The roll-on-roll-off passenger ferry MV ESTONIA sank during the night of 28 September 1994 in the Baltic Sea. In October 2000, divers recovered two palm-sized test pieces from the front bulkhead of the wreck. The investigators analysed these specimens to determine whether there were any indications of deliberate blasting. Since the wreck had been submerged for almost six years, it was clear that chemical traces would not be present on the surfaces of the test pieces. Therefore, the investigators performed comparative tests on shipbuilding steel to find a microstructural criterion that exclusively characterises a blast. The shipyard Jos. L. Meyer, Germany, had built the ESTONIA and supplied shipbuilding steel plates similar to that used for building the vessel in 1979/1980. The comparative tests comprised mechanical tests, shot peening tests and blasting tests using different explosives. Testing demonstrated that blasting always formed twinned ferrite grains in the microstructure over the whole cross-section of each of the 8 mm thick comparative plates. Although one of the original test pieces of the ESTONIA showed deformation twins, this was only confined up to 0.4 mm underneath the surfaces and not spread over the whole cross-section. Comparative shot peening tests produced the very same pattern of subsurface deformation twins. Therefore, the twins detected in the microsection of the test pieces of the ESTONIA wreck traced back to the shot peening process performed by the shipyard in 1979/1980 and not to a deliberate blast.
Investigations on the breakdown of a heat recovery steam generator during the initial operation run
(2014)
Several years ago, in 2003, an industrial heat recovery steam generator in charge of generating process steam in a petrochemical refinery was installed and prepared for initial operation. The steam generator enclosed an evaporator section and a superheater section consisting mainly of bundles of tubes with the longest up to several metres in length. During initial operation test runs severe leakages in the evaporator and superheater modules became noticeable. The test runs were stopped and after disassembly, through-wall cracks in several tube bends were found. BAM was commissioned to carry out the investigations in order to find out the reasons for the failure of the tubes. During on-site inspection a number of relevant damaged components and parts were selected and taken away to the laboratories for detailed inspection. Planned analyses were to comprise metallographic as well as fractographic investigations, mechanical fatigue testing and experimental as well as finite element vibration analyses on specimens and components. Soon, the fracture mechanism was found to be mechanical fatigue due to the fact that the examined fracture surfaces showed the very characteristic beachmarks and colouring patterns. To identify the particular loading and time at which crack initiation and crack propagation took place, experimental and numerical vibration analyses of specific tubes as well as mechanical fatigue tests on tube bends were carried out. Thus it was possible to identify the eigenfrequencies of individual tubes, to estimate the dynamic response as well as the nominal stresses and, hence, experimentally characterise the in-service fatigue strength of the components. Mechanical and thermal comparative tests on tube bends were performed simulating the conditions during the initial test run in order to get crack surfaces comparable to that of the originally damaged components. Thereby it became obvious that the fatigue cracks were initiated by vibrations the tube bundles were exposed to during rail transport from the manufacturers site to the place of installation. Based on these results, the damaged components could be repaired or exchanged without modification of the construction, but the rules relating packaging and securing for shipping had to be revised.