Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (79)
- Vortrag (52)
- Beitrag zu einem Tagungsband (18)
- Beitrag zu einem Sammelband (13)
- Posterpräsentation (12)
- Buchkapitel (2)
- Forschungsbericht (1)
Sprache
- Englisch (113)
- Deutsch (61)
- Mongolisch (3)
Schlagworte
- Glass (26)
- Sintering (20)
- Crystallization (10)
- LTCC (9)
- Foaming (7)
- Glas (7)
- Sintern (7)
- Viscosity (7)
- Water content (5)
- Crystal growth (4)
Organisationseinheit der BAM
Wasserdiffusion in Floatglas
(2005)
Advanced ceramics are promising key components for microsystems
engineering, communication Technology and medical engineering.
Driven by steadiiy increasing demands on dimensional accuracy of
components and Integration density, sintering has to be controlled at
an unprecedented degree of precision.
Being most crucial for components of complex shape, graded or heterogeneous-composed parts like LTCC multilayers for microsystems, precise control of sintering has a decisive influence on the dimensional accuracy, mechanical integrity and reliability of sintered components.
Thus, permanent or temporary shape distortions or warping during sintering may result from spatially heterogeneous microstructure and
temperature distribution, e.g. during the co-firing process of green
multilayer Stacks printed with metallization and other functional pastes.
Whereas permanent warping can be easily measured after sintering, temporary warping during firing is more difficult to measure. Nonetheless, this effect may cause latent failures later, which often limit the applicability of ceramic components.
Hochleistungssinterwerkstoffe spielen eine wachsende Rolle in derzeitigen Schlüsseltechnologien wie der Mikrosystem-, Informations-, Kommunikations- und Medizintechnik.
Dabei steigen die Anforderungen an die präzise Steuerung der Sinterung. Besonders für komplexe, gradierte oder heterogen zusammengesetzte Formkörper wie zum Beispiel keramische LTCC-Multilayer für die Mikrosystemtechnik hat die exakte Beherrschung dieses Prozessschrittes wesentlichen Einfluss auf die Maßhaltigkeit, mechanische Integrität und Zuverlässigkeit der gesinterten Bauteile. Bedingt durch die Heterogenität der mehrlagigen und mit Leit- und anderen Funktionspasten bedruckten Sinterkörper hinsichtlich ihrer sinterphysikalischen oder thermischen Eigenschaften können bleibende
oder temporäre Verwerfungen beim Schrumpfungsprozess auftreten, wobei letztere unter Umständen Ursache latenter Fehler im späteren Bauteil sind.
Highly porous (>60% open porosity) glass–ceramic scaffolds with remarkable mechanical properties (compression strength of ~15 MPa) were produced by indirect 3D printing. Precursor glass powders were printed into 3D ordered structures and then heat treated to sinter and develop crystalline phases. The final glass–ceramic contained a β-spodumene solid solution together with a secondary phase of lithium disilicate.
The precision of the printed geometry and the density of the struts in the scaffold depended on several processing parameters (e.g. powder size and flowability, layer thickness) and were improved by increasing the binder saturation and drying time. Two types of powders with different particle size distribution (PSD) and flowability were used. Powders with a larger PSD, could be processed within a wider range of printing parameters due to their good flowability; however, the printing precision and the struts density were lower compared to the scaffolds printed using the powder in a smaller average PSD.
Crystallization behavior in different atmospheres (air, Ar, and 7% H2/Ar) of lithium iron phosphate glass (33Li2O33Fe2O31Nb2O5–33P2O5 (LFNP)) powders with different sizes of 2–1000 µm was examined. The crystallization peak temperature (Tp) in Ar and 7% H2/Ar decreased with decreasing the particle size of glass powders, but the value of Tp in air was independent of particle size. The crystallized glass obtained by heating to Tp showed the formation of the α-Li3Fe2(PO4)3 and LiFePO4 crystalline phases. Fe2O3 crystals were formed only in the inside of crystallized glass plates in the heating in air. The crystallization of LiFePO4 was largely enhanced in the particle size of <2 µm during the heating in Ar and 7% H2/Ar atmospheres. The main crystallization mechanism in LFNP glass was found to be surface crystallization. Significant shrinkages were observed for glass compacts (pellets) in the heating in 7% H2/Ar. These results suggest that controlling particle sizes and atmospheres enables the design the morphology of LiFePO4 crystals in LFNP glass.
Lithium disilicate, leucite and apatite glass-ceramics have become state-of-the-art framework materials in the fabrication of all-ceramic dental restorative materials. The goal of this study was to examine the crack propagation behaviour of these three known glass-ceramic materials after they have been subjected to Vickers indentation and to characterize their crack opening profiles (δmeas vs. (a-r)). For this purpose, various methods of optical examination were employed. Optical microscopy investigations were performed to examine the crack phenomena at a macroscopic level, while high-resolution techniques, such as scanning electron microscopy (SEM) and atomic force microscopy (AFM), were employed to investigate the crack phenomena at a microscopic level. The crack patterns of the three glass-ceramics vary from fairly straightforward to more complex, depending on the amount of residual glass matrix present in the material. The high-strength lithium disilicate crystals feature a high degree of crosslinking, thereby preventing crack propagation. In this material, the crack propagates only through the residual glass phase, which constitutes 30%40% by volume. Having a high glass content of more than 65% by volume, the leucite and apatite glass-ceramics show far more complex crack patterns. Cracks in the leucite glass-ceramic propagate through both the glass and crystal phase. The apatite glass-ceramic shows a similar crack behaviour as an inorganicorganic composite material containing nanoscale fillers, which are pulled out in the surroundings of the crack tip. The observed crack behaviour and the calculated View the MathML source values of the three types of glass-ceramics were compared to the Kkic values determined according to the SEVNB method.