Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (52) (entfernen)
Sprache
- Englisch (50)
- Deutsch (1)
- Mehrsprachig (1)
Schlagworte
- Mechanochemistry (5)
- Nanoparticles (5)
- XRD (5)
- Catalysis (3)
- Alkaline earth metal coordination polymers (2)
- Aluminium (2)
- Brown-rot fungi (2)
- Coordination polymers (2)
- Doped systems (2)
- Fluorides (2)
Organisationseinheit der BAM
- 6 Materialchemie (10)
- 6.3 Strukturanalytik (9)
- 4 Material und Umwelt (4)
- 4.1 Biologische Materialschädigung und Referenzorganismen (4)
- 8 Zerstörungsfreie Prüfung (2)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.9 Chemische und optische Sensorik (1)
- 4.3 Schadstofftransfer und Umwelttechnologien (1)
- 5 Werkstofftechnik (1)
Wood treated with nano metal fluorides is found to resist fungal decay. Sol−gel synthesis was used to synthesize MgF2 and CaF2 nanoparticles. Electron microscopy images confirmed the localization of MgF2 and CaF2 nanoparticles in wood. Efficacy of nano metal fluoride-treated wood was tested against brown-rot fungi Coniophora puteana and Rhodonia placenta. Untreated wood specimens had higher
mass losses (∼30%) compared to treated specimens, which had average mass loss of 2% against C. puteana and 14% against R. placenta, respectively. Nano metal fluorides provide a viable alternative to current wood preservatives.
The fluorolytic sol–gel synthesis is applied with the intention to obtain two different types of core–shell nanoparticles, namely, SrF2–CaF2 and CaF2–SrF2. In two separate fluorination steps for core and shell formation, the corresponding metal lactates are reacted with anhydrous HF in ethylene glycol. Scanning transmission electron microscopy (STEM) and dynamic light scattering (DLS) confirm the formation of particles with mean dimensions between 6.4 and 11.5 nm. The overall chemical composition of the particles during the different reaction steps is monitored by quantitative Al Kα excitation X-ray photoelectron spectroscopy (XPS). Here, the formation of stoichiometric metal fluorides (MF2) is confirmed, both for the core and the final core–shell particles. Furthermore, an in-depth analysis by synchrotron radiation XPS (SR-XPS) with tunable excitation energy is performed to confirm the core–Shell character of the nanoparticles. Additionally, Ca2p/Sr3d XPS intensity ratio in-Depth profiles are simulated using the software Simulation of Electron Spectra for Surface Analysis (SESSA). In principle, core–shell like particle morphologies are formed but without a sharp interface between calcium and strontium containing phases.
Surprisingly, the in-depth chemical distribution of the two types of nanoparticles is equal within the error of the experiment. Both comprise a SrF2-rich core domain and CaF2-rich shell domain with an intermixing zone between them. Consequently, the internal morphology of the final nanoparticles seems to be independent from the synthesis chronology.