The sensitivity of low-loss perfluorinated polymer optical fiber (PF-POF) to gamma radiation is investigated for on-line radiation monitoring purposes. The radiation-induced attenuation (RIA) of a commercial PF-POF based on Cytop material is measured in the visible spectral region. The fiber RIA shows strong wavelength dependence with rapid increase towards the blue side of the spectrum. The wide range of radiation sensitivities is available via careful selection of appropriate monitoring wavelength. The accessible sensitivities span from 1.6 ± 0.2 dBm-1/kGy measured at 750 nm to 18.3 ± 0.7 dBm-1/kGy measured at 420 nm. The fairly high radiation sensitivity as well as its wide tunability makes the fiber a promising candidate for a broad range of applications.
The paper presents the first complex study of Gamma radiation effects on a low-loss perfluorinated polymer optical fiber (PF-POF) based on Cytop® polymer. Influence of gamma radiation on fiber’s optical, mechanical and climatic performance is investigated. The radiation-induced attenuation (RIA) in the visible and near-infrared region (0.4 μm-1.7 mm) is measured and its origins are discussed. Besides attenuation increase, radiation is also shown to decrease the thermal degradation stability of the fiber and to increase its susceptibility to water. With regard to complex fiber transmission performance upon irradiation, the optimal operation wavelength region of PF-POF-based systems intended for use in Radiation environments is determined to be around 1.1 μm. On the other hand, the investigated fiber holds potential for low-cost RIA-based optical fiber dosimetry applications with sensitivity as high as 260 dBm⁻¹/kGy in the visible region.
We present the fabrication and characterization of a polycarbonate (PC) microstructured polymer optical fiber (mPOF) and the writing of a fiber Bragg grating (FBG) in it to obtain a polymer optical FBG sen-sor. The manufacturing process of the PC mPOF consists of multiple consecutive stages, such as casting of pol-ymer granulates into a solid rod, machining and drilling of a 3-ring hexagonal lattice of holes into it, and finally drawing into fiber. We demonstrate that the obtained PC mPOF is photosensitive and FBGs can be conveniently inscribed into it, thereby enabling FBG-based temperature and strain sensing. The PC optical fibers are for some applications an attractive alternative to conventional materials used in POF fabrication, such as polymethyl methacrylate (PMMA). In general, PC can be used at temperature up to 120 °C and breaks at considerably higher strains than PMMA.
Solution doping of commercial polymethyl methacrylate (PMMA) polymer optical fibers (POFs) is presented as a novel approach for preparation of custom cladding-doped POFs (CD-POFs). The presented method is based on a solution-mediated diffusion of dopant molecules into the fiber cladding upon soaking of POFs in a methanol-dopant solution. The method was tested on three different commercial POFs using Rhodamine B as a fluorescent dopant. The dynamics of the diffusion process was studied in order to optimize the doping procedure in terms of selection of the most suitable POF, doping time and conditions. Using the optimized procedure, longer segment of fluorescent CD-POF was prepared and its performance was characterized. Fiber’s potential for sensing and illumination applications was demonstrated and discussed. The proposed method represents a simple and cheap way for fabrication of custom, short to medium length CD-POFs with various dopants.
Solution doping of off-the-shelf plastic optical fibers (POFs) represents rather simple and cheap way for preparing custom cladding-doped POFs (CD-POFs) with short to medium lengths. CD-POFs are especially attractive for environmental sensing applications, but might be of interest for illumination task as well. In this work, the proposed doping technique is tested with three different commercial low-cost polymethyl methacrylate (PMMA) POFs; Eska CK-40 and Eska GK-40 from Mitsubishi Rayon and Raytela PGU-FB1000 from Toray. The aim of the work is to aid the selection of the most suitable fiber yielding highest optical quality of prepared CD-POFs. Firstly, the optimal doping times are determined for the individual fiber types using short fiber samples. Secondly, longer 10 m CD-POFs are prepared from all tested fibersusing the optimized doping procedure. Finally, attenuation of pristine POFs and prepared CD-POFs is measured using optical time domain reflectometry in order to characterize the impacts of the doping on fiber optical properties. In addition, the importance of post-doping drying procedure for CD-POF optical performance is investigated as well. The results suggest that, although doping of all tested fibers is generally feasible, Eska CK-40 is the most suitable candidate with regard to the Doping efficiency and fiber post-doping performance.
Here we present the fabrication of a solid-core microstructured polymer optical fiber (mPOF) made of polycarbonate (PC), and report the first experimental demonstration of a fiber Bragg grating (FBG) written in a PC optical fiber. The PC used in this work has a glass transition temperature of 145°C. We also characterize the mPOF optically and mechanically, and further test the sensitivity of the PC FBG to strain and temperature. We demonstrate that the PC FBG can bear temperatures as high as 125°C without malfunctioning. In contrast, polymethyl methacrylate-based FBG technology is generally limited to temperatures below 90°C.
Gamma radiation induced effects in perfluorinated polymer optical fibers for sensing applications
(2015)
Radiation induced attenuation in perfluorinated polymer optical fiber was investigated as a potential mean for online. in situ gamma radiation monitoring. Spectral dependence of radiation induced attenuation was measured in the visible and near infrared range. Attenuation spectrum exhibits sharp increase both towards the ultraviolet and infrared side of the spectrum with 3 distinct peaks around 1400 nm. The fiber sensitivity to gamma radiation was further evaluated at two commonly used IR wavelengths (1310nm and l550nm} by pre- and post-irradiation optical time-domain reflectometry measurements. The examined fiber is sensitive up to lOO kGy of total absorbed dose with only minor saturation towards the large dose values. The influence of gamma radiation on the fiber mechanical properties was studied as well. Up to the maximal dose of 100 kGy, no significant deterioration of fiber strength and elasticity was observed.
A systematic study of annealing behavior of drawn PMMA fibers was performed. Annealing Dynamics were investigated under different environmental conditions by fiber longitudinal shrinkage monitoring. The shrinkage process was found to follow a stretched exponential decay function revealing the heterogeneous nature of the underlying molecular dynamics. The complex dependence of the fiber shrinkage on initial degree of molecular alignment in the fiber, annealing time and temperature was investigated and interpreted. Moreover, humidity was shown to have a profound effect on the annealing process, which was not recognized previously. Annealing was also shown to have considerable effect on the fiber mechanical properties associated with the relaxation of molecular alignment in the fiber. The consequences of fiber annealing for the climatic stability of certain polymer optical fiber-based sensors are discussed, emphasizing the importance of fiber controlled pre-annealing with respect to the foreseeable
operating conditions.
Systematic investigation of annealing behavior of drawn PMMA fibers was performed. Dynamics of annealing process were measured under different environmental conditions by fiber longitudinal shrinkage monitoring. Process was found to follow stretched exponential decay function indicating heterogeneous nature of underlying molecular dynamics. Consequences of fiber annealing for climatic stability of polymer optical fiber-based sensors are discussed, emphasizing importance of fiber controlled post-fabrication annealing. Dependence of induced fiber shrinkage on annealing time, temperature and fiber drawing conditions is investigated and interpreted. In addition, strong influence of humidity on annealing process was observed, which was not recognized in previous studies. This further highlights role of fiber post-fabrication thermal treatment with respect to intended operating conditions.
In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer. Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.