Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (81) (entfernen)
Schlagworte
- Residual stress (21)
- Residual stresses (18)
- Welding (16)
- Additive manufacturing (11)
- High-strength steels (10)
- Phase transformation (9)
- Restraint (8)
- Martensite (7)
- Neutron diffraction (6)
- Process parameters (6)
Organisationseinheit der BAM
- 9 Komponentensicherheit (38)
- 9.4 Integrität von Schweißverbindungen (38)
- 8 Zerstörungsfreie Prüfung (14)
- 8.5 Röntgenbildgebung (13)
- 9.2 Versuchsanlagen und Prüftechnik (13)
- 5 Werkstofftechnik (7)
- 5.0 Abteilungsleitung und andere (4)
- 5.1 Mikrostruktur Design und Degradation (4)
- 9.0 Abteilungsleitung und andere (3)
- 9.6 Additive Fertigung metallischer Komponenten (2)
- 8.0 Abteilungsleitung und andere (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
- 9.3 Schweißtechnische Fertigungsverfahren (1)
Paper des Monats
- ja (3)
Laser powder bed fusion (LPBF) of Ni-based superalloys shows great potential for high temperature applications, for example, as a burner repair application for gas turbines where the thin-walled structure is important. It motivates this work to investigate the evolution of microstructure and the anisotropic mechanical behavior when plate-like specimens are built with a thickness from 4 mm down to 1 mm. By performing texture analysis using neutron diffraction, a clear transition in fiber texture from <011> to <001> is indicated when the specimen becomes thinner. The residual stress shows no thickness dependence, and at the subsurface the residual stress reaches the same level as the yield strength. Due to the rough as-built surface, a roughness compensation method for mechanical properties of thin-walled structures is outlined and demonstrated. Tensile tests from room temperature up to 700 ◦C have been carried out. Anisotropic mechanical behavior is found at all temperatures, which is strongly related to the anisotropic texture evolution. Stronger texture evolution and grain rotations are discovered when the tensile loading is applied along the building direction. The mechanical behavior has been compared to a wrought material, where the high dislocation density and the subgrain structure of the LPBF material result in a higher yield strength. Combining the statistical texture analysis by neutron diffraction with mechanical testing, EBSD grain orientation mapping and the investigation of dislocation structures using transmission electron microscopy, this work illustrates the significance of texture for the thin-wall effect and anisotropic mechanical behavior of LPBF materials.
Wire arc additive manufacturing (WAAM) enables the efficient production of weight-optimized modern engineering structures. Further increases in efficiency can be achieved by using high-strength structural steels. Commercial welding consumables for WAAM are already available on the market. Lack of knowledge and guidelines regarding welding residual stress and component safety during production and operation leads to severely limited use for industry applications. The sensitive microstructure of high-strength steels carries a high risk of cold cracking; therefore, residual stresses play a crucial role. For this reason, the influences of the material, the WAAM process, and the design on the formation of residual stresses and the risk of cold cracking are being investigated. The material used has a yield strength of over 800 MPa. This strength is adjusted via solid solution strengthening and a martensitic phase transformation. The volume expansion associated with martensite formation has a significant influence on the residual stresses. The focus of the present investigation is on the additive welding parameters and component design on their influence on hardness and residual stresses, which are analyzed by means of X-ray diffraction (XRD). Reference specimens (hollow cuboids) are welded fully automated with a systematic variation of heat control and design. Welding parameters and AM geometry are correlated with the resulting microstructure, hardness, and residual stress state. Increased heat input leads to lower tensile residual stresses which causes unfavorable microstructure and mechanical properties. The component design affects heat dissipation conditions and the intensity of restraint during welding and has a significant influence on the residual stress.
In situ EDXRD study of MAG-welding using LTT weld filler materials under structural restraint
(2017)
Welding using low transformation temperature (LTT) filler materials is an innovative approach to mitigate detrimental welding residual stresses without cost-intensive post weldtreatments. Due to the local Generation of compressive residual stresses in the weld line by means of a delayed martensite transformation a significant enhancement of the cold cracking resistance of highly stressed welded components can be expected. For the effective usage of These materials a deeper understanding of the microstructural evolution inside the weld material is necessary to determine the complex processes that cause the residual stress formation during welding. Solid-state phase transformation kinetics and the evolution of strain in LTT weld filler materials are monitored in-situ at the instrument ID15A at the ESRF in Grenoble, France. The transferability to real components is implemented by using a realistic MAG welding process under consideration of structural restraint. During welding of multilayer joints, the phase Transformation and phase specific strain evolution of each individual layer is investigated in transmission geometry by means of energy-dispersive X-ray diffraction EDXRD using high energy synchrotron Radiation with a counting rate of 2.5 Hz. The measurement results of a 10% Cr / 10% Ni LTT weld filler are compared to data monitored for the conventional weld filler material G89. The in-situ data clearly indicate a strong effect on the local strain evolution and the formation of compressive strain. This results from the restraint volume expansion during the postponed austenite to martensite transformation of the LTT weld filler, which counteracts the thermal shrinkage. In contrast, for the conventional weld filler material the thermal contraction strains lead to tensile residual strain during welding. Furthermore, the results of in-situ observation during welding Show that the transformation kinetic is dependent on the welding sequence.
