The aim of the joint project ViPQuali (Virtual Product Qualification) was to describe a components ageing behaviour in a given environment, by numerical simulation.
Having chosen polypropylene (PP) as the material, which does not show sensitivity to moisture, the relevant weathering parameters of the doseresponse functions could be limited to spectral irradiance and temperature.
In artificial irradiation tests, for PP plates of varied stabiliser content, spectral sensitivity as well as temperature dependence of irradiation-caused crack formation was quantified. For that purpose, samples were exposed both to artificial weathering tests at various constant temperatures and to spectrally resolved irradiation. The temperature dependence could be modelled by an Arrhenius fit. For fitting the spectral sensitivity, a plateau function was chosen. Subsequently, the stabiliser content was parameterised and extrapolated.
The formed dose–response functions were incorporated into a Computational Fluid Dynamics (CFD) software program, simulating the environment of a sample within a Phoenix-exposed IP/DP (Instrument Panel/Door Panel box) box, based on sun position and weather conditions, including radiation interactions. Observed local effects as well as the general ageing advance of PP hats are compared with respect to simulation and experiment.
Resulting from this project, for this most simple example of PP of varied stabiliser content, the time to failure can be estimated for each weathering exposure environment with known time-resolved irradiance and temperature conditions.
At present, heterogeneous and fine-grained masonry rubble can only be recycled at very low level. To overcome this limitation, the material was employed as feedstock for the production of lightweight aggregates in a thermal process similar to that used in the manufacture of expanded clay and expanded slate. To that end, the fundamental suitability of masonry rubble as a raw material was evaluated. Experiments were carried out which indicated that lightweight granules with defined, adjustable properties similar to those of natural-material-based aggregates could be manufactured from masonry rubble. Structural lightweight concretes produced with these secondary aggregates achieved comparable performance to lightweight concretes produced with conventional expanded clay. Lightweight recycled building material aggregates represent a product that hardly requires any primary resources in its manufacture. In principle, the technique also seems to be well suited for high-quality recycling of other mineral waste materials.