Filtern
Dokumenttyp
- Vortrag (41)
- Zeitschriftenartikel (38)
- Beitrag zu einem Tagungsband (16)
- Posterpräsentation (2)
- Sonstiges (1)
- Forschungsbericht (1)
Schlagworte
- Residual stress (28)
- Eigenspannungen (18)
- Welding (17)
- Additive manufacturing (12)
- Hochfester Stahl (10)
- Residual stresses (10)
- Schweißen (10)
- Solidification cracking (8)
- Creep-resistant steel (7)
- Neutron diffraction (7)
- Stress relief cracking (7)
- Additive Manufacturing (6)
- DED-arc (6)
- High strength steel (6)
- High-strength steels (6)
- LTT (6)
- MAG-Schweißen (5)
- Post weld heat treatment (5)
- Varestraint test (5)
- X-ray diffraction (5)
- Additive Fertigung (4)
- High-strength steel (4)
- Kaltrisssicherheit (4)
- Restraint (4)
- Schwingfestigkeit (4)
- Varestraint-Test (4)
- Dilatometry (3)
- IN718 (3)
- Large-scale test (3)
- Phase transformation (3)
- Process parameters (3)
- Residual Stress (3)
- Residual Stresses (3)
- Selective Laser Melting (3)
- Selective laser melting (3)
- Synchrotron (3)
- Wasserstoff (3)
- AISI D2 (2)
- Bauteilprüfung (2)
- Cold cracking (2)
- Component test (2)
- Creep resistant steel (2)
- GMA welding (2)
- Heißrisse (2)
- Hot cracking (2)
- Hydrogen (2)
- LTT (Low Transformation Temperature) (2)
- LTT weld filler materials (2)
- Laser implantation (2)
- Laser powder bed fusion (2)
- Martensite (2)
- Microstructure and texture (2)
- Repair-welding (2)
- Residual stress analysis (2)
- SLM (2)
- Surface texturing (2)
- TiB2 (2)
- Varestraint testing (2)
- Weldability (2)
- Windenergie (2)
- hochfester Stahl (2)
- μCT-analysis (2)
- 13CrMoV9-10 (1)
- ADXRD (1)
- AGIL (1)
- AlSi10Mg alloy (1)
- As-built LPBF IN718 alloy (1)
- Aufmischung (1)
- Bauteiltest (1)
- Bragg-edge neutron 2D imaging (BENI) (1)
- CCT diagrams (1)
- Contour method (1)
- Coordinate measurement machine (1)
- Cracking (1)
- Crystallographic texture (1)
- Crystallographic texture control (1)
- Diffraction (1)
- Diffraction-elastic constants (1)
- Digital image correlation (1)
- Dislocation density (1)
- Distortion (1)
- Distortion upon baseplate removal (1)
- Duplex Stainless Steel (1)
- Effect of scanning strategies (1)
- Electron backscatter diffraction (EBSD) (1)
- Electron backscattered diffraction (1)
- Ermüdungsfestigkeit (1)
- Erstarrungsriss (1)
- Erstarrungsrisse (1)
- Fatigue (1)
- Fatigue strength (1)
- Ferrite (1)
- GMAwelding (1)
- HSLA steel (1)
- Hastelloy X (1)
- Heat control (1)
- Heat treatment (1)
- Heat-affected zone (1)
- Heißriss (1)
- High-strength filler metals (1)
- High-strength steel filler metal (1)
- High-strength structural steels (1)
- Hochdruck (1)
- Hochfeste Feinkornbaustähle (1)
- Hot tensile test (1)
- Hydrogen assisted cracking (1)
- Hydrogen-assisted cracking (1)
- IN718 PBF-LB/M (1)
- In-situ diffraction (1)
- In718 (1)
- Inconel 718 (1)
- Kaltriss (1)
- Kaltrissbildung (1)
- Kernel average misorientation (1)
- L-PBF (1)
- L-PBF IN718 material (1)
- LPBF (1)
- LTT filler metal (1)
- LTT-Zusatzwerkstoff (1)
- LTT-Zusatzwerkstoffe (1)
- Laboratory X-ray diffraction (1)
- Large scale test (1)
- Laser-based additive manufacturing (1)
- Localized laser dispersing (1)
- Low transformation temperature (1)
- Low transformation temperature filler materials (1)
- MVT (1)
- Martensit (1)
- Materialprüfung (1)
- Mechanical Engineering (1)
- Mechanics of Materials (1)
- Metal additive manufacturing (MAM) (1)
- Metals and Alloys (1)
- Microfocus X-ray computer tomography (μCT) (1)
- Minimum Waiting Time (1)
- Multi-pass welding (1)
- Near-surface X-ray diffraction (1)
- Neutron and X-ray diffraction (1)
- Neutronenbeugung (1)
- Nickel-based superalloys (1)
