Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (24)
- Zeitschriftenartikel (16)
- Beitrag zu einem Sammelband (16)
- Beitrag zu einem Tagungsband (12)
- Forschungsbericht (4)
- Sonstiges (2)
- Posterpräsentation (2)
Schlagworte
- Superalloys (6)
- Creep (5)
- Rafting (5)
- Extensometer (4)
- Nickel-base superalloys (4)
- Single crystal (4)
- TMF (4)
- CMSX-4 (3)
- Creep-deformation (3)
- Lattice distortion (3)
- SC16 (3)
- Thermo-mechanical fatigue (3)
- Axial-torsional Loading (2)
- Creep damage (2)
- Creep deformation (2)
- Dehnungsfehler (2)
- Einkristall (2)
- Fatigue (2)
- Gamma titanium aluminide (2)
- ISO 6892-1 (2)
- LCF (2)
- Measurement uncertainty (2)
- Microstructural degradation (2)
- Microstructure (2)
- Ni-base superalloy (2)
- Normung (2)
- Single-crystal nickel-base superalloys (2)
- Superlegierung (2)
- Temperaturschwankungen (2)
- Test methods (2)
- Thermo-mechanical Fatigue (2)
- Thermo-mechanische Ermüdung (2)
- X-ray diffraction (2)
- Accuracy (1)
- Analysis (1)
- Anisotropy of mechanical properties (1)
- Axial-torsional Belastung (1)
- Axial-torsional loading (1)
- Axial-torsional loadings (1)
- Carbon capture and storage (CCS) (1)
- Carburisation (1)
- Chaboche (1)
- Computersimulation (1)
- Constitutive law (1)
- Corrosion behaviour (1)
- Creep deformed (1)
- Damage (1)
- Dehngeschwindigkeit (1)
- Dehnungsgeregelt (1)
- Ductile grey cast iron (1)
- Dynamische Temperaturmessung (1)
- EN 10002-1 (1)
- EN 10275 (1)
- EN GJS X SiMo 4.05 (1)
- EN GJS X SiMo 5.1 (1)
- Effect of creep damage on LCF (1)
- Ermüdungsprüfung (1)
- European TENSTAND project (1)
- Fatigue testing standards (1)
- Force controlled TMF testing (1)
- Fractography (1)
- Gamma-Titanium Aluminide (1)
- Geschwindigkeitseinfluß (1)
- Grauguss mit globularem Graphit (1)
- Harmonisation (1)
- Heat resistant steels (1)
- High efficiency power plants (1)
- High temperature (1)
- High temperature LCF (1)
- Hocheffiziente Kraftwerke (1)
- Hochtemperatur (1)
- Hochtemperatur-LCF (1)
- Hochtemperaturverhalten (1)
- Hot corrosion (1)
- ISO 12111 (1)
- ISO 15363 (1)
- ISO materials testing standards (1)
- ISO mechanical testing standard (1)
- Kohlendioxidabscheidung und -speicherung (CCS) (1)
- Korrosionsverhalten (1)
- Lattice mismatch (1)
- Lebensdauer-Regeln (1)
- Lebensdauerabschätzung (1)
- Low Cycle Fatigue (1)
- Low cycle fatigue (1)
- Low-cycle fatigue (1)
- Low-cycle-fatigue (1)
- Materialidentifikation (1)
- Materialmodell (1)
- Mechanical properties (1)
- Mechanische Eigenschaften (1)
- Mehrachsige Belastung (1)
- Modeling (1)
- Modelling (1)
- Multiaxial fatigue (1)
- Nickel base superalloy (1)
- Nimonic 90 (1)
- Normative annex (1)
- Porosity (1)
- Power generation (1)
- Precipitates (1)
- Prior exposure (1)
- Product standard (1)
- Relative error (1)
- Relaxation (1)
- Schädigung (1)
- Secondary direction (1)
- Single crystal nickel-base superalloys (1)
- Spannungsgeregelt (1)
- Spröd-Duktil-Übergangstemperatur (1)
- Standardisation (1)
- Strain controlled tensile testing (1)
- Strain error (1)
- Stress rate (1)
- Superalloy (1)
- Superheater materials (1)
- Synchrotron x-ray radiation (1)
- TENSTAND (1)
- TENSTAND WP4 Report (1)
- TMF-Versuch (1)
- TNB-V5 (1)
- Temperature fluctuation (1)
- Thermal drift (1)
- Thermal expansion (1)
- Thermische Drift von Extensometern (1)
- Thermo-Mechanical strain-controlled fatigue testing (1)
- Thermomechanical (1)
- Thermomechanical fatigue (TMF) (1)
- Thermomechanische Ermüdung (1)
- Thermomechanische Ermüdung (TMF) (1)
- Titanaluminide (1)
- Titanium Aluminide (1)
- Titanium aluminides (1)
- Tnsile testing (1)
- Tube ring hydraulic pressure test (1)
- Turbine (1)
- Uncertainty annex (1)
- Uncertainty calculation (1)
- Vienna agreement (1)
- Viscoplasticity (1)
- Viskoplastische Materialmodelle (1)
- Warmfeste Stähle (1)
- X-ray-diffraction (1)
- Zugversuch (1)
- fatigue standard committee (1)
- temperature fluctuation of extensometers (1)
- von Mises Vergleichsspannung (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (24)
