Filtern
Dokumenttyp
Sprache
- Englisch (7)
Schlagworte
- Cell proliferation (2)
- Exocytosis (2)
- Gold nanoparticles (2)
- Quantum dots (2)
- Uptake studies (2)
- CCQM key comparison (1)
- Carbonitride (1)
- Cermet (1)
- DOPO (1)
- Epoxy resin (1)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (3)
- 1.2 Biophotonik (2)
- 1.7 Organische Spuren- und Lebensmittelanalytik (1)
- 1.8 Umweltanalytik (1)
- 5 Werkstofftechnik (1)
- 5.0 Abteilungsleitung und andere (1)
- 6 Materialchemie (1)
- 6.3 Strukturanalytik (1)
- 9 Komponentensicherheit (1)
- 9.5 Tribologie und Verschleißschutz (1)
Most studies about the interaction of nanoparticles (NPs) with cells have focused on how the physicochemical properties of NPs will influence their uptake by cells. However, much less is known about their potential excretion from cells. However, to control and manipulate the number of NPs in a cell, both cellular uptake and excretion must be studied quantitatively. Monitoring the intracellular and extracellular amount of NPs over time (after residual noninternalized NPs have been removed) enables one to disentangle the influences of cell proliferation and exocytosis, the major pathways for the reduction of NPs per cell. Proliferation depends on the type of cells, while exocytosis depends in addition on properties of the NPs, such as their size. Examples are given herein on the role of these two different processes for different cells and NPs.
Brittle materials, such as oxide glasses, are usually very sensitive to flaws, giving rise to a macroscopic fracture strength that is much lower than that predicted by theory. The same applies to metallic glasses (MGs), with the important difference that these glasses can exhibit certain plastic strain prior to catas- trophic failure. Here we consider the strongest metallic alloy known, a ternary Co 55 Ta 10 B 35 MG. We show that this macroscopically brittle glass is flaw-insensitive at the micrometer scale. This discovery emerges when testing pre-cracked specimens with self-similar geometries, where the fracture stress does not de- crease with increasing pre-crack size. The fracture toughness of this ultra-strong glassy alloy is further shown to increase with increasing sample size. Both these findings deviate from our classical under- standing of fracture mechanics, and are attributed to a transition from toughness-controlled to strength- controlled fracture below a critical sample size.
Product emissions chamber testing involves a complex protocol with several sources of measurement uncertainty (ASTM, 2010; ISO, 2006). Despite the potential for significant variability in measurement results within and among laboratories, there is no Standard method available to assess the accuracy of emissions chamber test results. Recently, Germany’s Federal Institute for Materials Research and Testing (BAM) started a program to evaluate the performance of laboratories testing for the AgBB (German Committee for Health-related Evaluation of Building Products) labelling scheme (Wilke et al., 2009). Test method validation was conducted through interlaboratory studies (ILS) with over 30 participants. Simultaneously, the National Institute of Standards and Technology (NIST) and Virginia Tech (VT) started a program to develop a series of reference materials that mimic real building products, can be tested in typical emissions chambers, and have independently known emission rates (Cox et al., 2010). BAM, NIST and VT subsequently joined forces to conduct a series of inter-laboratory studies using the prototype reference material. A pilot ILS was conducted with BAM and NIST followed by an expanded ILS with several participating countries. Results from these interlaboratory studies have the potential to define an internationally-accepted Standard approach to validate results from product emissions tests.
The comparison required the assignment of the mass fraction of folic acid present as the main component in the comparison sample. Performance in the comparison is representative of a laboratory's measurement capability for the purity assignment of organic compounds of medium structural complexity [molecular weight range 300–500] and high polarity (pKOW < −2).
Methods used by the eighteen participating NMIs or DIs were based on a mass balance (summation of impurities) or qNMR approach, or the combination of data obtained using both methods. The qNMR results tended to give slightly lower values for the content of folic acid, albeit with larger associated uncertainties, compared with the results obtained by mass balance procedures. Possible reasons for this divergence are discussed in the report, without reaching a definitive conclusion as to their origin.
The comparison demonstrates that for a structurally complex polar organic compound containing a high water content and presenting a number of additional analytical challenges, the assignment of the mass fraction content property value of the main component can reasonably be achieved with an associated relative standard uncertainty in the assigned value of 0.5%
A siloxane compound (MVC) and a bi-group phosphaphenanthrene/triazine compound (TGD) were employed in epoxy thermosets to explore high-efficiency flame retardant systems. With only 1wt% MVC and 3wt% TGD, an epoxy thermoset passed UL 94 V-0 rating test and achieved a limiting oxygen index value of 34.0%, exhibiting an excellent flame retardant effect. The MVC/TGD system not only decreased the peak value of heat release rate and effective heat of combustion but also imparted an improved charring ability to thermosets, thereby outstandingly reducing the flammability of 1%MVC/3%TGD/EP. Compared with the fire performance of 4%TGD/EP and 4%MVC/EP, the MVC/TGD system showed an obvious flame retardant synergistic effect, mainly depending on the general improvement of flame inhibition, charring and barrier effects of the thermoset during combustion. Evolved gas analysis combinedwith condensed-phase pyrolysis product Analysis jointly revealed the details of the changed pyrolysis mode.