Ceramic particulate composites in the system SiC-TiC-TiB2 sliding against SiC and Al2O3 under water
(1999)
The tribological behaviour of SiC, SiC-TiC and SiC-TiC-TiB2 was determined in oscillating sliding against SiC and -Al2O3 in water at room temperature. The tribo-systems with the composite materials containing TiC and TiB2 differ significantly from the systems with the single phase SiC: The wear is reduced and the friction is increased. The wear reduction up to a factor of 10 is mainly due to the formation of an oxide film containing titanium oxides which is soft, stable in water and well adhering to the bulk material. This oxide film is transferred to the alumina ball but not to the silicon carbide ball.
The friction and wear behaviour of a new developed, pressureless sintered TiB2 ceramic was studied in comparison to SiC against SiC and Al2O3 balls under unlubricated conditions at room temperature. Special attention was paid to the influence of relative humidity on friction and wear results. For both ceramics the coefficient of friction against both ball materials decreases with increasing humidity and is higher in tests against alumina than against SiC. The wear rate is affected significantly by humidity and decreases by one order of magnitude for Al2O3/SiC system and by 2 orders of magnitude for SiC/SiC system. For TiB2 wear rates are nearly not affected by humidity against both ball materials and are much smaller than for SiC.
Diamantähnliche Kohlenstoffschichten (DLC) zeichnen sich durch ein sehr günstiges Reibungs- und Verschleißverhalten aus. Auf vielen Werkzeugen und hochbelasteten Bauteilen ist DLC daher bereits erfolgreich im Einsatz. In naher Zukunft wird die Bedeutung dieser Schichten als Oberflächenschutz in tribologischen Systemen weiter ansteigen.
Wie viele Applikationsbeispiele zeigen, ist die Leistungsfähigkeit von DLC als Schicht zur Verringerung von Reibung und Verschleiß zwar groß, weist aber auch Grenzen auf. Vor allem bei höheren Temperaturen (> 300 °C) treten Strukturveränderungen oder sogar Oxidationsvorgänge auf, die auch die tribologischen Eigenschaften der Schichten verschlechtern können.
Reibungs- und Verschleißuntersuchungen (Schwingungsverschleiß) von DLC-Schichten wurden im Temperaturbereich von 25 °C bis 250 °C durchgeführt und zeigen ein schnelleres Durchreiben der Schicht bei höheren Temperaturen. Die Lebensdauer der Schichten wird mit zunehmender Prüftemperatur reduziert. Einsatzgrenzen für DLC-Schichten können abgeleitet werden.
Tribological characterisation of siliconcarbonitride ceramics derived from preceramic polymers
(2006)
Amorphous SiCN ceramics were prepared in a laboratory scale as disk shaped specimens with 10 mm diameter and 0.3 mm thickness. The friction and wear behaviour was characterised in gross slip fretting tests under unlubricated conditions at room temperature against steel (100Cr6) and ceramic (Al2O3). Tests with a ball-on-disk contact were performed in laboratory air with different content of water vapour. The results show clearly that the relative humidity has a significant effect on friction and wear behaviour. All tests in dry air lead to higher friction and higher wear rate than in normal air. Improved friction and wear behaviour was observed with increasing pyrolysis temperature up to 1100 °C of the SiCN specimens. This is attributed to increasingly better mechanical properties and higher stiffness of the amorphous network due to the evaporation of gaseous organic species and the formation of free graphite like carbon.
Contact formation and development are the basis of friction and wear modelling and understanding. Unanimously topography formation and development in friction contacts are regarded of highest importance for understanding and modelling friction processes. The frequently found running in behaviour of sliding contacts is—aside from the build up of reaction and transfer layers-at least partly caused by the topography development due to friction processes until a stable equilibrium state is reached.
Experimental results of friction and topography measurements are presented which demonstrate the mutual modification of friction and contact topography.
A special experimental set up with an AFM allowed to correlate the measured friction forces with the contact position and the topography at this point. In this way, friction force transitions and changes can be assigned to topography changes due to abrasion, adhesion and wear particle agglomeration.
Contact surfaces with artificial regular structures have been prepared to avoid problems with topography and friction correlation due to the statistical nature of roughness on technical contact surfaces. The friction effects of roughness were simulated by etched ditches of defined width, depth and distance on silicon or metal surfaces. This allowed to explain the mutual influences of topography and friction. The effect of a single asperity and of the 'roughness structures' could be demonstrated.
Topography measurements with an AFM correlated with the friction force could help to understand friction changes without changing any parameter.