Crack and fatigue resistance are relevant evaluation criteria for welded joints and are decreased by tensile residual
stresses resulting from the welding and cooling process, while compressive residual stresses can have a positive
influence on the characteristics mentioned. In order to generate compressive residual stresses, a set of post weld
treatment procedures is available, like shot peening, hammering, etc. These procedures have the disadvantage that
they are time and cost extensive and have to be applied after welding. As another point, such technologies can only
produce compressive stresses at the top surface, i.e. can only contribute to the reduction of the risk of cracks initiated
at the surface, like fatigue cracks. A chance to generate compressive stresses over the complete weld joint during the
welding procedure is offered by the so-called Low Transformation Temperature (LTT -) filler wires. Compared to
conventional wires, these materials show lower phase transformation temperatures, which can work against coolingrelated
tensile stresses, resulting from respective shrinkage restraint. In consequence, distinct compressive residual
stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially
applicable to high-strength steel welding. Welds produced with different LTT filler wires have shown different levels
and distributions of the resulting residual stresses depending on the specific transformation temperature. The
transformation temperatures are determined by temperature measurement. Classical X-ray diffraction as well as
diffraction methods using high energy synchrotron radiation have been used for residual stress analysis. By means of
high energy synchrotron diffraction in reflection mode residual stress depth gradients can be determined nondestructively.
The phase selective nature of the diffraction measurements enables the simultaneous determination of
the phase specific residual stresses of all contributing crystalline phases within one experiment. The application of
white beam diffraction implies recording of a multitude of diffraction lines within the energy range of the provided
energy spectrum of the white beam. By this means phase specific residual stress depth distributions up to distances of
150 ìm below the surface can be analysed for steel using the energy dispersive set-up of the HMI-beamline EDDI at
the Bessy site, Berlin, providing an energy range between 20-150 keV. As a side effect quantitative phase analysis can
be carried out using white energy dispersive diffraction e.g. the determination of the content of retained austenite in the
weld.
The application of high-strength fine-grained structural steels with yield strengths greater than or equal to 690 MPa expands because of present light weight design trends. The requirements regarding the welded components safety increased due to high loading capacity. This determines a sustainable and economic application as well. However, high welding residual stresses could diminish the components safety, especially due to high restraint conditions in component or repair welds. Therefore, this work is concerned with global and local welding stresses, especially crack-critical welding stresses in the HAZ and while root welding due to the restraint conditions. Restraint intensities of real components were analysed and realised with two different weld tests, alongside two different plate dimensions and steel grades. A comparison of the test results showed several significant effects for heat control and restraint intensity regarding restraint forces and local welding stresses. Among these effects, substantial influences were found for the filler metal selection with partially altered results for root and filler beads. Local stresses of weld seam and HAZ were affected differently.
The results reported in this research study are part of a larger EU RFCS (Research Fund for Coal and Steel) project where the aim is to study the fatigue behavior of improved welds in high strength steels by utilizing different improvement techniques. In this particular study LTT (Low Transformation Temperature) weld filler material have been investigated and their possibility to improve the fatigue strength. The characteristic of these filler material is that they undergo phase transformation at temperature close to room temperature which will reduce the tensile residual stress in the weld and in some cases result in compressive residual stresses. Two different LTT alloy compositions have been developed, with different Ms (Martensite Start) temperatures in order to study the amount of tensile/compressive residual stresses produced by these wires. Welding residual stress measurements were carried out by X-ray diffraction technique. Plates with welded longitudinal attachments were fabricated in 700 MPa and 960 MPa steel grades using different LTT filler materials. These specimens were fatigue tested in constant and variable amplitude loading and the fatigue test results were compared with results from specimen welded with conventional weld filler material.
Controlling the level of mostly detrimental residual stresses already during the welding process would be highly attractive as time and cost consuming post processing may be prevented. Therefore, in this study, the approach using suitable alloy concepts with reduced phase transformation temperatures has been evaluated concerning the interactions between transformation temperature, transformation kinetics and resulting residual stresses. Ideal tools for observing these phenomena in-situ are diffraction techniques. For that purpose, a special setup was developed allowing for localized observation of phase transformation kinetics during a real welding process by energy dispersive synchrotron diffraction (EDXRD). In the present work, this setup was successfully applied for the first time in order to characterize a selection of alloys especially designed for residual stress control. The results demonstrate that in-process observation is highly suitable for characterizing and discussing phase transformation sensitive phenomena like residual stress formation. Furthermore, it was proven that residual stresses can be effectively controlled by means of an adjusted alloy design.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a domi-nant role concerning so-called stress relief cracking (SRC) typically during post weld heat treat-ment (PWHT). Besides specific metallurgical factors (like secondary hardening due to re-precipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-re-melted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases compa-rable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input, and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analyzed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behavior, welding, and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively.
High-strength steels with yield strengths ≥ 690 MPa are becoming increasingly significant for modern steel constructions. Both quenched and tempered (QT) high-strength steels and steels produced by the thermo-mechanically controlled process (TMCP) are currently available. TMCP-steels are usually provided with a typical mill scale. Apart from the manufacturing process these steels differ also in their chemical composition. The influence of these differences are investigated here with focus on the residual stresses formed during TIG welding. Bead on plate welds have shown characteristic residual stress distributions depending on the type of steel as well as on the heat input and preheat temperature. The following work demonstrates that the fluid flow, induced by the elements present in the mill scale, leads to a deeper penetration of the material. This can also lead to increased residual stresses in the surface of the weld and the HAZ. Furthermore, higher heat input and preheat temperature can induce higher tensile residual stresses − which are evident in the present study.
Additive manufacturing (AM) by selective laser melting (SLM) offers ample scope for producing geometrically complex parts as compared to the traditional subtractive manufacturing strategies. However, the residual stresses which develop during the process can limit the application of SLM parts because they can reduce the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing. This study aims at the characterization of residual stresses in SLM parts by using different measurement techniques. The material used is the nickel based super Alloy 718. Microstructure as well as surface and bulk residual stresses were characterised. For residual stress analysis X-ray, synchrotron and neutron diffraction were applied. The results show different residual stress states dependent on the penetration depth in the sample offered by the different measurement techniques. Samples of Alloy 718 manufactured by SLM process can show high tensile residual stresses in the surface as high as the yield strength of the wrought alloy. Residual stresses in the bulk show considerably lower stress values.