Femto- and nanosecond laser ablation of polymethylmethacrylate (PMMA) and PMMA doped with a linear absorber was
investigated in the infrared spectral region. Ablation thresholds were determined and incubation phenomena were identified. The
degree of incubation was calculated employing a phenomenological model. The influence of the pulse duration on the
machining quality of the polymers was examined. The presence of an absorbing chromophore is not a prerequisite for a
controllable fs-laser structuring in contrast to the ns-treatment. Surface swelling always accompanied ablation.
The influence of different laser pulse lengths on the removal of a polymer layer from metal substrates was investigated. As model systems, doped poly(methylmetacrylate) (PMMA) on titanium and tungsten substrates were selected.
The ablation threshold and irradiation spot morphology of titanium and tungsten were compared for femtosecond (fs) and nanosecond (ns) laser irradiation and different pulse numbers. Nanosecond laser treatment resulted in a non-homogeneous surface morphology for both titanium and tungsten substrates. Femtosecond irradiation of tungsten revealed a homogeneous ablation spot with little changes in the surface morphology. For titanium, the formation of columnar structures within the irradiation spot was observed.
Two different dopant concentrations were used for PMMA to achieve an equal linear absorption coefficient for the femto- and nanosecond laser wavelengths of 790 and 1064 nm. The best results were achieved for the removal of doped PMMA by femtosecond laser irradiation, where only a minimal modification of the metal surface was detected. In the case of nanosecond laser exposure, a pronounced change of the structure was observed, suggesting that damage-free cleaning of the selected metal may only be possible using femtosecond laser pulses. Different experimental parameters, such as laser fluence, pulse repetition rate and sample speed were also investigated to optimize the cleaning quality of doped PMMA from tungsten substrates with femtosecond laser pulses.
This contribution investigates laser-induced damage of thin film and bulk polymer
samples, with the focus on physical processes occurring close to the damage threshold. In-situ
real-time reflectivity (RTR) measurements with picosecond (ps) and nanosecond (ns) temporal
resolution were performed on thin polymer films on a timescale up to a few microseconds (µs).
A model for polymer thin film damage is presented, indicating that irreversible chemical
modification processes take place already below the fluence threshold for macroscopic damage.
On dye-doped bulk polymer filters (as used for laser goggles), transmission studies using fs-and
ps-laser pulses reveal the optical saturation behavior of the material and its relation to the
threshold of permanent damage. Implications of the sub-threshold processes for laser safety
applications will be discussed for thin film and bulk polymer damage.