Filtern
Dokumenttyp
- Zeitschriftenartikel (16)
- Vortrag (3)
- Beitrag zu einem Tagungsband (2)
- Buchkapitel (1)
Sprache
- Englisch (22) (entfernen)
Schlagworte
- Non-metallic inclusions (4)
- Failure analysis (2)
- Fatigue (2)
- Fatigue crack (2)
- Fatigue fracture (2)
- Pores (2)
- Railway axles (2)
- Safe life design (2)
- Undamped structural elements (2)
- Accompanying measures (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
Unexpected wind-induced vibrations of the hangers have caused an early fatigue crack on specific steel components and joints of a railway bridge over the Elbe River at Lutherstadt Wittenberg, Germany. During regular periodic inspection a fatigue crack of approximately 240 mm length was found near a butt weld of the longest hanger. The hanger was immediately secured by welded butt straps across the crack. Based on experimental investigations of hanger vibrations additional bracings were added between the hangers to avoid wind-induced vibrations. The weld heat influence zone which was affected by high cyclic stresses was replaced by new material.
Nevertheless it was impossible to determine sufficient remaining service life for those remaining bridge components that were exposed to extreme high real load cycles. The grinding of the affected steel surfaces was the key element of the remedial actions. Furthermore, additional fracture mechanic calculations were carried out in order to assess the remaining service life of the welded joints. In this respect, the calculation approach used by Deutsche Bahn AG was compared to further procedures from the mechanical engineering field. These investigations showed that the studied, repaired components have both, bearing and fatigue capacities within the validity of standards.
The roll-on-roll-off passenger ferry MV ESTONIA sank during the night of 28 September 1994 in the Baltic Sea. In October 2000, divers recovered two palm-sized test pieces from the front bulkhead of the wreck. The investigators analysed these specimens to determine whether there were any indications of deliberate blasting. Since the wreck had been submerged for almost six years, it was clear that chemical traces would not be present on the surfaces of the test pieces. Therefore, the investigators performed comparative tests on shipbuilding steel to find a microstructural criterion that exclusively characterises a blast. The shipyard Jos. L. Meyer, Germany, had built the ESTONIA and supplied shipbuilding steel plates similar to that used for building the vessel in 1979/1980. The comparative tests comprised mechanical tests, shot peening tests and blasting tests using different explosives. Testing demonstrated that blasting always formed twinned ferrite grains in the microstructure over the whole cross-section of each of the 8 mm thick comparative plates. Although one of the original test pieces of the ESTONIA showed deformation twins, this was only confined up to 0.4 mm underneath the surfaces and not spread over the whole cross-section. Comparative shot peening tests produced the very same pattern of subsurface deformation twins. Therefore, the twins detected in the microsection of the test pieces of the ESTONIA wreck traced back to the shot peening process performed by the shipyard in 1979/1980 and not to a deliberate blast.
Investigations on the breakdown of a heat recovery steam generator during the initial operation run
(2014)
Several years ago, in 2003, an industrial heat recovery steam generator in charge of generating process steam in a petrochemical refinery was installed and prepared for initial operation. The steam generator enclosed an evaporator section and a superheater section consisting mainly of bundles of tubes with the longest up to several metres in length. During initial operation test runs severe leakages in the evaporator and superheater modules became noticeable. The test runs were stopped and after disassembly, through-wall cracks in several tube bends were found. BAM was commissioned to carry out the investigations in order to find out the reasons for the failure of the tubes. During on-site inspection a number of relevant damaged components and parts were selected and taken away to the laboratories for detailed inspection. Planned analyses were to comprise metallographic as well as fractographic investigations, mechanical fatigue testing and experimental as well as finite element vibration analyses on specimens and components. Soon, the fracture mechanism was found to be mechanical fatigue due to the fact that the examined fracture surfaces showed the very characteristic beachmarks and colouring patterns. To identify the particular loading and time at which crack initiation and crack propagation took place, experimental and numerical vibration analyses of specific tubes as well as mechanical fatigue tests on tube bends were carried out. Thus it was possible to identify the eigenfrequencies of individual tubes, to estimate the dynamic response as well as the nominal stresses and, hence, experimentally characterise the in-service fatigue strength of the components. Mechanical and thermal comparative tests on tube bends were performed simulating the conditions during the initial test run in order to get crack surfaces comparable to that of the originally damaged components. Thereby it became obvious that the fatigue cracks were initiated by vibrations the tube bundles were exposed to during rail transport from the manufacturers site to the place of installation. Based on these results, the damaged components could be repaired or exchanged without modification of the construction, but the rules relating packaging and securing for shipping had to be revised.
