Crystallization behavior in different atmospheres (air, Ar, and 7% H2/Ar) of lithium iron phosphate glass (33Li2O33Fe2O31Nb2O5–33P2O5 (LFNP)) powders with different sizes of 2–1000 µm was examined. The crystallization peak temperature (Tp) in Ar and 7% H2/Ar decreased with decreasing the particle size of glass powders, but the value of Tp in air was independent of particle size. The crystallized glass obtained by heating to Tp showed the formation of the α-Li3Fe2(PO4)3 and LiFePO4 crystalline phases. Fe2O3 crystals were formed only in the inside of crystallized glass plates in the heating in air. The crystallization of LiFePO4 was largely enhanced in the particle size of <2 µm during the heating in Ar and 7% H2/Ar atmospheres. The main crystallization mechanism in LFNP glass was found to be surface crystallization. Significant shrinkages were observed for glass compacts (pellets) in the heating in 7% H2/Ar. These results suggest that controlling particle sizes and atmospheres enables the design the morphology of LiFePO4 crystals in LFNP glass.
The crystallization behavior of sodium ion conductive Na2MnP2O7 glass was examined to clarify the crystallization mechanism. The formation of thermodynamically metastable phase, layered Na2MnP2O7, at the surface of the glass occurred. Heat treatment at 430 °C for 3 h lead to surface crystals of Na2MnP2O7 oriented with the (101) direction perpendicular to the sample surface. As the heat treatment temperature increased, the glass-ceramic samples deformed, and the presence numerous micro bubbles due to dissolved water was detected.