Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (48)
Sprache
- Englisch (46)
- Deutsch (1)
- Mehrsprachig (1)
Referierte Publikation
- ja (48) (entfernen)
Schlagworte
- Mechanochemistry (5)
- XRD (5)
- Nanoparticles (4)
- Catalysis (3)
- Alkaline earth metal coordination polymers (2)
- Coordination polymers (2)
- Doped systems (2)
- Heterogeneous catalysis (2)
- Lewis acid (2)
- Metal fluoride (2)
Organisationseinheit der BAM
Static TOF-SIMS results strongly underpin earlier conclusions from ESCA, XANES, and tracer studies that the accumulation of fluorine and chlorine at the surface of chromia by a heterogeneous reaction with a chlorofluorocarbon compound results in the formation of mixed chromium oxide halide species and not in the nucleation of CrCl3 and/or CrF3 phases.
The dismutation of CCl2F2 was used to probe the effect of halogenation of chromia by Cl/F exchange reactions to find out the difference between the halogenated inactive and active catalysts. The heterogeneous reactions were performed in a continuous flow Ni reactor and also under simulated reaction conditions in a reactor where after the reaction X-ray photoelectron spectroscopy (XPS) and X-ray excited Auger electron spectroscopy (XAES) analyses are possible without air exposure of the catalyst, i.e., under so-called "in situ" conditions. The Cr(III) 2p XP spectra, which revealed multiplet splitting features and satellite emission, were used for chemical analysis by using a simple evaluation procedure which neglects this inherent complexity. Chemical analysis was also applied by using chemical state plots for Cr 3s in order to cross-check Cr 2p related results. Both ex and in situ XPS show that as soon as Cr2O3 is exposed to CCl2F2 at 390°C fluorination as well as chlorination takes place at the catalyst surface. When the XPS surface composition reaches approximately 4 at. % fluorination and 6 at. % chlorination, maximum catalytic activity was obtained. Application of longer reaction times did not change significantly the obtained surface composition of the activated chromia. The fluorination and chlorination of chromia was further investigated by various HF and HCl treatments. The activated chromia samples and the Cr2O3, Cr(OH)3, CrF2OH, CrF3·H2O, α-CrF3, β-CrF3, and CrCl3 reference samples with well-known chemical structures were also characterized by X-ray absorption near edge structure (XANES), time-of-flight secondary ion mass spectroscopy (TOF-SIMS), pyridine-FTIR, wet chemical (F and Cl) analysis, X-ray powder diffraction (XRD), and surface area (BET) analysis. The results suggest that the formation of chromium oxide chloride fluoride species, e.g., chromium oxide halides, at the surface is sufficient to provide catalytic activity. The presence of any CrF3 and/or CrCl3 phases on the activated chromia samples was not found.
Lanthanides doped coordination polymers (CPs) with different binding motifs were synthesized to investigate the influence of the different fluorine positions in the structure on the decay time τ of the excited states. Fluorine can be integrated into the network mechanochemically via a fluorinated organic linker, here barium tetrafluoroterephthalate Ba(p-BDC-F4)2 or directly via a metal-fluorine bond (barium terephthalate fluoride BaF(p-BDC)0.5). The CP with a metal-fluorine bond shows the highest lifetime of the excited states of lanthanides (Eu3+, Tb3+ or Eu3+& Tb3+). The excitation of the lanthanides can be performed directly via the excitation wavelength typical for lanthanides and via the excitation wavelength of the linker. This enabled the simultaneous excitation of Eu3+ and Tb3+ in one CP. In the emission spectra (λem = 393 nm) of the mixed doped CPs (Eu3+ and Tb3+) the bands of both lanthanides can be observed. The integration into the crystal lattice and the homogeneous distribution of the lanthanides in the CPs is shown by X-ray diffraction, TEM, STEM-EDS measurements and the long decay times.
As the most electronegative element, fluorine has a strong influence on material properties such as absorption behaviour or chemical and thermal stability. Fluorine can be easily integrated into coordination polymers (CPs) via a fluorinated acetate, here trifluoroacetate in Ba(CF3COO)2, or directly via a metal fluorine bond (BaF(CH3COO)). In the present study both possibilities of fluorine integration were tested and their effect on structure and properties of barium coordination polymers was investigated in comparison with the non-fluorinated barium acetate (Ba(CH3COO)2). In addition to the study of their thermal behaviour and their decomposition temperature, the CPs structures were tested for their application as possible anode materials in lithium ion batteries and for their sorption of water and ammonia. The properties of the CPs can be traced back to the individual structural motifs and could thus trigger new design ideas for CPs in LIBs and/or catalysis.
