Organisationseinheit der BAM
- 6 Materialchemie (2)
- 6.3 Strukturanalytik (2)
Poly(l-lactide)s are synthesized and annealed at 120 °C and changes of the molecular weight distribution (MWD) are monitored by matrix-assited laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry. For example, benzyl alcohol+SnOct2 causes equilibration of odd- and even-numbered chains and the final goal of the transesterification is the most probable distribution. The underlying intermolecular transesterification is even observed at 100 and 80 °C in the solid state. However, cyclic tin mercaptide catalysts transform the initial most probable distribution into a MWD with maxima, which display a conspicuous fine structure due to a preferential crystallization of certain ring sizes. The optimum ring sizes for the crystallization are provided by ring-ring equilibration. The gradual formation of a special morphology shifts the melting temperature to values up to 187 °C. Annealing of commercial poly(l-lactide) with a cyclic tin catalyst also yields a distribution of mass peaks with a maximum showing the characteristic fine structure.
Five new catalysts are prepared from dibutyltin oxide and catechol (HCa),
2,3-dihydroxynaphthalene (NaCa), 4-tert-butyl catechol (BuCa), 4-cyano
catechol (CyCa), and 4-benzoyl catechol (BzCa), but only BuCa gives useful
results. When benzyl alcohol is used as an initiator, linear chains having
benzyl ester end groups are formed in a slow polymerization process. In
contrast to cyclic or noncyclic dibutyltin bisalkoxides, neat BuCa yields
cyclic poly(l-lactide)s via a fast ring-expansion polymerization. Under certain
conditions, a high-melting crystalline phase (Tm = 191 °C) is obtained.
At 160 °C and short reaction times even-numbered cycles are slightly
prevailing, but, surprisingly, at 120 °C, odd-numbered cycles are predominantly
formed. These results definitely prove that a ring-expansion mechanism
is operating.
Meso-Lactide was polymerized in bulk at 60, 80, and 100 °C by means of three different types of catalysts: dibutyltinsulfides (2,2-dibutyl-2-stanna-1,3-dithiolane and 2,20-dibutyl-2-stanna-1,3-dithiane), dibutyltin derivatives of substituted cate-chols (BuCa, CyCa, and BzCa), and dibutyltin derivatives of2,2 dihydroxybiphenyl (SnBi) and 2,2-dihydroxy-1,10-binaphthyl(SnNa. Only the latter two catalysts were active at 60 °C. The architecture of the resulting polylactides depends very much on the structure of the catalyst and on the temperature. At the lowest temperature (60 °C), SnBi and SnNa mainly yielded even-numbered linear chains, but SnNa also yielded even-numbered cycles at 100 °C and short reaction times. In contrast,BuCa, CyCa, and BzCa mainly yielded odd-numbered cycles, although the same catalysts yielded even-numbered linear chains when benzylalcohol was added.
With 2,2-dibutyl-2-stanna-1,3-dithiolane (DSTL) and 2-stanna-1,3-dioxa-4,5,6,7-dibenzoxepane (SnBiPh) as catalysts ring-expansion polymerizations (REP) were performed either in 2 M solution using three different solvents and two different temperatures or in bulk at 140 and 120 ◦C. A kinetically controlled rapid REP up to weight average molecular masses (Mẃs) above 300 000 was followed by a slower degradation of the molecular masses at 140 ◦C, but not at 120 ◦C Furthermore, a low molecular mass cyclic poly(L-lactide) (cPLA) with a Mn around 16 000 was prepared by polymerization in dilute solution and used as starting material for ring-ring equilibration at 140 ◦C in 2 M solutions. Again, a decrease of the molecular mass was detectable, suggesting that the equilibrium Mn is below 5 000. The degradation of the molecular masses via RRE was surprisingly more effective in solid cyclic PLA than in solution, and a specific transesterification mechanism involving loops on the surface of crystallites is proposed. This degradation favored the formation of extended-ring crystallites, which were detectable by a “saw-tooth pattern” in their MALDI mass spectra.