- Offshore (1)
- Offshore steel (1)
- Offshore steel grade (1)
- Offshore steels (1)
- Offshore wind turbine (1)
- Phasenumwandlung (1)
- Pipeline (1)
- Post Weld Heat Treatment (PWHT) (1)
- Post-weld heat treatment (1)
- Principal stress (1)
- Probengeometrie (1)
- Projekt AGIL - Alterung additiv gefertigter metallischer Materialien und Komponenten (1)
- Prüfung (1)
- Reheat cracking (1)
- Reparatur (1)
- Residual stress in AM (1)
- Residual stress reduction (1)
- Residual stress state (1)
- Retained Austenite (1)
- Roughness (1)
- Scan strategies (1)
- Scan strategy influence (1)
- Spannungsrelaxationsrisse (1)
- Stainless Steel (1)
- Strain-free lattice references (1)
- Strain-free lattice spacing (1)
- Stress Relief Cracking (SRC) (1)
- Stress balance (1)
- Stress balance condition (1)
- Submerged arc welding (1)
- Support configurations (1)
- Synchrotron X-ray diffraction (1)
- Synchrotron diffraction (1)
- Texture (1)
- TiC (1)
- TiN (1)
- Vickers hardness (1)
- WAAM (1)
- WRC 92 (1)
- Warmfester Stahl (1)
- Wind Energy (1)
- Wire Arc Additive Manufacturing (1)
- Wärmeführung (1)
- X-ray and Neutron Diffraction (1)
- X-ray and neutron diffraction (1)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (99) (entfernen)
Paper des Monats
- ja (3)
High-strength fine-grained structural steels have great potential for weight-optimized, efficient structures in many modern steel applications. Further advances in efficiency can be achieved through additive manufacturing and bionic design. Commercial high-strength filler materials for wire arc additive manufacturing (WAAM) are already provided by the consumable producers. Today, application would be strictly limited due to absence of quantitative findings or any guidelines for the industry regarding welding-related stresses and component safety during manufacturing and service. Hence, process- and material-related influences and design-related restraint conditions associated with formation of residual stresses and cold cracking risk are investigated. The aim is the accessibility of special WAAM self-restraining cold cracking tests and easy applicable processing recommendations, enabling an economical, fit-for-purpose and crack-safe WAAM of high-strength steels. This first study focuses on determination of interactions between WAAM process parameters, resulting layer geometry, microstructure and residual stresses, analyzed via X-ray diffraction. Defined reference specimens are automated welded using a special WAAM solid wire (yield strength >820 MPa). Geometric properties can be specifically adjusted by wire feed and welding speed, but cannot be varied arbitrarily, since a high heat input causes local overheating, inadmissible changes of microstructure and mechanical properties, defects and comparable high tensile residual stresses.
The residual stress (RS) in laser powder bed fusion (LPBF) IN718 alloy samples produced using a 67°-rotation scan strategy is investigated via laboratory X-ray diffraction (XRD) and neutron diffraction (ND). The location dependence of the strain-free (d₀) lattice spacing in ND is evaluated using a grid array of coupons extracted from the far-edge of the investigated specimen. No compositional spatial variation is observed in the grid array. The calculated RS fields show considerable non-uniformity, significant stress gradients in the region from 0.6 to 2 mm below the surface, as well as subsurface maxima that cannot be accounted for via XRD. It is concluded that failure to determine such maxima would hamper a quantitative determination of RS fields by means of the stress balance method.