Solidification Cracking Assessment of LTT Filler Materials by Means of Varestraint Testing and μCT
(2020)
Investigations of the weldability of metals often deal with hot cracking, as one of the most dreaded imperfections during weld fabrication. The hot cracking investigations presented in this paper were carried out as part of a study on the development of low transformation temperature (LTT) weld filler materials. These alloys allow to mitigate tensile residual stresses that usually arise during welding using conventional weld filler materials. By this means, higher fatigue strength and higher lifetimes of the weld can be achieved. However, LTT weld filler materials are for example, high-alloyed Cr/Ni steels that are susceptible to the formation of hot cracks. To assess hot cracking, we applied the standardized modified varestraint transvarestraint hot cracking test (MVT), which is well appropriate to evaluate different base or filler materials with regard to their hot cracking susceptibility. In order to consider the complete material volume for the assessment of hot cracking, we additionally applied microfocus X-ray computer tomography (μCT). It is shown that by a suitable selection of welding and MVT parameter the analysis of the complete 3D hot crack network can provide additional information with regard to the hot cracking model following Prokhorov. It is now possible to determine easy accessible substitute values (e.g., maximum crack depth) for the extent of the Brittleness Temperature Range (BTR) and the minimum critical strain Pmin.
Investigations on weldability often deal with hot cracking, as one of the most popular failure during weld fabrication. The modified varestraint transvarestraint hot cracking test (MVT) is well known for the assessment of the hot cracking susceptibility of materials. The shortcoming of this approach is that the information is only from the very near surface region, which inhibits access to the characteristic of the hot crack network in the bulk. Here, we report about a new approach, illustrated in the example of low transformation temperature (LTT) weld filler materials, to monitor the entire 3D hot crack network after welding by means of microfocus X-ray computer tomography (μCT).
The subject of this study is how, and to what extent, Varestraint/Transvarestraint test results are influenced by both testing parameters and characteristics of evaluation methods. Several different high-alloyed martensitic LTT (low Transformation temperature) filler materials, CrNi and CrMn type, were selected for examination due to their rather distinctive solidification cracking behaviour, which aroused interest after previous studies. First, the effects of different process parameter sets on the solidification cracking response were measured using standard approaches. Subsequently, microfocus X-ray computer tomography (μCT) scans were performed on the specimens. The results consistently show sub-surface cracking to significant yet varying extents. Different primary solidification types were found using wavelength dispersive X-ray (WDX) analysis conducted on filler metals with varying Cr/Ni equivalent ratios. This aspect is regarded as the main difference between the CrNiand CrMn-type materials in matters of cracking characteristics. Results show that when it comes to testing of modern highperformance alloys, one set of standard Varestraint testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
The residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction.
Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized.
While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements.
Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.
This study reports on the stress relaxation potential of stress-relieving heat treatments for laser powder bed fused 316L. The residual stress is monitored non-destructively using neutron diffraction before and after the heat treatment. Moreover, the evolution of the microstructure is analysed using scanning electron microscopy. The results show, that a strong relaxation of the residual stress is obtained when applying a heat treatment temperature at 900°C. However, the loss of the cellular substructure needs to be considered when applying this heat treatment strategy.
The triaxial distribution of the residual stress in laser powder bed fused austenitic steel 316L was determined by X-ray and neutron diffraction. The residual stress analysis results were linked to the thermal history of the specimens, which were manufactured with varying inter-layer-times and scanning velocities. A clear link between the in-process temperature of the specimens and the residual stress was found, based on in-situ monitoring data.
The control of friction and wear is a major concern in many industrial applications. A promising method for tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in a deterministic pattern where needed on highly stressed surfaces, i.e., on forming or cutting tools.
However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free metal matrix composite with a high share of homogeneously distributed particles and, especially, high implant hardness. In this study, TiN, TiC, and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel were investigated.
Although all powder materials had grain sizes smaller than 10 μm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (∼64%) was observed for TiB2. By scanning electron microscopy and energy dispersive x-ray spectroscopy, it was also shown that a significant share of the preplaced particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By x-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in situ formation of TiC particles, which was proven by electron backscatter diffraction.
In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown
the most promising results.