Filtern
Dokumenttyp
- Zeitschriftenartikel (17)
Referierte Publikation
- ja (17) (entfernen)
Schlagworte
- Computed tomography (6)
- X-ray computed tomography (5)
- Additive manufacturing (4)
- Cellular solids (3)
- 3D printing (2)
- Ceramics (2)
- Chaboche model (2)
- Delamination (2)
- GTN model (2)
- X-ray refraction (2)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (8)
- 8.5 Röntgenbildgebung (8)
- 2 Prozess- und Anlagensicherheit (1)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (1)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 8.0 Abteilungsleitung und andere (1)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (1)
- 9 Komponentensicherheit (1)
X-ray refraction is based on optical deflection of X-rays, similar to the well-known small angle X-ray scattering, but hundreds of times more intense, thus enabling shorter measurement time. We show that X-ray refraction techniques are suitable for the detection of pores, cracks, and in general defects. Indeed, the deflected X-ray intensity is directly proportional to the internal specific surface (i.e., surface per unit volume) of the objects. Although single defects cannot be imaged, the presence of populations of those defects can be detected even if the defects have sizes in the nanometer range.We present several applications of X-ray refraction techniques to composite materials:- To visualize macro and microcracks in Ti-SiC metal matrix composites (MMC);- To correlate fatigue damage (fibre de-bonding) of carbon fibre reinforced plastics (CFRP) to X-ray refraction intensity;- To quantify the impact damage by spatially resolved single fibre de-bonding fraction as a function of impact energy in CFRP laminates.An example of classic high-resolution computer tomography of an impact-damaged CFRP will also be presented, as a benchmark to the present state-of-the-art imaging capabilities. It will be shown that while (absorption) tomography can well visualize and quantify delamination, X-ray refraction techniques directly yield (spatially resolved) quantitative information about fibre de-bonding, inaccessible to absorption tomography.
Simple models describing the relationship between basic mechanical properties and the relative density of various types of porous metals (such as foams, sponges and lattice structures) are well established. Carefully evaluating these relationships experimentally is challenging, however, because of the stochastic structure of foams and the fact that it is difficult to systematically isolate density changes from variations in other factors, such as pore size and pore distribution. Here a new method for producing systematic sets of stochastic foams is employed based on electron beam melting (EBM) additive manufacturing (AM). To create idealised structures, structural blueprints were reverse-engineered by inverting X-ray computed tomographs of a randomly packed bed of glass beads. This three-dimensional structure was then modified by computer to create five foams of different relative density ρr, but otherwise consistent structure. Yield strength and Young’s modulus have been evaluated in compression tests and compared to existing models for foams. A power of 3 rather than a squared dependence of stiffness on relative density is found, which agrees with a recent model derived for replicated foams. A similar power of 3 relation was found for yield strength. Further analysis of the strength of nominally fully dense rods of different diameters built by EBM AM suggest that surface defects mean that the minimum size of features that can be created by EBM with similar strengths to machined samples is ∼1 mm.
Selective Electron Beam Melting (SEBM) is a promising powder bed Additive Manufacturing technique for near-net-shape manufacture of high-value titanium components. However without post-manufacture HIPing the fatigue life of SEBM parts is currently dominated by the presence of porosity. In this study, the size, volume fraction, and spatial distribution of the pores in model samples have been characterised in 3D, using X-ray Computed Tomography, and correlated to the process variables. The average volume fraction of the pores (b0.2%) was measured to be lower than that usually observed in competing processes, such as selective laser melting, but a strong relationship was found with the differentbeamstrategies used to contour ,and infill by hatching, a part section. The majority of pores were found to be small spherical gas pores, concentrated in the infill hatched region; this was attributed to the lower energy density and less focused beam used in the infill strategy allowing less opportunity for gas bubbles to escape the melt pool. Overall, increasing the energy density or focus of the beam was found to correlate strongly to a reduction in the level of gas porosity. Rarer irregular shaped pores were mostly located in the contour region and have been attributed to a lack of fusion between powder particles.
Electron Beam Melting (EBM) as a means of Additive Manufacturing (AM), is of interest for the fabrication of intricate geometries for cellular materials in areas where complex architectures are needed, e.g. biomedical implants. Most studies have focused on specific geometries and so the effect of the structure on mechanical performance is not well understood. Many kinds of micro- and macro-scale defects can arise in additively manufactured components, so assessment of their influence on properties is needed. In this work, lattices of Ti-6Al-4V having a cubic structure have been manufactured by EBM, and the effect of heat treatments above and below the β-transus temperature on microstructure and compression response have been investigated. The former modifies only slightly the α + β structure and mechanical performance whereas the latter leads to coarse alternating α and β lamellae packets and α at the prior grain boundaries with a 10% loss in yield strength. The variation in the compressive yield stress with strut diameter is in good accord with simple models based on compressive deformation rather than shearing or buckling. Internal pores for struts aligned with the build direction are found around the edges of the solid form, in regions which seem to be associated with the EB scan pattern. Struts normal to the build direction show more significant defects but their redundancy means that they do not compromise the compressive performance in the build direction. Using a particle size in the range 45–100 μm minimum weld-track sizes were experimentally and numerically identified to be 176 and 148 μm in depth respectively with a depth-to-width ratio of 0.55. This produced a beam pass of the order of 300 μm oversizing small features (struts of 0.4 and 0.6 mm nominal diameter) when a contour around the strut periphery was applied.
