The friction and wear behaviour of a new developed, pressureless sintered TiB2 ceramic was studied in comparison to SiC against SiC and Al2O3 balls under unlubricated conditions at room temperature. Special attention was paid to the influence of relative humidity on friction and wear results. For both ceramics the coefficient of friction against both ball materials decreases with increasing humidity and is higher in tests against alumina than against SiC. The wear rate is affected significantly by humidity and decreases by one order of magnitude for Al2O3/SiC system and by 2 orders of magnitude for SiC/SiC system. For TiB2 wear rates are nearly not affected by humidity against both ball materials and are much smaller than for SiC.
Diamantähnliche Kohlenstoffschichten (DLC) zeichnen sich durch ein sehr günstiges Reibungs- und Verschleißverhalten aus. Auf vielen Werkzeugen und hochbelasteten Bauteilen ist DLC daher bereits erfolgreich im Einsatz. In naher Zukunft wird die Bedeutung dieser Schichten als Oberflächenschutz in tribologischen Systemen weiter ansteigen.
Wie viele Applikationsbeispiele zeigen, ist die Leistungsfähigkeit von DLC als Schicht zur Verringerung von Reibung und Verschleiß zwar groß, weist aber auch Grenzen auf. Vor allem bei höheren Temperaturen (> 300 °C) treten Strukturveränderungen oder sogar Oxidationsvorgänge auf, die auch die tribologischen Eigenschaften der Schichten verschlechtern können.
Reibungs- und Verschleißuntersuchungen (Schwingungsverschleiß) von DLC-Schichten wurden im Temperaturbereich von 25 °C bis 250 °C durchgeführt und zeigen ein schnelleres Durchreiben der Schicht bei höheren Temperaturen. Die Lebensdauer der Schichten wird mit zunehmender Prüftemperatur reduziert. Einsatzgrenzen für DLC-Schichten können abgeleitet werden.