Optical multimode fibers are applied in materials processing (e.g. automotive industry), defense, aviation technology, medicine and biotechnology. One challenging task concerning the production of multimode fibers is the enhancement of laser-induced damage thresholds. A higher damage threshold enables a higher transmitted average power at a given fiber diameter or the same power inside a thinner fiber to obtain smaller focus spots.
In principle, different material parameters affect the damage threshold. Besides the quality of the preform bulk material itself, the drawing process during the production of the fiber and the preparation of the fiber end surfaces influence the resistance. Therefore, the change of the laser-induced damage threshold of preform materials was investigated in dependence on a varying thermal treatment and preparation procedure.
Single and multi-pulse laser-induced damage thresholds of preforms (F300, Heraeus) were measured using a Q-switched Nd:YAG laser at 1064 nm wavelength emitting pulses with a duration of 15 ns, a pulse energy of 12 mJ and a repetition rate of 10 Hz. The temporal and spatial shape of the laser pulses were controlled accurately.
Laser-induced damage thresholds in a range from 150 J cm-2 to 350 J cm-2 were determined depending on the number of pulses applied to the same spot, the thermal history and the polishing quality of the samples, respectively.
Single- and multi-shot ablation thresholds of gold films in the thickness range of 311400 nm were determined employing a Ti:sapphire laser delivering pulses of 28 fs duration, 793 nm center wavelength at 1 kHz repetition rate. The gold layers were deposited on BK7 glass by an electron beam evaporation process and characterized by atomic force microscopy and ellipsometry. A linear dependence of the ablation threshold fluence Fth on the layer thickness d was found for d ≤ 180 nm. If a film thickness of about 180 nm was reached, the damage threshold remained constant at its bulk value. For different numbers of pulses per spot (N-on-1), bulk damage thresholds of ~0.7 J cm-2 (1-on-1), 0.5 J cm-2 (10-on-1), 0.4 J cm-2 (100-on-1), 0.25 J cm-2 (1000-on-1), and 0.2 J cm-2 (10000-on-1) were obtained experimentally indicating an incubation behavior. A characteristic layer thickness of Lc 180 nm can be defined which is a measure for the heat penetration depth within the electron gas before electronphonon relaxation occurs. Lc is by more than an order of magnitude larger than the optical absorption length of α-1 12 nm at 793 nm wavelength.