AbstractThe sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures, like mobile or ship cranes. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of global and local welding-induced stresses may lead to crack formation and component failure, particularly in interaction with the degradation of the microstructure and mechanical properties of high-strength steels during the repair process. However, manufacturers hardly have any information about these issues and there is a lack of recommendations and guidelines to take these safety-relevant aspects into account in adequate repair concepts. The aim of this research is to derive recommendations for repair concepts appropriate to the stresses and materials involved providing a basis for standards and guidelines to avoid cold cracking, damage and expensive reworking especially for high-strength steels. Part 1 of this study involves systematic investigations of influences of shrinkage restraint during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures. The quantification of the shrinkage restraint of repair weld joints was achieved by means of experimental and numerical restraint intensity analysis. In welding experiments with self-restrained slot specimens, restraint intensity and introduction of hydrogen via the welding arc using anti spatter spray were varied systematically to analyse the effect on welding result, residual stresses and cold cracking. It could be shown that increasing restraint intensities result in significantly higher transverse residual stress levels. In the case of hydrogen introduction S500MLO showed no cold cracking independent of the restraint conditions. However, S960QL was found to be considerably cold cracking sensitive if hydrogen is introduced. With increasing restraint intensity length and number of cold cracks increases significantly. Part 2 [1] of this study is focussed on microstructure and residual stresses due to gouging and stress optimization via adequate heat control parameters in repair welding.
Influence of support configurations on the characteristics of selective laser-melted Inconel 718
(2018)
Samples fabricated using two different support configurations by following identical scan strategies during selective laser melting of superalloy Inconel 718 were characterized in this study. Characterization methods included optical microscopy, electron back-scattered diffraction and x-ray diffraction residual stress measurement. For the scan strategy considered, microstructure and residual stress development in the samples were influenced by the support structures. However, crystallographic texture intensity and the texture components formed within the core part of the samples were almost independent of the support. The formation of finer grains closer to the support as well as within the columnar grain boundaries resulted in randomization and texture intensity reduction by nearly half for the sample built on a lattice support. Heat transfer rates dictated by the support configurations in addition to the scan strategy influenced the microstructure and residual stress development in selective laser-melted Inconel 718 samples.
Stresses in repair welding of high-strength steels—part 2: heat control and stress optimization
(2024)
In welding of high-strength steels, e.g. for foundations and erection structures of wind energy plants, unacceptable defects can occasionally be found in the weld area, which should be removed by thermal gouging and subsequent re-welding. High shrinkage restraint of repair welds may lead to crack formation and component failure, predominantly in interaction with degraded microstructures and mechanical properties due to repair cycles. This study aims for elaboration of recommendations for repair concepts appropriate to the stresses and materials involved to avoid cold cracking, damage and expensive reworking. In part 1 [1] of this study, systematic investigations of influences of shrinkage restraint on residual stresses and cold cracking risk during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures were focussed. In this part 2, the microstructure, particularly hardness, and residual stresses due to gouging and influences of heat control parameters in repair welding are analysed. A clear reduction in residual stress after gouging can be observed, especially for the specimens with restrained transverse shrinkage. Gouging to a depth of approx. 2/3 of the seam height does not lead to a complete relaxation of the observed reaction forces. Particularly for the higher strength steel S960QL, there are pronounced areas influenced by the gouging process in which a degradation of the microstructure and properties should be assumed. Overall, the repair welds show a significant increase in the width of the weld and HAZ compared to the original weld, especially in the case of S960QL/G89. The repair welds show higher welding-induced stresses than the original welds, especially in the areas of the HAZ and the base metal close to the weld seam. This behaviour can be attributed overall to increased restraint conditions due to the remaining root weld or shorter gouge grooves. In good agreement with earlier investigations, the residual stresses transverse to the weld can be significantly reduced by upwardly limited working or interpass temperatures, and the reaction stresses resulting from high restraint conditions can be effectively counteracted. The influence of the heat input on the stress formation is low compared to the interpass temperature for both test materials.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing. The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized.
For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotronand the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates the dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.
Next to chemical composition, metallurgy and welding parameters, the intensity of restraint is one of the variables influencing solidification cracking. Tests like the Houldcroft Test, rate the hot cracking susceptibility indirectly on the amount of restraint the welding can endure without cracking. Modern lightweight steel construction welds can be subject to a larger amount of restraint due to their high-strength nature compared to classical use cases. By varying the plate thickness of Controlled Thermal Severity (CTS) tests produced out of S1100 QL, it was possible to vary the intensity of restraint on fillet welds at a high level. Testing was conducted with four different filler wires for Metal Active Gas (MAG) welding, including three solid and one metal-cored wire. In addition, two sets of welding parameters were tested. The first set with high heat input and high welding speed was shown to be more prone to solidification cracking compared to the second set with lower heat input and welding speed. The results show an increase in solidification cracking with increasing restraint severity.