New coordination polymers with 2D network structures with fluorine directly coordinated to the metal ion were prepared both via mechanochemical synthesis and fluorolytic sol–gel synthesis. Depending on the synthesis route, the samples show different particle sizes, according to SEM imaging. The crystal structures of barium acetate fluoride, strontium acetate fluoride, and lead acetate fluoride (BaFIJCH3COO), SrFIJCH3COO) and PbFIJCH3COO)) were solved from X-ray powder diffraction data. The structure solution is backed by the results from 19F MAS NMR, FT IR data, and thermal analysis. The calculated chemical shifts of the 19F MAS NMR spectra coincide well with the measured ones. It turns out that the grinding conditions have a remarkable influence on the mechanochemical synthesis and its products. Our systematic study also indicates a strong influence of the atomic radii of Ca, Sr, Ba, and Pb on the success of the syntheses.
Rare-earth based luminescent materials are key functional components for the rational design of light-conversion smart devices. Stable Eu3+-doped strontium fluoride (SrF2) nanoparticles were prepared at room temperature in ethylene glycol. Their luminescence depends on the Eu content and changes after heat treatment. The crystallinity of heat-treated material increases in comparison with as-synthesized samples. Particles were investigated in solution using X-ray diffraction, small-angle X-ray scattering, and X-ray spectroscopy. After heat treatment, the size of the disordered nanoparticles increases together with a change of their local structure. Interstitial fluoride ions can be localized near Eu3+ ions. Therefore, non-radiative relaxation from other mechanisms is decreased. Knowledge about the cation distribution is key information for understanding the luminescence properties of any material.
Conventional simultaneous thermal analysis, capillary-coupled TGMS, in situ and ex situ Raman and Mössbauer spectroscopy, as well as chemical analysis have been used for the investigation of the first decomposition step of the mixed valence chloroferrate (dmpipzH2)6[Fe(II)Cl4]2[Fe(III)Cl4]2[Fe(II)Cl5][Fe(III)Cl6]. Under argon at ca. 200°C, an almost complete reduction proceeds in a solid state reaction forming Fe(II). It is accompanied by the release of HCl and, to a minor degree, carbon containing species. A multi-phase product with at least two chloroferrate species, coke, and C,H,N-containing polymers is formed. Binuclear iron complexes, such as (dmpipzH)2[Fe(II)2Cl6], and small amounts of (dmpipzH)[Fe(III)Cl4] have been proposed to be the major and minor component of the product mixture, respectively.
Fluorides are well-known as wood preservatives. One of the limitations of fluoride-based wood preservatives is their high leachability. Alternative to current fluoride salts such as NaF used in wood protection are low water-soluble fluorides. However, impregnation of low water-soluble fluorides into wood poses a challenge. To address this challenge, low water-soluble fluorides like calcium fluoride (CaF2) and magnesium fluoride (MgF2) were synthesized as nanoparticles via the fluorolytic sol−gel synthesis and then impregnated into wood specimens. In this study, the toxicity of nano metal fluorides was assessed by termite mortality, mass loss and visual analysis of treated specimens after eight weeks of exposure to termites, Coptotermes formosanus. Nano metal fluorides with sol concentrations of 0.5 M and higher were found to be effective against termites resulting in 100% termite mortality and significantly inhibited termite feeding. Among the formulations tested, the least damage was found for specimens treated with combinations of CaF2 and MgF2 with an average mass loss less than 1% and visual rating of “1”. These results demonstrate the efficacy of low water-soluble nano metal fluorides to protect Wood from termite attack.
Improved Durability of Wood Treated with Nano Metal Fluorides against Brown-Rot and White-Rot Fungi
(2022)
Low-water soluble metal fluorides such as magnesium fluoride (MgF2) and calcium Fluoride (CaF2) were evaluated for decay protection of wood. Initially, the biocidal efficacy of nano metal fluorides (NMFs) against wood destroying fungi was assessed with an in-vitro agar test. The results from the test showed that agar medium containing MgF2 and CaF2 was more efficient in preventing fungal decay than stand-alone MgF2 or CaF2. These metal fluorides, in their nanoscopic form synthesized using fluorolytic sol-gel synthesis, were introduced into the sapwood of Scots pine and beech wood and then subjected to accelerated ageing by leaching (EN 84). MAS 19F NMR and X-ray micro CT images showed that metal fluorides were present in treated wood, unleached and leached. Decay resistance of Scots pine and beech wood treated with NMFs was tested against Wood destroying fungi Rhodonia placenta and Trametes versicolor in accordance with EN 113. Results revealed that mass losses were reduced to below 3% in wood treated with the combination of MgF2 and CaF2.
It is concluded that NMFs provide full protection to wood even after it has been leached and can be used as wood preservatives in outdoor environments.