Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (143)
- Vortrag (51)
- Beitrag zu einem Tagungsband (30)
- Beitrag zu einem Sammelband (28)
- Posterpräsentation (13)
- Buchkapitel (10)
Schlagworte
- Femtosecond laser (28)
- Laser-induced periodic surface structures (LIPSS) (26)
- Femtosecond laser ablation (24)
- Laser ablation (23)
- Laser processing (14)
- Radiation protection (12)
- Silicon (11)
- Laser cleaning (10)
- Ablation (9)
- Materialbearbeitung (9)
Organisationseinheit der BAM
- 6 Materialchemie (56)
- 6.2 Material- und Oberflächentechnologien (56)
- 9 Komponentensicherheit (4)
- 9.5 Tribologie und Verschleißschutz (4)
- 6.7 Materialsynthese und Design (3)
- 4 Material und Umwelt (2)
- 4.1 Biologische Materialschädigung und Referenzorganismen (2)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
Paper des Monats
- ja (3)
The ultrafast laser ablation of silicon has been investigated experimentally and theoretically. The theoretical description is based on molecular dynamics (MD) simulations combined with a microscopic electronic model. We determine the thresholds of melting and ablation for two different pulse durations =20 and 500 fs. Experiments have been performed using 100 Ti:Sap-phire laser pulses per spot in air environment. The ablation thresholds were determined for pulses with a duration of 25 and 400 fs, respectively. Good agreement is obtained between theory and experiment.
KrF excimer laser ablation of polyethylene terephthalate (PET), polyimide (PI) and polycarbonate (PC) in air was studied by an in situ monitoring technique using a microphone. The microphone signal generated by a short acoustic pulse represented the etch rate of laser ablation depending on the laser fluence, i.e., the ablation strength. From a linear relationship between the microphone output voltage and the laser fluence, the single-pulse ablation thresholds were found to be 30 mJ cm-2 for PET, 37 mJ cm-2 for PI and 51 mJ cm-2 for PC (20-pulses threshold). The ablation thresholds of PET and PI were not influenced by the number of pulses per spot, while PC showed an incubation phenomenon. A microphone technique provides a simple method to determine the excimer laser ablation threshold of polymer films.
The laser ablation behaviour of ion-doped glass filter materials under irradiation with femtosecond laser pulses was investigated with respect to spot size and repetition rate. The damage threshold fluence of Schott BG18 depends on the size of the irradiated area. The effect is discussed in terms of a defect-site model.
High-power optical multimode fibers are essential components for materials processing
and surgery and can limit the reliability of expensive systems due to breakdown at the end faces.
The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of
the technology applied. The aim of this paper is the identification of technological parameters that
are crucial for the fiber quality.
Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of
OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed
were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage
thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms,
which underwent different thermal treatments above the transition temperature, were tested with
respect to their damage resistivity. Single and multi pulse LIDT measurements were done in
accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm
wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were utilized. For the fibers, LIDT
values (1-on-1, 1064 nm and 532 nm) increased with growing CCDR and with decreasing drawing
velocities.
Optical multimode fibers made of fused silica are widely used for transmission of high power laser pulses. Bending of fibers creates mechanical stress inside the material. The bend stress of a fiber can be calculated from bend radius, geometrical fiber parameters and Young's Modulus of the fiber core material and reaches typically values of 220 MPa. A thermo-elastic model of Kusov et al. predicts a quadratic dependence of laser-induced damage threshold fluence with applied stress.
In the present study, fiber preform material F300 (Heraeus) was loaded mechanically with pressures up to 220 MPa representing 20% of the pressure resistance of fused silica. Bulk laser-induced damage thresholds (LIDT) were evaluated using a longitudinal multimode Q-switched Nd:YAG laser (1064 nm) at a pulse duration of 12 ns with polarization states parallel and perpendicular to the stress direction. LIDT of fused silica samples of about 700 J/cm2 were found. LIDT did not show a dependence on mechanical pressure and polarization state which is a consequence of the small ratio of maximum applied stress (220 MPa) to Young's Modulus of fused silica (72.5 GPa).
Single-pulse damage thresholds of hydrogenated amorphous carbon (a-C:H) films were measured for 8-ns laser pulses at 532-nm wavelength. Layer thicknesses from below the optical penetration depth to above the thermal diffusion length (60 nm13 µm) were examined. After correction of the damage-threshold values for the fraction of energy effectively absorbed by the material, the damage threshold was found to increase linearly with the layer thickness, also for film thicknesses below the optical penetration depth of a-C:H. The threshold fluence reached the bulk value for a layer thickness equal to the thermal diffusion length. The thermal diffusion coefficient was obtained from fitting the experimental data. Several phenomena like graphitization, blistering, exfoliation, and ablation were observed for different fluence regimes and film thicknesses.
Hydrogenated amorphous carbon layers were deposited on BK7 glass in a plasma-assisted chemical vapor deposition
process. Low and high refracting films with thicknesses d ranging from 11 nm to 5.8 µm were produced having refractive
indices n between 1.68 and 2.41 and linear absorption coefficients of α~100 cm-1 and α~20000 cm-1 at 800 nm wavelength as a result of different plasma modes. Laser ablation thresholds Fth in dependence on d were determined using 30-fs laser pulses. Low absorbing layers show a constant Fth while Fth increases with rising d up to the optical penetration depth of light α-1 for high absorbing films.