This article focuses on the selective placement of additional LTT layers to generate compressive residual stresses in fatigue-critical areas of conventional weld joints. This enables an economical solution without effecting the integrity of welded joints. For this, longitudinal stiffeners made of high-strength steel were gas metal arc welded using conventional welding consumable in the first layer. Afterwards, a chromium-nickel alloyed LTT welding consumable was deposit on front sides of the stiffeners. By varying the welding parameters, different weld geometries of the LTT filler metal could be analyzed. The effects of additional LTT layers were investigated with regards to residual stresses, microstructure and strength. X-ray residual stresses measurements show that the residual stresses at the failure critical weld toe are significantly reduced by using additional LTT layers. While the conventional weld is characterized by tensile residual stresses, compressive residual stresses can be detected at the LTT weld. The level of residual stresses is influenced by the geometry of the LTT layer. Additional LTT layers with a high offset to the conventional weld generate more compressive residual stress in the HAZ than with a low offset. Therefore, the weld geometry has a considerable impact on the residual stress profile.
Influence of machining on residual stresses in additive manufactured high-strength steel components
(2024)
This study focuses on the effect of machining on the residual stresses and distortion of WAAM specimens. Defined specimens were welded fully automatically with a special WAAM solid wire (yield strength >820 MPa) with different geometric designs. The residual stresses state before and after cutting of the AM structure from the substrate plate were analyzed by means of X-ray diffraction on the specimen surface and complementary by 3d deformation analyses using photogrammetry. The results reveal significant influences of the geometry on the relaxation and redistribution of residual stresses.
MVT testing was conducted in Transvarestraint mode in multiple welding conditions and under a range of bending speeds. The materials observed were high strength filler metals used in GTAW namely DIN EN ISO 16834-A G 69 4 M21 Mn3Ni1CrMo (G69), 16834-A G 89 6 M21 Mn4Ni2CrMo (G89 6), 16834-A G 89 5 M21 Mn4Ni2,5CrMo (G89 5) and a filler wire 18276-A T 89 4 ZMn2NiCrMo M M21 1 H5 (T89). For evaluation light optical microscope pictures were used. Pixels containing cracks were manually segmented using a self-written program. Out of the segmented images data including crack length, position and area can be calculated for every crack. The results show dependencies of solidification cracking on the test parameters.
Diese Studie konzentriert sich auf den Einfluss der Bearbeitung auf die Eigenspannungen und den Verzug von WAAM-Proben. Definierte Proben wurden vollautomatisch mit einem speziellen WAAM-Massivdraht (Streckgrenze >820 MPa) mit unterschiedlichen geometrischen Designs geschweißt. Der Eigenspannungszustand vor und nach dem Abtrennen der AM-Struktur von der Substratplatte wurde mittels Röntgenbeugung an der Probenoberfläche analysiert und durch 3D-Verformungsanalysen mittels Photogrammetrie ergänzt. Die Ergebnisse zeigen einen signifikanten Einfluss der Geometrie auf die Relaxation und Umverteilung der Eigenspannungen.
Der Vortrag befasst sich mit der gezielten Einbringung zusätzlicher LTT-Lagen zur Erzeugung von Druckeigenspannungen in ermüdungskritischen Bereichen von konventionellen Schweißverbindungen. Dies ermöglicht eine wirtschaftliche Lösung, ohne die Integrität der Schweißverbindungen zu beeinträchtigen. Dazu wurden Längssteifen aus hochfestem Stahl in der ersten Lage mit konventionellem Schweißzusatzwerkstoff mittels Metall-Lichtbogenschweißen geschweißt. Anschließend wurde ein Chrom-Nickel-legierter LTT-Schweißzusatz auf die Stirnseiten der Steifen aufgebracht. Durch Variation der Schweißparameter konnten verschiedene Schweißnahtgeometrien des LTT-Zusatzwerkstoffs analysiert werden.
The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also
affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to validate the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was assessed using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While the WRC ’92 diagram predictions were deemed accurate to acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, though the values were higher, and scatter was wider, and the conversion factor is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds.
