Full penetration 15 kW Yb fibre laser butt welding of thick AlMg3 (AW 5754) plates was performed in PA position. A contactless inductive electromagnetic weld pool support system was used to prevent gravity dropout of the melt. The welding speed needed to achieve 20 mm penetration was ~0·5 m min-1. An ac power supply of ~244 W at 460 Hz was necessary to completely suppress gravity dropout of the melt and eliminate sagging of the weld pool root side surface. The oscillating magnetic field can suppress the Marangoni convection in the lower part of the weld pool. The system was also successfully used in the full penetration welding of 30 mm thick AlMg3 plates.
Al-Mg-Si alloys are known to be highly susceptible to solidification cracking except when using an appropriate filler metal (e.g., 4343 or 5356), although the amount of dilution required to avoid cracking has never been a well-defined quantity. The aim of the present study is to determine a relationship between filler metal dilution, local strain rate conditions, and cracking susceptibility. Making use of the controlled tensile weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and non-crack conditions for different local strain rates and dilution amounts, holding all other welding parameters constant. This boundary, presented in the form of critical strain rate-dilution map, defines the critical amount of 4043 filler metal required to avoid solidification cracking when arc welding 6060 aluminium, depending upon local strain rate.
The main characteristic feature of deep penetration laser beam welding is a large temperature difference between the plasma cavity (keyhole) in the centre of the weld pool and the melting/solidification front. Large temperature gradients in the weld pool result in a very intensive thermocapillary (Marangoni) convection. The weld pool surface width becomes very large and unstable. However, an externally applied oscillating magnetic field can stabilize the surface of the melt (the Garnier-Moreau effect, 1983). In the present work this technology was used to stabilize the surface of the weld pool in partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 alloyin PA position. The AC magnet was mounted on the laser welding head. The oscillating magnet field was oriented perpendicular to the welding direction. It was found that the AC magnet field can drastically reduce the surface roughness of welds. The analysis of the x-ray images shows a rastic reduction of porosity content in the welds. This effect can be explained as a result of electromagnetic ectification of the melt.
An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction.
The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM)
induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM)
contribution to the surface tension (the Garnier-Moreau effect)
The ever larger requirements of the material selection in the range of maritime industry necessitate the application of high-tech materials. Titanium because of its excellent mechanical properties at low weight is an attractive alternative for the construction of ships. The goal of this investigation was to design a welding method for joining samples of 16 mm thick Ti3Al2.5 V. The welding experiments with a 20 kW Yb-fiber laser source and varying combinations of parameters were intended to qualify the laser beam welding process. The welding results were analyzed by non-destructive and destructive testing. In addition, the welding tests were recorded with two high-speed cameras to observe the weld pool and the vapor plume. The evaluation of the high-speed images in correlation with the results of non-destructive testing shows, that a significant improvement of process stability and weld quality can be achieved by the suppression of the vapor plume.