2,2-Dibutyl-2-stanna-1,3-dioxepane (DSDOP) was polycondensed with bis(4-chlorothiophenyl) suberat under various reaction conditions, but only moderate molecular weights (Mn 10000) were obtained. The MALDI-TOF mass spectrosmetry revealed the formation of cyclic oligo- and polyesters in addition to linear species having OH, CO2H, and unreacted 4-chlorothiophenyl ester endgroups.
Furthermore, -Caprolactone (-CL) was polymerized with DSDOP as the initiator at monomer/initiator (M/I) ratios of 20 and 50. The resulting tin-containing macrocyclic polylactones were reacted with sebacic acid bis(4-thiocresyl)ester at three different temperatures and with different reaction times. Analogous polycondensations were conducted with suberic acid bis(4-chlorothiophenyl) ester. The presence of thioarylester endgroups in the isolated polyesters was checked by 1H NMR spectroscopy. The highest conversions were found at long reaction times (24 or 72 hours), or after the addition of pyridine and N,N-dimethylaminopyridine as catalysts. Despite high conversions, the number average molecular weights (Mn's) did not exceed values around 20000. Even in the samples having the highest molecular weights, unreacted 4-chlorothiophenylester endgroups were detected by GPC measurements evaluated with a UV-detector. It is concluded that both factors, cyclization and incomplete conversion, contribute to the limitation of the chain growth.
Numerous polycondensations of isosorbide and suberoyl chloride or other aliphatic dicarboxylic acid dichlorides were performed with pyridine as a catalyst and HCl acceptor. The reaction conditions were varied to optimize both the molecular weight and the fraction of cyclic oligo- and polyesters. Furthermore, we attempted to obtain the cyclic monomer by catalyzed back-biting degradation of the molten cyclic polyesters above 220 °C in vacuo. The polyesters were characterized by viscosity and size exclusion chromatographic measurements as well as matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. In selected cases, mixtures of linear and cyclic polyesters were treated with a hot solution of partially methylated ß-cyclodextrin in methanol. This treatment allowed for a selective extraction of the linear chains up to approximately 5000 Da.