The friction and wear behaviour of thin hard coatings, such as TiN and the promising class of C-based coatings (a-C, a-C:H, and diamond for example), are compared under oscillating and reciprocating sliding conditions. The typical effects of test parameters, such as stroke, frequency, normal force, relative humidity and test duration, are described as a basis for the proper selection of test conditions or, conversely, for the selection of suitable coatings for particular practical applications.
Friction and wear data from over 1000 vibrating tests using thin hard coatings against 100Cr6 and against Al2O3 have been compiled in a database. This allows easy manipulation and comparison of test results. Using selection criteria and filter procedures (e. g., lifetime of coatings, friction limits, and critical wear rate), suitable coating systems for different test conditions can be chosen from the database. The effects of test parameters on friction and wear behaviour and changes have anyway to be known for meaningful tribotesting, as well as for the selection of coatings.
The friction and wear behaviour of a new developed, pressureless sintered TiB2 ceramic was studied in comparison to SiC against SiC and Al2O3 balls under unlubricated conditions at room temperature. Special attention was paid to the influence of relative humidity on friction and wear results. For both ceramics the coefficient of friction against both ball materials decreases with increasing humidity and is higher in tests against alumina than against SiC. The wear rate is affected significantly by humidity and decreases by one order of magnitude for Al2O3/SiC system and by 2 orders of magnitude for SiC/SiC system. For TiB2 wear rates are nearly not affected by humidity against both ball materials and are much smaller than for SiC.