Filtern
Dokumenttyp
Sprache
- Englisch (2) (entfernen)
Referierte Publikation
- ja (2)
Schlagworte
- BAMline (2) (entfernen)
Organisationseinheit der BAM
In order to investigate their microcracking behaviour, the microstructures of several β-eucryptite ceramics, obtained from glass precursor and cerammed to yield different grain sizes and microcrack densities, were characterized by laboratory and synchrotron x-ray refraction and tomography. Results were compared with those obtained from scanning electron microscopy (SEM). In SEM images, the characterized materials appeared fully dense but computed tomography showed the presence of pore clusters. Uniaxial tensile testing was performed on specimens while strain maps were recorded and analyzed by Digital Image Correlation (DIC). X-ray refraction techniques were applied on specimens before and after tensile testing to measure the amount of the internal specific surface (i.e., area per unit volume). X-ray refraction revealed that (a) the small grain size (SGS) material contained a large specific surface, originating from the grain boundaries and the interfaces of TiO2 precipitates; (b) the medium (MGS) and large grain size (LGS) materials possessed higher amounts of specific surface compared to SGS material due to microcracks, which decreased after tensile loading; (c) the precursor glass had negligible internal surface. The unexpected decrease in the internal surface of MGS and LGS after tensile testing is explained by the presence of compressive regions in the DIC strain maps and further by theoretical arguments. It is suggested that while some microcracks merge via propagation, more close mechanically, thereby explaining the observed X-ray refraction results. The mechanisms proposed would allow the development of a strain hardening route in ceramics.
The employment of synchrotron radiation for refraction topography of materials has considerable advantages over standard x-ray sources. The much higher beam intensity and the parallel and monochromatic radiation provide faster measurements and better angular and spatial resolution. X-ray refraction techniques image the inner surface and interface concentration of micro-structured materials. This effect of x-ray optics is additional to small-angle scattering by diffraction, when the scattering objects reach micrometre dimensions. We have developed x-ray refraction techniques within the last decade in order to meet the growing demands for improved non-destructive characterization of high-performance composites, ceramics and other low-density materials. Sub-micron particle dimensions, the pore size of ceramics, the crack density distribution and single fibre debonding within damaged composites can be measured and visualized by computer-generated interface topographs. For this purpose investigations are now being performed at the new hard x-ray beamline of the Federal Institute for Materials Research and Testing (BAM) at BESSY, Berlin. This BAMline provides monochromatic radiation of photon energies from 5 to 60 keV from a double multilayer and/or a double-crystal monochromator. A separate instrument is dedicated to the further development and application of synchrotron radiation refraction (SRR) topography. Different from conventional small-angle scattering cameras with collimating slits and pinholes, scattering angles down to a few seconds of arc are selected by a single-crystal analyser, similar to a Bonse-Hart diffractometer. A 20 µm spatial resolution of the scattering micro-structures is achieved by a CCD camera with a fluorescent converter. First SRR topographs of aircraft composites [carbon fibre-reinforced plastics (CFRP), carbon fibre-reinforced ceramics (C/C), metal matrix ceramics (MMC)] will be reported.