The Varestraint test and its variant Transvarestraint are one of the most widely used techniques for evaluating a material solidification cracking sensitivity during welding. The result of such tests is a crack length which is proportional to the material’s cracking susceptibility. Nevertheless, the welding and load parameters can unintentionally influence the crack length, which in some cases can distort the material evaluation. An approach is described as to how these effects can be assessed with the aid of a digital crack analysis. The crack lengths are compared position-dependently with their possible propagation due to the weld pool movement during continuous loading. The index derived from this can be used by the operator to evaluate his test parameters. In addition, a comparison of the results of different Varestraint setups is made possible. Alongside experimental results, a numerical sensitivity analysis is presented on how individual welding and loading parameters can affect the crack lengths.
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed.
Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet.
Die Verwendung hochfester Feinkornbaustähle hat für viele Anwendungen des Stahlbaus ein großes Potenzial für gewichtsoptimierte, effiziente Strukturen mit ho-her mechanischer Beanspruchbarkeit. Weitere Zugewinne an Effizienz sind durch generative Fertigungsschritte sowie bionische Bauweisen erzielbar. Hierzu stehen bereits kommerzielle hochfeste drahtförmige Zusatzwerkstoffe für formgebendes MSG-Schweißen zur Verfügung. Dem Einsatz stehen noch fehlende quantitative Aussagen zu den fertigungsbedingten Beanspruchungen und der Bauteilsicherheit während Herstellung und Betrieb im Wege. Dies betrifft insbesondere prozess- sowie materialbedingte Einflüsse und die konstruktive Schrumpfbehinderung verbunden mit der Ausbildung hoher Zugeigenspannungen und damit zusammenhängenden Kaltrissbildung.
Hierfür wurden im Projekt detaillierte und anwenderbezogene Kenntnisse zu den komplexen Wechselwirkungen zwischen Schweißprozess und Wärmeführung während der Fertigung, der metallurgischen Vorgänge und insbesondere der vorliegenden konstruktiven Einflüsse auf die entstehenden Eigenspannungen erarbeitet, um ein frühzeitiges Bauteilversagen aufgrund eines hohen fertigungsbedingten Beanspruchungsniveaus bis hin zu einer Rissbildung während der Fertigung sicher zu vermeiden. Gleichzeitig wurden die Einflüsse auf die mechanisch-technologischen Gütewerte systematisch analysiert. Zudem wurden die Auswirkungen trennender Verfahren durch Entfernen der Substratplatte sowie durch die spanende Bearbeitung der Vorformlinge zu Endbauteilgeometrien geklärt, da diese unmittelbar den Eigenspannungszustand beeinflussen und deutlichen Verzug der Bauteile auslösen.
Für das generative Schweißen konnten Verarbeitungsempfehlungen sowie Normenvorgaben erarbeitet werden. Dies hilft insbesondere KMU eine wirtschaftliche, beanspruchungsgerechte und risssichere generative Fertigung von Bauteilen aus hochfesten Feinkornbaustählen zu ermöglichen.
The effect of two types of scanning strategies on the grain structure and build-up of Residual Stress (RS) has been investigated in an as-built IN718 alloy produced by Laser Powder Bed Fusion (LPBF). The RS state has been investigated by X-ray diffraction techniques. The microstructural characterization was performed principally by Electron Backscatter Diffraction (EBSD), where the application of a post-measurement refinement technique enables small misorientations (< 2°) to be resolved. Kernel average misorientation (KAM) distributions indicate that preferably oriented columnar grains contain higher levels of misorientation, when compared to elongated grains with lower texture. The KAM distributions combined with X-ray diffraction stress maps infer that the increased misorientation is induced via plastic deformation driven by the thermal stresses, acting to self-relieve stress. The possibility of obtaining lower RS states in the build direction as a consequence of the influence of the microstructure should be considered when envisaging scanning strategies aimed at the mitigation of RS.
Beim Schweißen höherfester Stähle mit LTT-Zusatzwerkstoffen im Wurzelbereich der Schweißverbindung wird eine Erhöhung der Kaltrisssicherheit durch die Erzeugung von Druckeigenspannungen erreicht.
Es sind mechanische Gütewerte und Eigenspannungen in Abhängigkeit der Randbedingungen, insbesondere der Wärmeführung und des Nahtaufbaus im Wurzelbereich, systematisch zu ermitteln. Durch das Ableiten von Verarbeitungsempfehlungen wird eine sichere und optimale Handhabung der LTT-Zusätze ermöglicht.
Ziel ist die Entwicklung eines Maßnahmenkatalogs für die schweißtechnische Verarbeitung von LTT-Zusatzwerkstoffen zur Kaltrissvermeidung im Wurzelbereich höherfester Schweißverbindungen speziell für den Offshore-Bereich.
