Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (24)
- Zeitschriftenartikel (16)
- Beitrag zu einem Sammelband (16)
- Beitrag zu einem Tagungsband (12)
- Forschungsbericht (4)
- Sonstiges (2)
- Posterpräsentation (2)
Schlagworte
- Superalloys (6)
- Creep (5)
- Rafting (5)
- Extensometer (4)
- Nickel-base superalloys (4)
- Single crystal (4)
- TMF (4)
- CMSX-4 (3)
- Creep-deformation (3)
- Lattice distortion (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (24)
Creep damage of single-crystal nickel base superalloys: mechanisms and effect on low cycle fatigue
(2010)
The main mechanisms of creep damage of single-crystal nickel-base superalloys are the loss of the interface coherency, coarsening of the γ / γ'-microstructure, precipitation of topologically closed packed phases and growth of porosity. This degradation deteriorates the mechanical properties such as yield stress, creep lifetime and especially low-cycle fatigue life, which can be reduced nearly by a factor of 10. The degradation kinetics during creep was characterised quantitatively on the superalloy CMSX-4. A new non-destructive testing technique was applied to cover a wide test parameter range with few specimens in a relatively short time: repeated load annealing of wedge shaped specimens.
Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling
(2012)
The continuing increase of steam parameters of fossil fuelled high efficiency power plants and new combustion concepts for the capture and storage of carbon dioxide lead to harsher service conditions for the components and structural materials of such facilities. The present work introduces a test concept that allows testing of candidate materials under simultaneous mechanical and corrosive loading. The material's reaction can be directly investigated under simulated temperature, load and corrosion conditions of modern installations. First results obtained for different heat resistant steels suggest a strong influence of the environmental medium on the fatigue and creep behaviour. Such findings complement the data that is available from the classical qualification process of the materials and may support the material selection for new power plant installations.
Experimental characterization and mechanical modeling of creep induced rafting in superalloys
(2012)
A constitutive model has been developed for the high temperature mechanical behavior of single crystal superalloys, including rafting and its consequences. The flow stress depends on the γ channel width via the Orowan stress. An evolution equation for channel widening during high temperature straining has been derived and calibrated with measurements. Therein, rafting is assumed to be driven by the relaxation of internal stresses. The model is able to represent the mechanical softening at high stresses consecutive to rafting. The model has been applied to simulate rafting during uniaxial creep in several crystal orientations, in notched specimens as well as in cyclically loaded specimens.
A new experimental technique (repeated load annealing of flat wedge shaped specimens) was proposed for characterization of microstructural degradation under creep conditions. This technique was applied to investigate the microstructural degradation of the nickel-base superalloy CMSX-4 in a wide range of temperatures and stress levels. The results obtained allowed to describe analytically the kinetics of rafting, which is important to predict the reduction of fatigue lifetime and yield stress.