Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (52)
- Beitrag zu einem Tagungsband (38)
- Beitrag zu einem Sammelband (12)
- Vortrag (6)
- Posterpräsentation (4)
- Forschungsbericht (1)
Schlagworte
- Corrosion (44)
- CCS (41)
- Steel (35)
- CO2-storage (18)
- Pipeline (17)
- High temperature corrosion (12)
- CO2-injection (9)
- Heat treatment (8)
- Supercritical CO2 (7)
- Aquifer (6)
Organisationseinheit der BAM
- 5 Werkstofftechnik (39)
- 5.1 Mikrostruktur Design und Degradation (39)
- 7 Bauwerkssicherheit (6)
- 7.6 Korrosion und Korrosionsschutz (6)
- 5.6 Glas (2)
- 8 Zerstörungsfreie Prüfung (2)
- 8.0 Abteilungsleitung und andere (2)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
Eingeladener Vortrag
- nein (6)
Basic research on the corrosive effect of flue gases has been performed at the BAM Federal Institute for Materials Research and Testing (Germany). Conditions at both high and low temperatures were simulated in specially designed experiments. Carburization occured in flue gases with high CO2 content and temperatures higher than 500 °C. In SO2 containing flue gases sulphur was detected in the oxide scale. At lower temperatures no corrosion was observed when gases with low humidity were investigated. Humidity higher than 1500 ppm was corrosive and all steels with Cr contents lower than 12% revealed corroded surfaces. At low temperatures below 10 °C a mixture of sulphuric and nitric acid condensed on metal surfaces. Acid condensation caused severe corrosion. Humidity, CO2, O2, and SO2 contents are the important factors determining corrosion. Below 300 °C acid condensation is the primary reason for corrosion. Low humidity and low temperatures are conditions which can be expected in the CO2 separation and treatment process. This work includes major conditions of the flue gas and CO2 stream in CCS plants and CCS technology.
Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection.
During the compression of emission gasses into deep geological layers (Carbon Dioxide Capture and Storage, CCS) CO2-corrosion will become a relevant safety issue. The reliability of the steels used at a geological onshore CCS-site in the Northern German Bassin 42CrMo4 (1.7225, AISI 4140) used for casing, and the injection pipe steels X46Cr13 (1.4034, AISI 420 C), X20Cr13 (1.4021, AISI 420 J) as well as X35CrMo17 (1.4122) is demonstrated in laboratory experiments. Samples were kept in a synthetic aquifer environment at T = 60 °C. This corrosive environment is then saturated with technical CO2 at a flow rate of 3 l/h. Microstructures were characterized by X-ray diffraction, light microscopy, scanning electron microscopy, and energy dispersive X-ray analysis, after a series of heat treatments (700 h to 2 years). The non-linear isothermal surface corrosion behaviour of the steels reveals surface corrosion rates around 0.10.8 mm/year, when obtained by mass gain. Severe pit corrosion (pit heights ca. 4.5 mm) are only located on the injection pipe steels. Main phases of the continuous scales are siderite FeCO3 and goethite α-FeOOH. The formation of the non-protective layer is likely to form via a
transient Fe(OH)2-phase.
The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, C02-corrosion of the injection pipe steels has to be given special attention when engineering CCSsites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Cr 13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a C02-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the C02 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO} in both types of Steel.
The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CC>2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Crl3 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC>2-saturated synthetic aquifer environment similar to possible geological onshore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCCh in both types of Steel.
When engineering a Carbon Capture and Storage site (CCS) local corrosion (pitting) of the injection pipe steel may become an issue when emission gasses from oxyfuel power plants are compressed into deep geological layers. This highly corrosive environment arises when the flue gasses, mainly composed of CO2 , are injected into saline aquifer water. Immediately carbonic acid is formed causing corrosive attack of the injection steels. The influence of heat treatment on the local corrosion resistance was demonstrated in laboratory experiments at 60 °C and ambient pressure for three steels X46Cr13 (1.4034), X20Cr13 (1.4021) and X5CrNiCuNb16-4 (1.4543) under a similar liquid corrosive environment as found at a geological onshore CCS-site in the Northern German Bassin.
We present a new method for the complete three-dimensional (3D) calibration of scanning probe microscopes (SPM) and other high-resolution microscopes, e.g., scanning electron microscopes (SEM) and confocal laser scanning microscopes (CLSM), by applying a 3D micrometre-sized reference structure with the shape of a cascade slope-step pyramid. The 3D reference structure was produced by focused ion beam induced metal deposition. In contrast to pitch featured calibration procedures that require separate lateral and vertical reference standards such as gratings and step height structures, the new method includes the use of landmarks, which are well established in calibration and measurement tasks on a larger scale. However, the landmarks applied to the new 3D reference structures are of sub-micrometre size, the so-called 'nanomarkers'. The nanomarker coordinates are used for a geometrical calibration of the scanning process of SPM as well as of other instrument types such as SEM and CLSM. For that purpose, a parameter estimation routine involving three scale factors and three coupling factors has been developed that allows lateral and vertical calibration in only one sampling step. With this new calibration strategy, we are able to detect deviations of SPM lateral scaling errors as well as coupling effects causing, e.g., a lateral coordinate shift depending on the measured height position of the probe.