Up to now, there exists a lack of methods for the additive manufacturing of voluminous ceramic parts with properties comparable to those of conventionally manufactured ones. A high density after sintering is needed to reach the superior properties of ceramic materials. We have developed a new additive manufacturing method, Laser-Induced Slip casting (LIS), to generate ceramic green bodies with high particle packing density and with virtually no restriction in the particle size of the feedstock, especially in terms of small particles. This is achieved by laser-induced local drying of slurries, with the process resembling many features of the well-established stereolithography, but without the excessive use of polymeric material. Thus, unlike the stereolithography process, the resulting green bodies can be processed like traditionally produced ceramic parts. This method allows large and dense additive-manufactured parts to be obtained from conventional water-based ceramic slurries. As an example, we will demonstrate the application of this novel technique with Si3N4.
One of the great strengths of X-ray computed tomography over conventional inspection methods (ultrasound, thermography, radiography) is that it can image damage in 3D. However for curved ordeformed composite panels it can be difficult to automatically ascribe the damage to specific plies or inter-ply interfaces. An X-ray computed tomography (CT) data processing methodology is developed to extract the through-thickness distribution of damage in curved or deformed composite panels. The method is applied to [(0°/90°)2]s carbon fibre reinforced polymer (CFRP) panels subjected low velocity impact damage (5 J up to 20 J) providing 3D ply-by-ply damage visualisation and analysis. Our distance transform approach allows slices to be taken that approximately follow the composite curvature allowing the impact damage to be separated, visualised and quantified in 3D on a ply-by-ply basis. In this way the interply delaminations have been mapped, showing characteristic peanut shaped delaminations with the major axis oriented with the fibres in the ply below the interface. This registry to the profile of the panel constitutes a significant improvement in our ability to characterise impact damage in composite laminates and extract relevant measurements from X-ray CT datasets.
The use of novel multi-scale correlative methods, which involve the coordinated characterisation of matter across a range of length scales, are becoming of increasing value to materials scientists. Here, we describe for the first time how a multi-scale correlative approach can be used to investigate the nature of ductile fracture in metals. Specimens of a nuclear pressure vessel steel, SA508 Grade 3, are examined following ductile fracture using medium and high-resolution 3D X-ray computed tomography (CT) analyses, and a site-specific analysis using a dual beam plasma focused ion beam scanning electron microscope (PFIB-SEM). The methods are employed sequentially to characterise damage by void nucleation and growth in one volume of interest, allowing for the imaging of voids that ranged in size from less than 100 nm to over 100 mm. This enables the examination of voids initiated at carbide particles to be detected, as well as the large voids initiated at inclusions. We demonstrate that this multi-scale correlative approach is a powerful tool, which not only enhances our understanding of ductile failure through detailed characterisation of microstructure, but also provides quantitative information about the size, volume fractions and spatial distributions of voids that can be used to inform models of failure. It isfound that the vast majority of large voids nucleated at MnS inclusions, and that the volume of a void varied according to the volume of its initiating inclusion raised to the power 3/2. The most severe voiding was concentrated within 500 mm of the fracture surface, but measurable damage was found to extend to a depth of at least 3 mm. Microvoids associated with carbides (carbide-initiated voids) were found to be concentrated around larger inclusion-initiated voids at depths of at least 400 mm. Methods for quantifying X-ray CT void data are discussed, and a procedure for using this data to calibrate parameters in the Gurson-Tvergaard Needleman (GTN) model for ductile failure is also introduced.
X-ray tomography characterisation of lattice structures processed by selective electron beam melting
(2017)
Metallic lattice structures intentionally contain open porosity; however, they can also contain unwanted closed porosity within the structural members. The entrained porosity and defects within three different geometries of Ti-6Al-4V lattices, fabricated by Selective Electron Beam Melting (SEBM), is assessed from X-ray computed tomography (CT) scans. The results suggest that horizontal struts that are built upon loose powder show particularly high (~20 x 10⁻³ vol %) levels of pores, as do nodes at which many (in our case 24) struts meet. On the other hand, for struts more closely aligned (0° to 54°) to the build direction, the fraction of porosity appears to be much lower (~0.17 x 10⁻³%) arising mainly from pores contained within the original atomised powder particles.
Several cylindrical specimens and dental implants, presenting diagonal lattice structures with different cell sizes (600, 900 and 1200 µm) were additively manufactured by selective laser melting process. Then they were implanted for two months in a sheep. After removal, they were studied by Archimedes’ method as well as X-ray computed tomography in order to assess the penetration of bone into the lattice. We observed that the additive manufactured parts were geometrically conform to the theoretical specifications. However, several particles were left adhering to the surface of the lattice, thereby partly or entirely obstructing the cells. Nevertheless, bone penetration was clearly visible. We conclude that the 900 µm lattice cell size is more favourable to bone penetration than the 1200 µm lattice cell size, as the bone penetration is 84 % for 900 µm against 54 % for 1200 µm cell structures. The lower bone penetration value for the 1200 µm lattice cell could possibly be attributed to the short residence time in the sheep. Our results lead to the conclusion that lattice implants additively manufactured by selective laser melting enable better bone integration.
In order to characterise the material and damage behaviour of additively manufactured polyamide 12 (PA12) under quasi-static load and to implement it in a numerical model, experiments under quasi-static load as well as microstructural investigations were carried out. Selective laser sintering (SLS) was used as the manufacturing process. For the classification of the material behaviour, quasi-static cyclic tests with holding times as well as tensile tests were performed. X-ray refraction and computed tomography (CT) were used to investigate the damage behaviour. The Chaboche model, which has already been applied for metallic materials under thermomechanical loading, served as the basis for the selection of the numerical material model. The same procedure was used for the selection of the damage model, where the Gurson–Tvergaard–Needleman (GTN) model was chosen, which was already used for porous metallic materials. The Chaboche model shows very good agreement with experimental results. Furthermore, the coupling with the GTN model allows a very good modelling of the damage behaviour. Finally, it could be shown that the selected models are suitable to simulate the material and damage behaviour of 3D printed PA12.