In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Influence of deposition hatch length on residual stress in selective laser melted Inconel 718
(2018)
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.
The phase transformation under various cooling rates and in different HAZ regions for high-strength armour steel was analysed by dilatometry. To develop a continuous cooling transformation (CCT) diagram, the samples were heated up to a peak temperature of 1250 °C to achieve a coarse-grained microstructure and then cooled down with a cooling time t 8/5 varying from 3 to 240 s. Analysis of dilatation curves revealed the austenite decomposition process, during which transformation temperatures were determined. The results showed martensitic transformations for all welding-relevant cooling times. Furthermore, to analyse different heat-affected subzones of the weld, the peak temperature was varied between 550 and 1250 °C at a constant cooling time t 8/5 of 6 s. The simulated coarse-grained heat-affected zone (CGHAZ) and fine-grained-heat affected zone (FGHAZ) showed only martensitic transformations with transformation temperatures below 400 °C. The steel exhibited an inhomogeneous hardness with hardening in the CGHAZ and FGHAZ and softening in the intercritical and subcritical HAZ. The physically simulated microstructure was validated by a real hybrid laser-arc weld microstructure.
The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts
(2018)
The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.
The avoidance of failures during the fabrication or operation of petrochemical reactors made of creep-resistant, low-alloy steels as 13CrMoV9-10 requires still research despite over 60 years of international investigations in the field of stress relief cracking. The quality of modern base materials and filler metals leads to the fact that previously known crack causes, such as impurities of S or P, recede into the background. Rather, the causes are increasingly to be found in the fabrication process. Investigations on the influence of heat control on the stresses in welded components and thus on the stress relief cracking sensitivity under realistic manufacturing conditions are not yet available. This work is subdivided in two parts. Part 1 of this study focused on the effect of heat control during submerged arc welding on the stresses. For this purpose, a testing facility was applied, which allows to observe the forces and moments accumulating during welding or heat treatment in a component-like specimen under shrinkage restraint. The stress acting in the specimen increases with higher preheat/interpass temperatures and higher heat input. During the heat treatment, the stresses are relieved. Nevertheless, cracks are formed already during heating. The total crack length correlates with the heat input.
Welding of 13CrMoV9-10 vanadium steel requires care due to an increased susceptibility to stress relief cracking during post weld heat treatment. Previous research into the crack formation in creep-resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gathered regarding the crack formation during post weld heat treatment considering real-life restraint conditions. This work is subdivided in two parts. Part I showed that an increasing heat input during submerged arc welding under restraint led to an increasing stress level in the joint prior to the post weld heat treatment. The magnitude of stress relief cracking observed in the heat-affected zone after the post weld heat treatment is affected by the heat input. In Part II of this work, the cracks and the associated microstructure which occurred under restraint were studied. The application of a Special acoustic emission analysis indicated that the cracks formed in a temperature range between 300 and 500 °C during the post weld heat treatment. The toughness in the heat-affected zone of the restrained welds was affected by the welding heat input.
Microstructural analyses of all specimens revealed accelerated aging due to precipitation of carbides during post weld heat treatment under restraint.
Laser powder bed fusion (LPBF) of Ni-based superalloys shows great potential for high temperature applications, for example, as a burner repair application for gas turbines where the thin-walled structure is important. It motivates this work to investigate the evolution of microstructure and the anisotropic mechanical behavior when plate-like specimens are built with a thickness from 4 mm down to 1 mm. By performing texture analysis using neutron diffraction, a clear transition in fiber texture from <011> to <001> is indicated when the specimen becomes thinner. The residual stress shows no thickness dependence, and at the subsurface the residual stress reaches the same level as the yield strength. Due to the rough as-built surface, a roughness compensation method for mechanical properties of thin-walled structures is outlined and demonstrated. Tensile tests from room temperature up to 700 ◦C have been carried out. Anisotropic mechanical behavior is found at all temperatures, which is strongly related to the anisotropic texture evolution. Stronger texture evolution and grain rotations are discovered when the tensile loading is applied along the building direction. The mechanical behavior has been compared to a wrought material, where the high dislocation density and the subgrain structure of the LPBF material result in a higher yield strength. Combining the statistical texture analysis by neutron diffraction with mechanical testing, EBSD grain orientation mapping and the investigation of dislocation structures using transmission electron microscopy, this work illustrates the significance of texture for the thin-wall effect and anisotropic mechanical behavior of LPBF materials.
Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system with a load capacity of 2 MN specifically developed for online monitoring of stress formation and cracking are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be quantified in-situ during welding and post weld heat treatment. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. Elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of mechanical stresses resulting from welding on stress relief cracking is demonstrated by the example of a creep resistant steel. Reheat cracks were monitored online during post weld heat treatment.
Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum load capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing. The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized. For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotronand the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates the dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im ersten Teil dieses Beitrages werden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes präsentiert. Dies beinhaltet zunächst die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Schweißgefüge und deren Härte mit dem Ziel, reproduzierbare Verbindungseigenschaften für die nachfolgende Schwingfestigkeitsprüfung herzustellen.
Der zweite Teil des Beitrages beschäftigt sich mit den dazugehörigen Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz. Das verwendete Schweißdetail ist eine Verbindungsschweißung am Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht). Weitergehend wird eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit werden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallo-grafisch charakterisiert. Die Ergebnisse zeigen, dass LTT-Zusatzwerkstoffe unter Einhaltung wesentlicher Konstruktionsrichtlinien zu einem deutlichen Anstieg der Schwingfestigkeit führen. Dadurch kann das Leichtbaupotential hochfester Stahlgüten genutzt werden.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a dominant role concerning so-called stress relief cracking (SRC) typically during post weld heat treatment (PWHT). Besides specific metallurgical factors (like secondary hardening due to reprecipitation), high tensile residual stresses are a considerable influence factor on SRC.
For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using Tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-Profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-remelted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases comparable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im ersten Teil dieses Beitrages werden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes präsentiert. Dies beinhaltet zunächst die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Schweißgefüge und deren Härte mit dem Ziel, reproduzierbare Verbindungseigenschaften für die nachfolgende Schwingfestigkeitsprüfung herzustellen. Der zweite Teil des Beitrages beschäftigt sich mit den dazugehörigen Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz.
Das verwendete Schweißdetail ist eine Verbindungsschweißung am Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht). Weitergehend wird eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit werden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Die Ergebnisse zeigen, dass LTT-Zusatzwerkstoffe unter Einhaltung wesentlicher Konstruktionsrichtlinien zu einem deutlichen Anstieg der Schwingfestigkeit führen. Dadurch kann das Leichtbaupotential hochfester Stahlgüten genutzt werden.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a domi-nant role concerning so-called stress relief cracking (SRC) typically during post weld heat treat-ment (PWHT). Besides specific metallurgical factors (like secondary hardening due to re-precipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-re-melted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases compa-rable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
Compared to conventional welding consumables using low transformation temperature (LTT) filler materials is an innovative method to mitigate tensile residual stresses due to delayed martensite transformation of the weld. For the effective usage of LTT filler materials, a deeper understanding of the complex processes that lead to the final residual stress state during multipass welding is necessary. Transformation kinetics and the strain evolution of multi-pass welds during welding were investigated in situ at the beamline HEMS@PETRAIII, Germany. Compared to conventional welds, the total strain was reduced and compression strain was achieved when using LTT filler materials. For an optimal use of the LTT effect in the root of multi-pass welds, the alloying concept must be adapted taking care of dilution.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im ersten Teil dieses Beitrages werden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes präsentiert. Dies beinhaltet zunächst die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Schweißgefüge und deren Härte mit dem Ziel, reproduzierbare Verbindungseigenschaften für die nachfolgende Schwingfestigkeitsprüfung herzustellen.
Der zweite Teil des Beitrages beschäftigt sich mit den dazugehörigen Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz.
Das verwendete Schweißdetail ist eine Verbindungsschweißung am Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht). Weitergehend wird eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit werden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Die Ergebnisse zeigen, dass LTT-Zusatzwerkstoffe unter Einhaltung wesentlicher Konstruktionsrichtlinien zu einem deutlichen Anstieg der Schwingfestigkeit führen. Dadurch kann das Leichtbaupotential hochfester Stahlgüten genutzt werden.
In the present study, the susceptibility to HAC of the HSLA steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same weld heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded Implant-test [ ] was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). But in all specimens, cracks initiated at the notch root of the spiral notch of the implants within the coarse-grained HAZ. However, the test series with Mod. SA showed a significant extension of the time-to-failure of several hours compared to tests carried out with Conv. A, see Fig. 1a. The reason is the deeper weld penetration in case of Mod. SA (Fig. 1b and Fig. 1c), which causes longer diffusion path for hydrogen. The fracture topography of the ruptured implant specimens with Conv. A was typical ductile in specimen center and quasi-cleavage like at the edge of the specimens. When using Mod. SA, the topography changed to primarily quasi-cleavage fracture topography with shares of intergranular fracture and secondary crack appearance.
