- Polycondensation (3) (entfernen)
Various dibutyltin derivatives were polycondensed with aliphatic ,-dicarboxylic acids having chain lengths from 4 (succinic acid) to 22 carbon atoms. White crystalline products were obtained from all experiments, and the structure of the products was independent of the synthetic method. Viscosity measurements revealed low molecular weights (n 1 500 Da) in all cases. Vapor pressure osmometry (VPO) measurements and matrix-assisted laser desorption time-of-flight (MALDI-TOF) mass spectrometry proved that cyclic dimers and trimer were formed from dicarboxylic acids having 6 to 16 carbons, but mainly the monomeric cycle from docosane dioic acid. Heating to 250°C did not change the structure. Therefore, the results indicate that the macrocycles are the result of a thermodynamically controlled ring-closing polycondensation. This means that linear high-molecular weight poly(dibutyltin dicarboxylate)s cannot exist above room temperature.
Poly(ether sulfone)s were prepared by polycondensation of silylated 4-tert-butylcatechol and 4,4?-difluorodiphenylsulfone in N-methylpyrrolidone. The feed ratio and the reaction time were varied to study the influence of stoichiometry and conversion on molecular weight and extent of cyclization. Molecular weights and molecular weight distributions (MWD)s were characterized by SEC measurements calibrated with polystyrene. Light scattering confirmed that calibration with polystyrene gives reasonable results and revealed a tendency towards a bimodal MWD for the samples rich in cycles. The MALDI-TOF mass spectrometry indicated that the extent of cyclization increased with higher conversion and with optimization of the stoichiometry. This interpretation was confirmed by 1H NMR endgroup analyses. For the samples with the highest molar masses only mass peaks of cycles were found, which were detectable up to 20 000 Da before and up to 27 000 Da after fractionation. Via the pseudo-high dilution method low molar mass poly(ether sulfone) containing more than 95 mol% of cycles were prepared, and even these low molar mass samples had broad MWDs. DSC measurements indicated that the glass transition temperatures depend on the structure of the endgroups and increase with higher fractions of cycles.