Intramedullary hip screws (IMHSs) are implanted for the fixture of pertrochanteric femoral fractures (thigh bone). The present work investigates the failure of an IMHS implant after the rehabilitation period which required a revision surgery where the upper femur had to be replaced by a hip endoprosthesis. Due to litigation the corresponding failure analysis was conducted at BAM Federal Institute for Materials Research and Testing and is the subject of this article. By order of the customer failure causes due to material and fabrication failures should be particularly investigated. Therefore, thorough fractographic, chemical as well as metallographic investigations were carried out. In order to assess possible fabrication failures selected dimensions of the components were compared with the technical drawings and the surface topography was analysed.
The investigation revealed several causes for the fracture of the lag screw which is the implant component intended to fix the position of the femoral head. These are in descending order of relevance: (1) the screw was placed incorrectly and therefore had a smaller bending stiffness, (2) the femoral fracture zone was not stable, i.e., the lag screw 'moved out' of its proper position and (3) the laser marking on the lag screw was relatively large and led to a metallurgical notch at the now, because of the above mentioned points, severely stressed region. A material- or fabrication failure was not the root cause for the fracture of the lag screw. It was mainly due to its incorrect placement during surgery and the instability of the bone fracture. Furthermore, the implant geometry with 130° was not well-suited for the patient's anatomy. A 135°-IMHS might have been biomechanically preferable. Based on the determined failure causes and influences a relative lifetime estimation led to about 10% of the lifetime of a correctly placed 135°-IMHS assuming a sufficiently stable bone fracture zone.
On July 9, 2008 a high speed train derailed in Cologne main Station, Germany at a low speed because an axle was broken. Fortunately, the derailment happened at a low speed so that nobody was injured. The reason for the broken axle was investigated and it turned out that most likely large inclusions located shortly undemeath the surface in a T-transition were the origin of the final crack. Basing on that result, a systematic investigation on existing safety assessments of railway axles was performed. This results in an analysis of the production process of axles and in a critical review of existing of existing assessments. Improvements and future developments are outlined.
In July 2008 an ICE3 high speed train rated for 330 km/h service speed derailed during departure from Cologne, Central Station, Germany, due to fatigue failure of one of the driving axles. The train was emergency stopped immediately and, due to low travel speed at this point, no serious injuries occurred to passengers. Referring to public interest, the public attorneys office solicited the German Federal Institute for Materials Research and Testing (BAM) for the analysis of the root cause.
No deviations from specification were found in the geometries of the basic parts of the bogie or the wheelset assembly. Inspection of the axle fragments using standard acoustic non-destructive testing (NDT) techniques revealed no additional cracks and no indications of oversized discontinuities. Metallographic and chemical inspection of the axle material and its microstructure revealed all parameters to be acceptable except for an elevated impurity level.
The fracture surfaces of the axle fragments were heavily damaged due to some continued travel after final breakage on the high speed line before Cologne Central Station. Extensive visual inspection of the remaining beachmarks was carried out to find the origin of the fatigue crack. The region of the crack origin was located near the axle surface but could not be analysed in detail due to secondary damage. Fatigue was identified as the mechanism of crack growth until final fracture, but the reasons for crack initiation initially remained unclear.
Neither standard NDT techniques nor metallography according to the relevant axle specifications were able to identify inclusions in the material that could have served as crack initiation sites. However, discontinuities were detected near the crack origin in micro computer tomography and ultrasonic immersion testing. Subsequent metallographic sample preparation was targeted to specific areas based on the location coordinates of the flaws identified by these NDT techniques. These revealed non-metallic inclusions that were much larger than admissible for the relevant specifications. It is likely that the fatigue crack in the highly loaded axle volume initiated at those non-metallic inclusions.
The safety assessment of railway axles is based on a two-stage approach: fatigue strength design and regular inspections which, in terms of a general safety philosophy refer to safe-life and damage tolerance concepts. Starting with a recent failure case, a broken axle of a German high speed train, a discussion is presented on issues of both safety levels. These include ideas for finite life design, the treatment of in-service effects on the fatigue strength due to flying ballast damage and corrosion pits, the effect of corrosion on fatigue crack initiation and propagation, potential effects of non-metallic inclusions in steels, the way to detect them by quality control measures and reliability aspects of non-destructive testing with respect to the detection of fatigue cracks. Proposals are made how the safety level could be further improved.