The control of friction and wear is a major concern in many industrial applications. A promising method for tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in a deterministic pattern where needed on highly stressed surfaces, i.e., on forming or cutting tools.
However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free metal matrix composite with a high share of homogeneously distributed particles and, especially, high implant hardness. In this study, TiN, TiC, and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel were investigated.
Although all powder materials had grain sizes smaller than 10 μm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (∼64%) was observed for TiB2. By scanning electron microscopy and energy dispersive x-ray spectroscopy, it was also shown that a significant share of the preplaced particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By x-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in situ formation of TiC particles, which was proven by electron backscatter diffraction.
In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown
the most promising results.
Low transformation temperature (LTT) welding consumables offer an innovative approach to increase the fatigue strength of welded high-strength steel structures. LTT welding consumables are characterized by a martensitic phase transformation near ambient temperature, which generates compressive residual stresses in the weld and heat affected zone (HAZ). The aim is to achieve a weld geometry, which generate high compressive residual stresses at the fatigue crack critical weld toe.
Longitudinal stiffeners were gas metal arc welded using a conventional welding consumable; the base material was a high strength steel S700M. A chromium-nickel alloyed LTT consumable was deposit subsequently just on front sides of the stiffeners. Different welding parameters led to varying cross sections of the weld. The residual stresses were determined using X-ray diffraction (XRD) in the crack critical HAZ.
When using only the conventional, the HAZ is characterized by high tensile residual stresses. The additional application of the LTT alloy leads to a significant reduction of the tensile residual stresses. Depending on the weld geometry, even compressive residual stresses can be observed at the weld toe
Low Transformation Temperature (LTT)-Schweißzusätze sind ein innovativer Ansatz, um Eigenspannungen in Schweißnähten zu reduzieren. Dieser Vortrag behandelt neben den Einfluss der LTT-Schweißzusätze auch deren Naht-Ausführungen. Die unterschiedlichen LTT-Nahtgeometrien haben einen signifikanten Einfluss auf den Eigenspannungsabbau in der Schweißnaht und der Wärmeeinflusszone (WEZ).
The use of Low Transformation Temperature (LTT) filler materials is an innovative way to reduce welding residual stresses. The generation of compressive residual stresses in the weld and heat-affected zone can lead to an improvement of the fatigue life of high-strength welds. However, high-alloy filler metals can be prone to solidification cracking. Two important LTT alloys were evaluated under variable welding and loading parameters using the Modified Varestraint/Transvarestraint (MVT) test. Initially conflicting results were interpreted using a newly developed image-based crack detection routine [1]. Based on the melt pool dimensions, the shape of the isotherms is reconstructed, and the theoretical crack growth along numerically determined crystallization paths is considered in relation to the cracks observed. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate.
Wire arc additive manufacturing (WAAM) enables the efficient production of weight-optimized modern engineering structures. Further increases in efficiency can be achieved by using high-strength structural steels. Commercial welding consumables for WAAM are already available on the market. Lack of knowledge and guidelines regarding welding residual stress and component safety during production and operation leads to severely limited use for industry applications. The sensitive microstructure of high-strength steels carries a high risk of cold cracking; therefore, residual stresses play a crucial role. For this reason, the influences of the material, the WAAM process, and the design on the formation of residual stresses and the risk of cold cracking are being investigated. The material used has a yield strength of over 800 MPa. This strength is adjusted via solid solution strengthening and a martensitic phase transformation. The volume expansion associated with martensite formation has a significant influence on the residual stresses. The focus of the present investigation is on the additive welding parameters and component design on their influence on hardness and residual stresses, which are analyzed by means of X-ray diffraction (XRD). Reference specimens (hollow cuboids) are welded fully automated with a systematic variation of heat control and design. Welding parameters and AM geometry are correlated with the resulting microstructure, hardness, and residual stress state. Increased heat input leads to lower tensile residual stresses which causes unfavorable microstructure and mechanical properties. The component design affects heat dissipation conditions and the intensity of restraint during welding and has a significant influence on the residual stress.