Tensile testing according to EN 10002-1 is one of the basic mechanical tests to characterise the mechanical properties of metallic materials. This testing procedure has been regularly under development for many decades in order to modify and amend it and to bring it up to an up to date standard. Today tensile testing for quality control in metals manufacturing industry is routinely performed automatically with computer controlled testing machines. Due to economical needs of industry proposals were made by a European Standard Committee to amend the standard EN 10002-1. A European research project with the acronym TENSTAND was started to validate the proposed modifications of the tensile testing standard. The work package 4 of the project was to validate the machine control characteristics. A comparison test program was started with ten partners, 4 test piece geometries and 3 test parameters for 6 materials, partly with upper and lower yield strength and partly with 0.2 % proof strength to compare experimental results according to the proposal to modify the standard EN 10002-1. Initially testing in the strain control mode was introduced as well as switching of the control mode to crosshead control 1 and switching of the testing speed at appropriate points during the test. The comparison test was evaluated statistically and scientifically. The following conclusions were derived from the comparison test and summarised as recommendations to the standard committees. The scatter of the material properties were not significantly reduced by introducing the amended testing procedure. Few of the reasons for the continuously observed scattercan be identified as follows: The material properties are observed to be widely dependent on the testing speed. As a consequence the range for the allowed testing speed must be reduced. The closed loop control was not optimised sufficiently in some tests, the use of complicated testing machine software led to misinterpretation of software commands, individual testing equipment and implementation of the tensile testing procedure led also to scatter of the material properties which lay in a range of few percent. This is blurred by the inhomogeneity of the material.
Microstructural and Mechanical Performance Assessment of Diffusion Bonded Bimetallic Model Discs
(2003)
The stability of microstructure and the microhardness of a NiCoCrAlY alloy was studied after thermal treatment at high temperatures and subsequent quenching into ice water. The alloy revealed mainly two ordered phases, a gamma' phase with L12 lattice structure and a beta phase with B2 structure. The gamma' phase is shown to become unstable in the temperature range between 1073 K and 1373 K where it undergoes an order-disorder phase transformation. The low transformation temperature compared to pure Ni3Al is ascribed to deviations from the Ni3Al stoichiometry and to the additional alloying elements Co and Cr. The gamma'-gamma order-disorder transformation is shown to be attended by a decrease in microhardness of about 30 %.
Specimens of single crystal superalloy SC16 were creep deformed at 1223 K along [0 0 1] up to ±0.5% creep strain using stresses of -150 MPa and +150 MPa, respectively. Line widths and peak positions of superlattice reflections were measured by means of X-ray diffraction parallel and perpendicular to the load axis in the temperature range between 293 K and 1173 K. The line widths were found to decrease with the increase of temperature for both directions on the two specimens after tensile and compressive creep deformation. After both kinds of creep deformation the crystal lattice showed tetragonal distortion which decreased with increasing temperature. The tetragonality after tensile creep deformation was larger than unity while it was smaller than unity after compressive creep deformation. The peak positions and widths restored after cooling back to room temperature. The experimental results can qualitatively be explained by the creation of dislocations during deformation and their anisotropic arrangement at the γ/γ' interfaces.
