH peak heights saturate and a low temperature shoulder appears on the β-relaxation peak. This emerging relaxation mode (βH2O relaxation) was assigned to the motions of H2O molecules. βH2O relaxation was found to be faster than βOH but slower than γ relaxation. Activation energy of the different relaxation modes increased in the order γ < βH2O < βOH < α.
We present an easy-to-apply method to predict structural trends in the internal nucleation tendency of oxide glasses. The approach is based on calculated crystal fracture surface energies derived from easily accessible diatomic bond energy and crystal lattice data. The applicability of the method is demonstrated on literature nucleation data for isochemically crystallizing oxide glasses.
The effect of hydration on the kinetic fragility of soda-lime-silica glasses was investigated by viscometry in the glass transition range. Water-bearing glasses were prepared from industrial float glass (FG) and a ternary model glass (NCS = 16Na2O 10CaO 74SiO2 in mol%) by bubbling steam through the melt at 1480 °C and up to 7 bar. Additionally, a sodium borosilicate glass (NBS = 16Na2O 10B2O3 74SiO2 in mol%) was hydrated under equal conditions. As detected by infrared spectroscopy water dissolves in the glasses exclusively as OH-groups. The hydration resulted in a total water content CW up to ~ 0.2 wt% for FG, NCS and NBS glasses. Kinetic fragility, expressed by the steepness index m, was determined from the temperature dependence of η at the glass transition. Viscosity data from previous studies on hydrous float glasses (CW > 1 wt%) were surveyed together with literature data on the (H2O)Na2OCaOSiO2, (H2O)Na2OSiO2 and (H2O)SiO2 systems to expand the range of water concentration and bulk composition. We could demonstrate that m decreases for all glasses although water is dissolved as OH and should depolymerize the network. An empirical equation of the general type m = a - b logCW where a, b are fitting parameters, enables m to be predicted, for each glass series as function of the water content CW. The enlarged data base shows that the parameter B of the Arrhenius viscosity-temperature relation decreases much stronger than the isokom temperature at the glass transition.
We studied sintering of LTCC-type glass matrix composites (GMCs) consisting of small glass and alumina particles of equal size. Primarily, crystals act as rigid inclusions, decelerating the densification rate. In later stages, they also dissolve, partially increasing the viscosity. Release of alumina finally induces crystallization of alumosilicates, which enables post-firing stability. To study both effects, two model GMCs were prepared: an α-Al2O3 + barium alumoborosilicate glass (BABS)GMC, which shows neither significant dissolution nor crystallization, and an α-Al2O3 + calcium alumoborosilicate glass (CABS)GMC, which dissolves readily and promotes crystallization. The kinetics of shrinkage for both GMC were modeled by utilizing Frenkel theory for the early stage and MackenzieShuttleworth theory for the late stage, assuming that sintering is superimposed by the weighted contributions of triparticle glasscrystal clusters, their random occurrence (ideal mixing), and a shrinkage rate controlled by the GMC effective viscosity. In agreement with modeling, the experimental results showed that the shrinkage rate of BABSGMC decreases progressively for crystal volume fractions Φ > 0.15. The attainable shrinkage is reduced by up to 8% for Φ = 0.45. For the CABSGMC with Φ = 0.25, a reduction of Φ to 0.20 was evident due to partial α-Al2O3 dissolution. This effect was found able to increase the sintering temperature by ~5060 K.
Highly porous (>60% open porosity) glass–ceramic scaffolds with remarkable mechanical properties (compression strength of ~15 MPa) were produced by indirect 3D printing. Precursor glass powders were printed into 3D ordered structures and then heat treated to sinter and develop crystalline phases. The final glass–ceramic contained a β-spodumene solid solution together with a secondary phase of lithium disilicate.
The precision of the printed geometry and the density of the struts in the scaffold depended on several processing parameters (e.g. powder size and flowability, layer thickness) and were improved by increasing the binder saturation and drying time. Two types of powders with different particle size distribution (PSD) and flowability were used. Powders with a larger PSD, could be processed within a wider range of printing parameters due to their good flowability; however, the printing precision and the struts density were lower compared to the scaffolds printed using the powder in a smaller average PSD.
A novel method to generalize kinetic data of viscous crack healing in glasses is proposed. The method assumes that crack healing progress is proportional to the healing time, t, and indirect proportional to viscosity, n. This way, crack length and crack width data, normalized to the initial crack length and plotted versus t/n, allow to compare crack healing progress for different cracks and healing temperatures in a master curve. Crack healing experiments conducted in this study demonstrate the applicability of this method for a commercial microscope slide glass.
The short- and long-term structural evolution and aging of solgel materials prepared under mild conditions are studied by fluorometry, dynamic light scattering (DLS), 29Si NMR and gravimetry. In combination with the first, a newly developed donoracceptor-substituted fluorescent probe with two acidophilic sites of different strength and topology is introduced. Its performance in detecting changes in parameters such as polarity, proticity, and pore volume on the microscopic scale is compared to two other dyes and to the macroscopic changes revealed by DLS, NMR and gravimetry. At early stages of the solgel process, fluorometry, DLS and NMR reveal similar changes which are typical of the structural evolution of SiO2 sols having different synthesis parameters. During later times of sol aging, DLS and NMR reflect the growth of the network and indicate that all sols approach similar structural equilibria. Fluorometry supports these findings by signalling a gradual decrease in mobile species with high proton activity. The formation of the spanning cluster upon gelation is strongly evident only from DLS results while the local environment of the fluorophore remains largely unchanged. However, the fluorescent dye is able to report microscopic changes even during long-term aging. Drying of the gels with a pronounced contraction of solvated pores is readily observable by fluorometry and gravimetry. During the late reaction stages, the fluorescence properties of the tailor-made dye are still sensitive toward the environment.
The crystallization of 11BaO-25CaO-64SiO2 mol% glass powders and related effects of glass powder milling have been studied by X-ray diffraction (XRD), light and scanning electron microscopy (SEM) and differential thermal analysis (DTA). Glass powders were made by ZrO2 crushing with subsequent sieving or sedimentation or alternatively made by milling with agate, corundum and tungsten carbide. Although surface crystallization was detectable during late sintering, all powders fully sintered. Wollastonite was found as primary crystal phase followed by cristobalite and sanbornite precipitation. The latter crystallization steps caused a second DTA-peak for fine powders. DTA-peak temperatures shifted to lower temperature with decreasing particle size in any case. No significant effects of milling materials on DTA-peak temperatures were evident. As an exception, however, milling in agate caused strongly decreased temperatures of the second DTA-peak. This observation can be explained by the progressive mechanical damaging, which results from the required prolonged milling time with agate due to its small materials density, and the fact that diamond made scratches did promote surface crystallization of cristobalite. The present study thus shows that even for glass powders with excellent sinterability, milling can affect microstructure evolution.
We propose a model to describe the sintering kinetics of polydispersed glass particles, having no adjustable parameter. The model is based on three sintering stages: a pure Frenkel' (F) first step, a mixed Frenkel/MackenzieShuttleworth' stage, and a third, pure MackenzieShuttleworth' (MS) step. The model considers sample shrinkage as the sum of the partial shrinkage of several clusters, each consisting of equally sized particles and each showing independent F or MS behavior. The overall set of clusters mimics the specimen's real particle size distribution. We then introduce the concept of neck forming ability, which allows the formation of necks among particles of different sizes, relaxing the clustering condition. Using experimental physical parameters: particle size distribution, viscosity, surface energy, and the theoretical neck forming ability, the model describes well the sintering kinetics of an alumino-borosilicate glass powder having polydispersed, irregular shaped particles in a variety of temperatures. The sintering kinetics of the real powder is slower, but not far from the calculated kinetics of a monodispersed distribution containing only particles of average size. Thus the model provides a tool for estimating the sintering kinetics of real glass powders, for any size distribution and temperature, thus minimizing the number of laboratory experiments.
For the first time evidence is provided that a nanocrystalline and stacking-disordered, chemically stabilized β-cristobalite form of AlPO4 occurs in a sewage sludge ash (SSA). This proof is based on a combined X-ray powder diffraction and X-ray fluorescence investigation of an SSA produced at a large-scale fluidized bed incineration facility serving a catching area with a population of 2 million. The structural and chemical characterization was carried out on 'as received' SSA samples as well as on solid residues remaining after leaching this SSA in sodium hydroxide solution. Thus, it was ascertained that the observed nanocrystalline and stacking-disordered cristobalite-like component belongs to the aluminum phosphate component of this SSA, rather than to its silicon dioxide component. In addition, a direct proof is presented that the chemically stabilized β-cristobalite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850°C), typical for fluidized bed incinerators.