Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (80)
Sprache
- Englisch (80)
Referierte Publikation
- ja (80) (entfernen)
Schlagworte
- MALDI-TOF MS (44)
- Polylactide (39)
- Cyclization (25)
- Polycondensation (19)
- Ring-opening polymerization (13)
- Crystallization (8)
- MALDI (7)
- Crystalinity (6)
- Polyesters (6)
- Polymerization (6)
Organisationseinheit der BAM
- 6 Materialchemie (49)
- 6.3 Strukturanalytik (49)
Poly(ether sulfone)s were prepared by polycondensation of silylated 4-tert-butylcatechol and 4,4?-difluorodiphenylsulfone in N-methylpyrrolidone. The feed ratio and the reaction time were varied to study the influence of stoichiometry and conversion on molecular weight and extent of cyclization. Molecular weights and molecular weight distributions (MWD)s were characterized by SEC measurements calibrated with polystyrene. Light scattering confirmed that calibration with polystyrene gives reasonable results and revealed a tendency towards a bimodal MWD for the samples rich in cycles. The MALDI-TOF mass spectrometry indicated that the extent of cyclization increased with higher conversion and with optimization of the stoichiometry. This interpretation was confirmed by 1H NMR endgroup analyses. For the samples with the highest molar masses only mass peaks of cycles were found, which were detectable up to 20 000 Da before and up to 27 000 Da after fractionation. Via the pseudo-high dilution method low molar mass poly(ether sulfone) containing more than 95 mol% of cycles were prepared, and even these low molar mass samples had broad MWDs. DSC measurements indicated that the glass transition temperatures depend on the structure of the endgroups and increase with higher fractions of cycles.
3,5-Bis(4-fluorobenzoyl)phenol was polycondensed under various reaction conditions. Low molecular weights were obtained (Mn < 8000 Da), and MALDI-TOF mass spectrometry indicated that the chain growth was limited by cyclization. In the best mass spectra the cyclic, hyperbranched poly(ether ketone)s were detectable up to masses around 14 000 Da. When 4,4'-difluordiphenyl sulfone was added, star-shaped polymers having a diphenyl sulfone star center were formed, but cyclization was not completely suppressed. The results were compared to those obtained from "linear polycondensations" based on 4,4'-difluorobenzophenone (DFBP) and 4-tert-butylcatechol or bisphenol A. The poly(ether ketone)s of DFBP had also low molecular weights and contained high fractions of cycles. It is concluded that also in the case of hyperbranched polymers cyclization competes with propagation at any stage of the polycondensation at any concentration. Therefore, the fundamental trend of any "abn" polycondensation is the formation of star-shaped polymers having a cyclic core and hyperbranched star arms.
Copolyesters with an alternating sequence of terephthalic acid and aliphatic dicarboxylic acids were prepared with three different methods. First, dicarboxylic acid dichlorides were reacted with bis(2-hydroxyethyl)terephthalate (BHET) in refluxing 1,2-dichlorobenzene. Second, the same monomers were polycondensed at 0-20 °C in the presence of pyridine. Third, dicarboxylic acid dichlorides and silylated BHET were polycondensed in bulk. Only this third method gave satisfactory molecular weights. Matrix-assisted laser desorption/ionization time-of-flight mass spectrometry revealed that the copolyesters prepared by the pyridine and silyl methods might have contained considerable fractions of cyclic oligoesters and polyesters despite the absence of transesterification and backbiting processes. The alternating sequences and thermal properties were characterized with 1H NMR spectroscopy and differential scanning calorimetry measurements, respectively. In agreement with the alternating sequence, all copolyesters proved to be crystalline, but the crystallization was extremely slow [slower than that of poly(ethylene terephthalate)]. A second series of alternating copolyesters was prepared by the polycondensation of silylated bis(4-hydroxybut- yl)terephthalate with various aliphatic dicarboxylic acid dichlorides. The resulting copolyesters showed significantly higher rates of crystallization, and the melting temperatures were higher than those of the BHET-based copolyesters. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3371-3382, 2001
Poly(ether-sulfone)s having an identical backbone were prepared by four different methods. First, silylated bisphenol A (BSBA) was polycondensed with 4,4'-difluorodiphenyl sulfone (DFDPS) and K2CO3 in N-methylpyrrolidone with variation of the temperature. Second, analogous polycondensation were conducted using CsF as catalyst (and no K2CO3). Third, CsF-catalyzed polycondensations BSBA and DFDPS were conducted in bulk up to 290 C. Fourth, free bisphenol was polycondensed with DFDPS or 4,4'-dichlorodiphenyl sulfone and K2CO3 in DMSO with azeotropic removal of water. MALDI-TOF mass spectroscopy revealed that the first method mainly yielded cyclic poly(ether-sulfone)s which were detected up to masses around 13 000 Da. These and other results suggest that these polycondensations take a kinetically kontrolled course at tempeatures 145 C. This interpretation is also valid for the fourth method where high yields of cycles were obtained with DFDPS. With the less reactive 4,4'-dichlorodiphenyl sulfone lower conversions, lower molecular weights and lower fractions of cycles were found. In contrast to KF (resulting from K2CO3) CsF cleaves the poly(ether sulfone) backbone at temperatures > 145 C. Smaller amounts of smaller cycles were found in these CsF-catalyzed polycondensations which were in this case the result of thermodynamically controlled "back-biting degradation".