High-resolution diffraction using synchrotron x-ray radiation was applied to study γ´ precipitates with an L12 superlattice crystal structure in the single crystal superalloy SC16 after creep deformation at 1223 K with a creep strain of ±0.5% for tensile and compressive loads, respectively. The measurements of full width at half maximum (FWHM) of 001 and 100 γ´ superlattice reflections were performed at various temperatures from ambient temperature to 1173 K in vacuum. The experimental results revealed that the FWHM of both reflections decrease with increasing temperature. It is well-known that changes in particle size and lattice distortion in materials could lead to a variation of FWHM. The observed behaviour is discussed in the light of both the above-mentioned aspects. The decrease in the peak width is mainly attributed to the temperature dependence of the internal strain state.
A major international inter-comparison exercise on strain-controlled thermo-mechanical fatigue (TMF) has been undertaken to validate a new European Code of Practice for TMF Testing and to provide underpinning information for an ISO Standard. This paper focuses on (a) distribution of samples of Nimonic 90, (b) the establishment of a protocol for testing and reporting results, and (c) the analysis of the results. Participants in the inter-comparison exercise comprised eight inner-circle partners who primarily used test pieces which were all manufactured at the same workshop, albeit of three different test piece geometries, and ten outer-circle participants who manufactured their own test pieces, of their own in-house geometry. Each participant undertook three repeat in-phase (IP) tests and three repeat out-of-phase (OP) tests. The tests were conducted at temperatures cycling between 400 °C and 850 °C, with a strain range selected to give a failure life of approximately 1000 cycles, resulting in a stress range of up to ~1000 MPa. The testing conditions were chosen following a preliminary evaluation of critical testing parameters. Results from solid circular and solid flat test piece geometries, together with hollow tubular test pieces have been compared. The influence of temperature measurement using different types of temperature sensors has also been investigated. In-house repeatability has been assessed, together with inter-laboratory reproducibility. The results have been correlated with modulus and thermal expansion data for individual tests. Initially, the largest contribution to scatter in the results was attributed to human errors in reporting the results, compounded by computer assisted cut-and-paste errors. Once these obvious discrepancies had been corrected, it was possible to use the data sets to point to some recommendations regarding testing procedures that can be incorporated into the Code of Testing Practice [Hähner P et al. Code of practice for thermo-mechanical fatigue testing TMF-Standard-Work Package 6 Report, September 2005] and provide technical underpinning for the ISO Standard. The results and the procedures used for analysis are presented.
Thermo-mechanical fatigue (TMF) testing plays an increasingly important role in the design, the reliability assessment and the lifecycle management of safety critical components used, for instance, for power generation, in the process industry and in aeronautical and automotive applications, with a view to increasing the fuel efficiency, safety and service intervals, while reducing production (and material) costs. In a European Commission funded research project (acronym: TMF-Standard) of the 5th Framework Programme, 20 European laboratories have undertaken a joint research effort to establish a validated code-of-practice (CoP) for strain-controlled TMF testing. Starting from a survey of the testing protocols and procedures previously used by the partners, a comprehensive pre-normative research activity into various issues has been completed, addressing the dynamic temperature control, the effects of deviations in nominal temperatures and phase angles, the influences of temperature gradients, as well as the practicalities of test interruption and restart procedures. Meaningful allowable tolerances for the various test parameters were identified and practical recommendations as to the test techniques were formulated. From this a preliminary CoP was compiled and used to guide an extensive round robin exercise among the project partners. From the statistical analysis of that exercise, a validated CoP was derived dealing with strain-controlled constant amplitude TMF of nominally homogeneous metallic materials subjected to spatially uniform temperature fields and uniaxial mechanical loading. It is intended to give advice and guidance on the appropriate test setup, testing procedures and the analysis of results, in particular for newcomers in the field of strain-controlled TMF. This paper highlights some of the results of the TMF-Standard project. Moreover, commonalities and differences of the present CoP with respect to the standard documents for strain-controlled TMF, which have been developed at ISO and ASTM levels, are presented in this paper.
