Hardness and pitting corrosion resistance are the major quality criteria of cutlery. Both are achieved by the heat treatment (austenitization, quenching and tempering) of the normally used martensitic stainless steels. The established quality control method regarding the pitting corrosion resistance is an alternating immersion test in 1 % NaCl solution at 60 °C according to DIN EN ISO 8442. This standard test shows a high deviation, which limits any optimization of the heat treatment process. New approaches for corrosion testing of martensitic stainless-steels were developed and used in the last years to connect the weak pitting corrosion resistance of martensitic stainless-steels with the phenomenon of chromium depletion. The tempering temperatures used in the industrial heat treatment of cutlery are too low to explain the appearance of chromium depletion. For this reason, a systematic investigation of three heat treatment parameters (austenitization time, cooling speed and tempering temperature) were performed on the martensitic stainless-steels X50CrMoV15 (1.4116) to detect their contribution to chromium depletion. The electrochemical potentiodynamic reactivation (EPR), which is very sensitive to any change of the microstructure, was used to quantify the degree of chromium depletion. The KorroPad indicator-test was applied to correlate low pitting corrosion resistance to the presence of chromium depletion. The results of all investigations allow conclusions about the very small process window, which is necessary to achieve cutlery with high pitting corrosion resistance.
The KorroPad indicator test was invented at the Federal Institute for Materials Research and Testing to detect stainless-steel surfaces susceptible to pitting corrosion. The KorroPad indicator test is thus an interesting alternative for manufacturers, processors, users and researchers to time consuming exposition experiments and complex electrochemical investigations, which are normally used to reveal surface-related processing errors resulting in reduced pitting corrosion resistance. Furthermore, the KorroPad indicator test can be used to visualize alloy- and microstructure-related factors causing susceptibility to pitting corrosion. The detection limit of the KorroPad indicator test was characterized in this work using reference alloys with different chromium content (5 % to 18 %). The alloy-specific detection limit was shifted successfully to higher chromium content by increasing the concentrations of NaCl and K3[Fe(CN)6]. The modified KorroPads can now be used to establish an alloy-specific quality control regarding the pitting corrosion resistance of different stainless steel grades.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion re-sistance due to chromium depletion.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Die Legierungselemente (Chrom und Kohlenstoff) und die Wärmebehandlung bestimmen Korrosionsbeständigkeit und Härte martensitischer nichtrostender Stähle. Verschiedene wissenschaftliche Arbeiten haben bereits gezeigt, dass die Korrosionsbeständigkeit sehr stark vom Anteil an Chromkarbiden im Gefüge bestimmt wird. Der kombinierte Einfluss von Kohlenstoffgehalt und der Abkühlgeschwindigkeit beim Härten wurde mit Fokus auf die Korrosionsbeständigkeit bisher nur unzureichend untersucht. Die Literatur liefert außerdem gegensätzliche Aussagen über den Einfluss der Abkühlgeschwindigkeit, was möglicherweise auf unterschiedliche Kohlenstoffgehalte zurückgeführt werden kann. In dieser Arbeit wird daher systematisch untersucht, ab welcher Abkühlgeschwindigkeit es bei den Werkstoffen X20Cr13 und X46Cr13 zu Karbidbildung und Chromverarmung kommt. Die Variation der Abkühlgeschwindigkeit erfolgte für die industriell relevante Härtetemperatur von 1050 °C mit dem Stirnabschreckversuch. In Abhängigkeit von der Abkühlgeschwindigkeit wurden an den Stirnabschreckproben Gefüge, Härte und Korrosionsbeständigkeit (EPR, kritische Lochkorrosionspotentiale) untersucht und die Ergebnisse mit thermodynamischen Berechnungen (ThermoCalc) korreliert. Aus den Ergebnissen wird abgeleitet, unter welchen Bedingungen die Abkühlgeschwindigkeit die Korrosionsbeständigkeit beeinflusst.
Der nichtrostende, aushärtbare Stahl 1.4542 (X5CrNiCuNb16-4) wird aufgrund der guten mechanischen Eigenschaften und der hohen Korrosionsbeständigkeit in einer Vielzahl von technischen Anwendungen eingesetzt. Das Verhältnis zwischen den mechanischen Eigenschaften und der Korrosionsbeständigkeit wird durch eine gezielte Wärmebehandlung eingestellt. Härte und Festigkeit werden durch die Bildung von fein verteilten Kupferausscheidungen bei der Warmauslagerung erreicht. Werden dabei auch Chromkarbide gebildet, reduziert sich gleichzeitig die Korrosionsbeständigkeit. Um den Einfluss der Warmauslagerung auf die Eigenschaften zu charakterisieren, wurden verschiedene Alterungszustände erzeugt und vergleichend untersucht. Dabei wurde außerdem der Einfluss einer starken Kaltumformung auf das Alterungsverhalten und die Korrosionsbeständigkeit untersucht. Zur Charakterisierung der Veränderungen wurden die Gefüge im REM untersucht und der magnetisierbare Anteil sowie die Vickershärte ermittelt. Zum Nachweis korrosionsanfälliger Zustände wurde die elektrochemisch potentiodynamische Reaktivierung (EPR) genutzt. Die Ergebnisse zeigen, dass die Kaltverfestigung die Ausscheidungskinetik beschleunigt und die Korrosionsbeständigkeit durch die Warmauslagerung bei 600 °C deutlich reduziert wird.