This paper describes a modified experimental setup for the test apparatus 20-L-Sphere (also known as 20-L Siwek Chamber), that enables the test samples to be kept under inert atmospheric conditions nearly until ignition. This setup was designed to allow the determination of safety characteristics of nano powders under most critical circumstances (e.g. minimisation of the influence of oxidation before the test itself). The aim of this modification was to determine, whether or not the current setup and procedures underestimate the explosion violence and ignitability of nano powders. For this purpose, two different methods, the so called inerting method and the modified method (using a special nozzle called mushroom nozzle) are used. Both methods are described in the paper. The work includes experimental results of micrometer dusts to validate the modified method. Moreover first results of nanometer iron and aluminium dusts are presented, which were kept at inert conditions until shortly before the ignition. The tested nano iron was found to react pyrophoric, as soon as it gets in contact with air, while the tested nano aluminium did not generally show such behaviour. Tests with nano aluminium using the inerting method revealed a higher pressure rise in comparison to the standard test procedure. This could suggest a different extent of passivation. To investigate this effect more closely, further testes with more nano powders are required.
Modified setup of 20-L-sphere for the determination of safety characteristics of nano powders
(2013)
This paper describes a modified experimental setup for the test apparatus 20-L-Sphere (also known as 20-L Siwek Chamber), that enables the test samples to be kept under inert atmospheric conditions nearly until ignition. This setup was designed to allow the determination of safety characteristics of nanopowders under most critical circumstances (e.g. minimisation of the influence of oxidation before the test itself). The aim of this modification was to determine, whether or not the current setup and procedures underestimate the explosion violence and ignitability of nanopowders. The work includes experimental results of micrometer dusts to validate the modified setup. Moreover first results of nanometer iron and Aluminium dusts are presented, which were kept at inert conditions until shortly before the ignition. The tested nano iron was found to react pyrophoric, as soon as it gets in contact with air, while the tested nano Aluminium did not generally show such behaviour.
This paper describes experiences and results of experiments with several metallic dusts within the nanometer range. The nano dusts (aluminium, iron, zinc, titanium and copper) were tested in a modified experimental setup for the test apparatus 20 L-sphere (also known as 20-L Siwek Chamber), that enables the test samples to be kept under inert atmospheric conditions nearly until ignition. This setup was already introduced in earlier papers by the authors. It was designed to allow the determination of safety characteristics of nano powders under most critical circumstances (e.g. minimisation of the influence of oxidation before the test itself). Furthermore the influence of passivation on explosion behaviour is investigated and additional tests with deposited dust were carried out to describe the burning behaviour of all dusts. For a better characterisation all samples were tested with a simultaneous thermal analysis (STA). To minimise the influence of oxidation all samples were handled at inert conditions until shortly before ignition or start of the test respectively.
This paper describes experiences and results of experiments with several metallic dusts within the nanometer range. The nano dusts (aluminium, iron, zinc, titanium and copper) were tested in a modified experimental setup for the test apparatus 20 L-sphere (also known as 20-L Siwek Chamber), that enables the test samples to be kept under inert atmospheric conditions nearly until ignition. This setup was already introduced in earlier papers by the authors. It was designed to allow the determination of safety characteristics of nano powders under most critical circumstances (e.g. minimisation of the influence of oxidation before the test itself). Furthermore the influence of passivation on explosion behaviour is investigated and additional tests with deposited dust were carried out to describe the burning behaviour of all dusts. For a better characterisation all samples were tested with a simultaneous thermal analysis (STA). To minimise the influence of oxidation all samples were handled at inert conditions until shortly before ignition or start of the test respectively.
Protection from explosion events requires the determination of key safety parameters like lower explosion limit. maximum Explosion over-pressure. and maximum rate of pressure rise. These Parameters are routinely obtained through standard tests performed typically either in a 20 L -sphere or a 1 m3-container. But several aspects are worth a closer investigation. Firstly, the test apparatus must be able to disperse a fairly uniform dust cloud. However. previous investigations showed that actually the current dispersion System can be improved. Secondly, the influence of humidity on the explosivity is not considered in current standards. lt is just stated that the relative humidity should be checked and noted down.
though some provisions exist in American standards. Thirdly. the ignition delay time is sometimes modified to study the impact of the dust cloud turbulence on flame propagation but is often misunderstood.
Maybe these aspects have not been thoroughly considered for micron powders. However. in the case of nanopowders. the importance of these influencing factors was shown in order to duly evaluate explosion parameters. Experimental evidences confirm these aspects and alternative solutions will be presented.
This work presents an overview about the explosion behaviour of metallic powders from micron to nanosize.
Aluminium, magnesium, titanium, iron and zinc were considered and their explosion safety parameters were analysed as a function of their mean primary particle size either determined by BET measurements, particle size distribution. To depict the course of explosion behaviour for these metals, extensive literature review has been performed and additional experimental tests were also performed. Generally, decreasing the particle size in a metallic powder leads to a higher explosion severity. It appears that this statement is true till a critical Diameter below which the explosion severity (pmax, dp/dtmax) decreases for all the considered powders. This critical size can be explained by theoretical considerations on the nature of thermal transfer in the flame, namely by analysing the Cassel model. Finally, semi-empirical models were also developed for aluminium to highlight the specific micrometre and nanometre behaviour and the influence of turbulence, particle burning time, Diameter and concentration. The influence of these key parameters needs to be further assessed in a future work in order to better understand the mechanisms involved and to extend the scope to other powdered materials.