The role of cyclization in polycondensations is discussed for two different scenarios: thermodynamically-controlled polycondensation (TCPs) on the one hand and kinetically-controlled polycondensations (KCPs) on the other. The classical CarothersFlory theory of step-growth polymerization does not include cyclization reactions. However, TCPs involve the formation of cycles via back-biting degradation, and when the ringchain equilibrium is on the side of the cycles the main reaction products of the TCP will be cyclic oligomers. Two groups of examples are discussed: polycondensations of salicyclic acid derivatives (e.g. aspirin) and polycondensations of dibutyltin derivatives with long {alpha}-, {omega}-diols or dicarboxylic acids. Furthermore, various kinetically-controlled syntheses of polyesters and polyamides were studied and carefully optimized in the direction of high molecular weights. High fractions of cyclic oligomers and polymers were found by MALDI-TOF mass spectrometry, and their fractions increased with optimization of the process for molecular weight. These results disagree with the CarothersFlory theory but agree with the theoretical background of the RuggliZiegler dilution method (RZDM). When poly(ether-sulfone)s were prepared from 4,4'-difluorodiphenylsulfone and silylated bisphenol-A two different scenarios were found. With CsF as catalyst at a temperature of more than 145°C cyclic oligoethers were formed under thermodynamic control. When the polycondensation was promoted with K2CO3 in N-methylpyrolidone at ?145°C the formation of cyclic oligoethers and polyethers occurred under kinetic control. A new mathematical formula is presented correlating the average degree of polymerization with the conversion and taking into account the competition between cyclization and propagation.
2,2-Dibutyl-2-stanna-1,3-dioxepane (DSDOP) was polycondensed with bis(4-chlorothiophenyl) suberat under various reaction conditions, but only moderate molecular weights (Mn 10000) were obtained. The MALDI-TOF mass spectrosmetry revealed the formation of cyclic oligo- and polyesters in addition to linear species having OH, CO2H, and unreacted 4-chlorothiophenyl ester endgroups.
Furthermore, -Caprolactone (-CL) was polymerized with DSDOP as the initiator at monomer/initiator (M/I) ratios of 20 and 50. The resulting tin-containing macrocyclic polylactones were reacted with sebacic acid bis(4-thiocresyl)ester at three different temperatures and with different reaction times. Analogous polycondensations were conducted with suberic acid bis(4-chlorothiophenyl) ester. The presence of thioarylester endgroups in the isolated polyesters was checked by 1H NMR spectroscopy. The highest conversions were found at long reaction times (24 or 72 hours), or after the addition of pyridine and N,N-dimethylaminopyridine as catalysts. Despite high conversions, the number average molecular weights (Mn's) did not exceed values around 20000. Even in the samples having the highest molecular weights, unreacted 4-chlorothiophenylester endgroups were detected by GPC measurements evaluated with a UV-detector. It is concluded that both factors, cyclization and incomplete conversion, contribute to the limitation of the chain growth.
We prepared 2,2-dibutyl-2-stanna-1,3-dithiacycloalkanes from dibutyltin oxide and ,-dimercaptoalkanes. Heterocycles with five-, six-, seven-, or nine-ring members were used as bifunctional monomers for polycondensations with aliphatic dicarboxylic acid chlorides. These polycondensations conducted in bulk were highly exothermic and yielded poly(thio ester)s with number average molecular weights (Mn's) in the range of 5000-30,000 Da. These poly(thio ester)s proved to be rapidly crystallizing materials with melting temperatures in the range of 90-150 °C. In addition to the success of the new synthetic approach, two interesting and unpredictable results were obtained. All volatile species detectable by matrix assisted laser desorption induced-time of flight (MALDI-TOF) mass spectrometry were cyclic oligo- and poly(thio ester)s. Second, several polyesters showed a reversible first-order change of the crystal modification as identified by differential scanning calorimetry measurements and X-ray scattering with variation of the temperature. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 3656-3664, 2000
Polycondensations of 1,6-hexane diol and sebacic acid were conducted in bulk with addition of a lanthanide triflate as acidic catalyst. With exception of promethium triflate all lanthanide triflates were studied. A particularly low molecular weight was obtained with neodym triflate and the best results with samarium triflate. With Sm(OTf)3 weight average (Mw) values up to 65 kDa (uncorrected SEC data) were achieved after optimization of the reaction conditions. Comparison of these results with those obtained from bismuth, magnesium, and zinc triflates, on the one hand, and comparison with the acidities of all catalysts, on the other, indicates that the esterification mechanism involves complexation of monomer by metal ions. Preparation of multiblock copoly(ether ester)s failed due to insufficient incorporation of poly(tetrahydrofuran) diols.