Purpose is the formulation, numerical implementation, identification and application of a material model for ductile damage and failure during cyclic and non-proportional loading.
The authors combined a hyperelasticity-based elasto-plastic model for non-linear isotropic as well as kinematic hardening with a modified Gurson model. Evolution strategy helped identify the model parameters for the high-strength steel 10MnMoNi5-5. The simulation of ductile failure in fracture mechanics specimens verified the model with respect to cyclic loading at two temperatures. The simulation of additional fracture mechanics applications validated the model as to the development of residual stresses at the crack tip under cyclic loads.
Welding is one of the most common methods in industrial practice for joining components. Its main advantages are high speed in manufacturing combined with low costs and, usually, a high degree of flexibility, integrity and reliability. Nevertheless, welding is a highly complex metallurgical process and, therefore, weldments are susceptible to material discontinuities, flaws and residual stresses which may lead to structural failure and life time reduction. As a consequence weldments are an important field of fracture mechanics methods although its application is more complex than for homogeneous or non-welded structures. The aim of the paper is to provide an overview on the current state of fracture mechanics application to weldments. It starts by discussing the specific features which any fracture mechanics analysis of weldments has to take into account. Then, the experimental determination of fracture toughness, fatigue crack propagation and tensile properties of weldments is addressed. Finally, the analytical determination of the crack driving force in components and structural integrity assessment approaches for weldments are presented.
The roll-on-roll-off passenger ferry MV ESTONIA sank during the night of 28 September 1994 in the Baltic Sea. In October 2000, divers recovered two palm-sized test pieces from the front bulkhead of the wreck. The investigators analysed these specimens to determine whether there were any indications of deliberate blasting. Since the wreck had been submerged for almost six years, it was clear that chemical traces would not be present on the surfaces of the test pieces. Therefore, the investigators performed comparative tests on shipbuilding steel to find a microstructural criterion that exclusively characterises a blast. The shipyard Jos. L. Meyer, Germany, had built the ESTONIA and supplied shipbuilding steel plates similar to that used for building the vessel in 1979/1980. The comparative tests comprised mechanical tests, shot peening tests and blasting tests using different explosives. Testing demonstrated that blasting always formed twinned ferrite grains in the microstructure over the whole cross-section of each of the 8 mm thick comparative plates. Although one of the original test pieces of the ESTONIA showed deformation twins, this was only confined up to 0.4 mm underneath the surfaces and not spread over the whole cross-section. Comparative shot peening tests produced the very same pattern of subsurface deformation twins. Therefore, the twins detected in the microsection of the test pieces of the ESTONIA wreck traced back to the shot peening process performed by the shipyard in 1979/1980 and not to a deliberate blast.
Investigations on the breakdown of a heat recovery steam generator during the initial operation run
(2014)
Several years ago, in 2003, an industrial heat recovery steam generator in charge of generating process steam in a petrochemical refinery was installed and prepared for initial operation. The steam generator enclosed an evaporator section and a superheater section consisting mainly of bundles of tubes with the longest up to several metres in length. During initial operation test runs severe leakages in the evaporator and superheater modules became noticeable. The test runs were stopped and after disassembly, through-wall cracks in several tube bends were found. BAM was commissioned to carry out the investigations in order to find out the reasons for the failure of the tubes. During on-site inspection a number of relevant damaged components and parts were selected and taken away to the laboratories for detailed inspection. Planned analyses were to comprise metallographic as well as fractographic investigations, mechanical fatigue testing and experimental as well as finite element vibration analyses on specimens and components. Soon, the fracture mechanism was found to be mechanical fatigue due to the fact that the examined fracture surfaces showed the very characteristic beachmarks and colouring patterns. To identify the particular loading and time at which crack initiation and crack propagation took place, experimental and numerical vibration analyses of specific tubes as well as mechanical fatigue tests on tube bends were carried out. Thus it was possible to identify the eigenfrequencies of individual tubes, to estimate the dynamic response as well as the nominal stresses and, hence, experimentally characterise the in-service fatigue strength of the components. Mechanical and thermal comparative tests on tube bends were performed simulating the conditions during the initial test run in order to get crack surfaces comparable to that of the originally damaged components. Thereby it became obvious that the fatigue cracks were initiated by vibrations the tube bundles were exposed to during rail transport from the manufacturers site to the place of installation. Based on these results, the damaged components could be repaired or exchanged without modification of the construction, but the rules relating packaging and securing for shipping had to be revised.
On July 9, 2008 a high speed train derailed in Cologne main Station, Germany at a low speed because an axle was broken. Fortunately, the derailment happened at a low speed so that nobody was injured. The reason for the broken axle was investigated and it turned out that most likely large inclusions located shortly undemeath the surface in a T-transition were the origin of the final crack. Basing on that result, a systematic investigation on existing safety assessments of railway axles was performed. This results in an analysis of the production process of axles and in a critical review of existing of existing assessments. Improvements and future developments are outlined.
The safety assessment of railway axles is based on a two-stage approach: fatigue strength design and regular inspections which, in terms of a general safety philosophy refer to safe-life and damage tolerance concepts. Starting with a recent failure case, a broken axle of a German high speed train, a discussion is presented on issues of both safety levels. These include ideas for finite life design, the treatment of in-service effects on the fatigue strength due to flying ballast damage and corrosion pits, the effect of corrosion on fatigue crack initiation and propagation, potential effects of non-metallic inclusions in steels, the way to detect them by quality control measures and reliability aspects of non-destructive testing with respect to the detection of fatigue cracks. Proposals are made how the safety level could be further improved.
The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection.