Ideally, bioactive ceramics for use in alveolar ridge augmentation should possess the ability to activate bone formation and, thus, cause the differentiation of osteoprogenitor cells into osteoblasts at their surfaces. Therefore, in order to evaluate the osteogenic potential of novel bone substitute materials, it is important to examine their effect on osteoblastic differentiation. This study examines the effect of rapidly resorbable calcium-alkali-orthophosphates on osteoblastic phenotype expression and compares this behavior to that of β-tricalcium phosphate (TCP) and bioactive glass 45S5. Test materials were three materials (denominated GB14, GB9, GB9/25) with a crystalline phase Ca2KNa(PO4)2 and with a small amorphous portion containing either magnesium potassium phosphate (GB14) or silica phosphate (GB9 and GB9/25, which also contains Ca2P2O7); and a material with a novel crystalline phase Ca10[K/Na](PO4)7 (material denominated 352i). SaOS-2 human bone cells were grown on the substrata for 3, 7, 14, and 21 days, counted, and probed for an array of osteogenic markers. GB9 had the greatest stimulatory effect on osteoblastic proliferation and differentiation, suggesting that this material possesses the highest potency to enhance osteogenesis. GB14 and 352i supported osteoblast differentiation to the same or a higher degree than TCP, whereas, similar to bioactive glass 45S5, GB9/25 displayed a greater stimulatory effect on osteoblastic phenotype expression, indicating that GB9/25 is also an excellent material for promoting osteogenesis.
Solubility and ingrowth behaviour of degradable and figuline calcium alkaline phosphate cements
(2012)
The thrust of the investigations presented here is to point out the degradation behaviour in vitro and the ingrowth behaviour in vivo of four different calcium alkaline phosphate cements. Two of the figuline and mouldable composites consist of the crystalline phase Ca2KNa(PO4)2 and two of the crystalline phase Ca10[K/Na](PO4)2 each containing 2wt% medium gel strength porcine gelatin. Furthermore A-TCP was added to both Ca10[K/Na](PO4)2 cements as a hardening supporting reactant. The testing material groups differ in small amorphous portions containing either silica phosphate (GB9), magnesium potassium phosphate (GB14) or diphosphates (401545 and 401545(70)). The respective composites show a monomodal particle size distribution (d50~7µm; span~4) and an average total porosity around 28vol%.For the solubility studies cylindrical samples (d=6mm; h=12mm) were stored in a 0.1mol TRIS buffer solution and incubated at 37°C for maximum 50 weeks. The storage solution was analysed and renewed every week. The results are plotted cumulative. For the in vivo studies critical size defects were dissected to mandibles in a sheep model in which a 1cm³ area of the bottom of the mandibles was surgically resected and replaced with the figuline cements whereas the mouldability allows the reconstruction of the original outer contour without draining off even when replacing upside down.
Biocompatible materials such as porous bioactive calcium phosphate ceramics or titanium are regularly applied in dental surgery: ceramics are used to support the local bone regeneration in a given defect, afterwards titanium implants replace lost teeth. The current gold standard for bone reconstruction in implant dentistry is the use of autogenous bone grafts. But the concept of guided bone regeneration (GBR) has become a predictable and well documented surgical approach using biomaterials (bioactive calcium phosphate ceramics) which qualify as bone substitutes for this kind of application as well. We applied high resolution synchrotron microtomography and subsequent 3d image analysis in order to investigate bone formation and degradation of the bone substitute material in a three-dimensional manner, extending the knowledge beyond the limits of classical histology. Following the bone regeneration, titanium-based implants to replace lost teeth call for high mechanical precision, especially when two-piece concepts are used in order to guaranty leak tightness. Here, synchrotron-based radiography in comparison with classical laboratory radiography yields high spatial resolution in combination with high contrast even when exploiting micro-sized features in these kind of highly attenuating objects. Therefore, we could study micro-gap formation at interfaces in two-piece dental implants with the specimen under different mechanical load. We could prove the existence of micro-gaps for implants with conical connections as well as to study the micromechanical behavior of the mating zone of conical implants during loading. The micro-gap is a potential issue of failure, i. e. bacterial leakage which can induce an inflammatory process.