Filtern
Dokumenttyp
Sprache
- Englisch (3)
Referierte Publikation
- ja (3)
Schlagworte
- Catalysis (3) (entfernen)
Time-optimized 15N quantitative NMR (qNMR) is described for the precise determination of Lewis and Brønsted site concentrations per gram catalyst, enabling a measurement time reduction of more than a factor of 10. The proof-of-principle is demonstrated for amorphous aluminum hydroxide fluorides with their tunable Lewis to Brønsted functionalities and relevance to highly active and selective heterogeneous catalysis using pyridine as a widely accepted probe molecule for Lewis and Brønsted sites. Two different Lewis centers were found, and reliable site concentrations down to the micromole per gram region can be determined. Furthermore, 1H{15N} REDOR NMR for the acid proton at the Brønsted site yields a distance of the 15N atom of bonded pyridine to this acid proton of (0.112 ± 0.002) nm, such that fast motion/diffusion of the Brønsted site-bonded pyridine at the surface can be excluded.
Solgel prepared ternary FeF3–MgF2 materials have become promising heterogeneous catalysts due to their porosity and surface Lewis/Brønsted acidity (bi-acidity). Despite the good catalytic performance, nanoscopic characterisations of this type of material are still missing and the key factors controlling the surface properties have not yet been identified, impeding both a better understanding and further development of ternary fluoride catalysts. In this study, we characterised the interaction between the bi-acidic component (FeF3) and the matrix (MgF2) on the nano-scale. For the first time, the formation pathway of FeF3–MgF2 was profiled and the template effect of MgF2 during the synthesis process was discovered. Based on these new insights two novel materials, FeF3–CaF2 and FeF3–SrF2, were established, revealing that with decreasing the atomic numbers (from Sr to Mg), the ternary fluorides exhibited increasing surface acidity and surface area but decreasing pore size. These systematic changes gave rise to a panel of catalysts with tuneable surface and bulk properties either by changing the matrix alkaline earth metal fluoride or by adjusting their ratios to Fe or both. The template effect of the alkaline earth metal fluoride matrix was identified as the most probable key factor determining the surface properties and further influencing the catalytic performance in ternary fluoride based catalysts, and paves the way to targeted design of next-generation catalysts with tunable properties.
15N NMR of pyridine has been used to study Lewis and Brønsted sites at the acid surface of magnesium hydroxide fluoride at two different pyridine loadings with ratios of excess pyridine compared to pyridine molecules bound to Lewis and Brønsted sites of about 1:1 (highly loaded) and 0.15:1 (low loaded), respectively. The Lewis and Brønsted sites can be distinguished by the 15N chemical shift of pyridine at about –100 ppm (LPy) and –175 ppm (BPy). In both samples a very broad 15N resonance is found around –88 ppm assigned to weakly adsorbed (excess) pyridine molecules via hydrogen bridges (HPy). Additionally, another signal at about –49 ppm is observed in the highly loaded sample only representing physisorbed pyridine (PPy). A slow chemical exchange process of strongly bound LPy and BPy molecules with excess HPy and PPy molecules can be monitored using 15N exchange NMR. It takes place on a time scale of about 50–100 ms at room temperature. All pyridine molecules have the same 15N T1 and its value increases from 800 ms (highly loaded sample) to 5.3 s (low loading) hinting on changed pyridine mobility depending on the loading level.