Time dependence of y/y' Lattice Mismatch in Creep-deformed Single Crystal Superalloy SC16 at 1173 K
(2007)
Für viskoplastische Stoffgesetze wird das prinzipielle Verfahren der Identifikation von Materialmodell-Parametern für das Spannungs-Verformungs- und Versagens-Verhalten metallischer Werkstoffe am Beispiel von Hochtemperatur-Ermüdung aufgezeigt. Dies betrifft zum Einen die Verwendung geeigneter und auch möglichst weniger Experimente zur Hervorbringung der zu beschreibenden Phänomene des Werkstoffverhaltens und deren gezielte Auswertung sowie zum Anderen die physikalisch kontrollierte Führung einer numerischen Optimierung zur Ermittlung vertrauenswürdiger Materialparameterwerte. Diese Vorgehensweise wurde erfolgreich auf Warmarbeitsstähle sowie poly- und einkristalline Superlegierungen angewendet.
SC16 at 950 °C under LCF loading on smooth cylindrical specimen: influence of secondary orientation
(2008)
The uniaxial, torsional and axial-torsional thermomechanical fatigue (TMF) behavior of the near-γ TiAl-alloy TNB-V5 was investigated. TMF tests were performed at 400-800 °C with mechanical strain amplitudes ranging from 0.15% to 0.7%. The tests were conducted thermomechanically in-phase (IP) and out-of-phase (OP).
For the same lifetimes, uniaxial IP tests required the highest strain amplitudes, while OP test conditions were most damaging and needed the lowest strain amplitudes. The Mises equivalent mechanical strain amplitudes of pure torsional tests were found in between uniaxial in-phase and out-of-phase tests for the same lifetimes. The non-proportional multiaxial out-of-phase test showed a lower lifetime at the same equivalent mechanical strain amplitude compared to the other types of tests.
The microstructure has been characterized applying electron microscopy and microstructural parameters such as fraction of twinned grains, grain size, lamellar distance and dislocation density have been quantified.
Creep damage of single-crystal nickel base superalloys: mechanisms and effect on low cycle fatigue
(2010)
The main mechanisms of creep damage of single-crystal nickel-base superalloys are the loss of the interface coherency, coarsening of the γ / γ'-microstructure, precipitation of topologically closed packed phases and growth of porosity. This degradation deteriorates the mechanical properties such as yield stress, creep lifetime and especially low-cycle fatigue life, which can be reduced nearly by a factor of 10. The degradation kinetics during creep was characterised quantitatively on the superalloy CMSX-4. A new non-destructive testing technique was applied to cover a wide test parameter range with few specimens in a relatively short time: repeated load annealing of wedge shaped specimens.
Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling
(2012)
The continuing increase of steam parameters of fossil fuelled high efficiency power plants and new combustion concepts for the capture and storage of carbon dioxide lead to harsher service conditions for the components and structural materials of such facilities. The present work introduces a test concept that allows testing of candidate materials under simultaneous mechanical and corrosive loading. The material's reaction can be directly investigated under simulated temperature, load and corrosion conditions of modern installations. First results obtained for different heat resistant steels suggest a strong influence of the environmental medium on the fatigue and creep behaviour. Such findings complement the data that is available from the classical qualification process of the materials and may support the material selection for new power plant installations.
Experimental characterization and mechanical modeling of creep induced rafting in superalloys
(2012)
A constitutive model has been developed for the high temperature mechanical behavior of single crystal superalloys, including rafting and its consequences. The flow stress depends on the γ channel width via the Orowan stress. An evolution equation for channel widening during high temperature straining has been derived and calibrated with measurements. Therein, rafting is assumed to be driven by the relaxation of internal stresses. The model is able to represent the mechanical softening at high stresses consecutive to rafting. The model has been applied to simulate rafting during uniaxial creep in several crystal orientations, in notched specimens as well as in cyclically loaded specimens.
A new experimental technique (repeated load annealing of flat wedge shaped specimens) was proposed for characterization of microstructural degradation under creep conditions. This technique was applied to investigate the microstructural degradation of the nickel-base superalloy CMSX-4 in a wide range of temperatures and stress levels. The results obtained allowed to describe analytically the kinetics of rafting, which is important to predict the reduction of fatigue lifetime and yield stress.