Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (38)
- Beitrag zu einem Tagungsband (8)
- Vortrag (3)
Schlagworte
- Neutron imaging (12)
- Neutron tomography (9)
- Neutron radiography (7)
- Tomography (5)
- Computed tomography (4)
- Fuel cell (4)
- Bragg-edge imaging (3)
- Computertomographie (3)
- Debye–Waller factor (3)
- Hydrogen (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
X-ray compton tomography
(2014)
The potentials of incoherent X-ray Scattering (Compton) tomography are investigated. Imaging materials of very different density or atomic number at once is a perpetual challenge for X-ray tomography or radiography, in general. In a basic laboratory set-up for simultaneous perpendicular Compton Scattering and direct beam attenuation tomographic scans are conducted by single channel photon counting. This results in asymmetric distortions of the projection profiles of the scattering CT-data set. ln a first approach corrections of Compton scattering data by taking advantage of rotational symmetry yield tomograms without major geometric artefacts.
A cylindrical sample composed of PE, PA, PVC, glass and wood demonstrates similar Compton contrast for all the substances, while the conventional absorption tomogram only reveals the two high order materials.
Compärison to neutron tomography reveals astonishing similarities except for the glass component (without hydrogen). Therefore, Compton CT bears the potential to replace neutron tomography, which requires much more efforts.
The potentials of incoherent X-ray scattering (Compton) computed tomography (CT) are investigated. The imaging of materials of very different atomic number or density at once is generally a perpetual challenge for X-ray tomography or radiography. In a basic laboratory set-up for simultaneous perpendicular Compton scattering and direct beam attenuation tomography are conducted by single channel photon counting line scans. This results in asymmetric distortions of the projection profiles of the scattering CT data set. In a first approach, corrections of Compton scattering data by taking advantage of rotational symmetry yield tomograms without major geometric artefacts. A cylindrical sample composed of PE, PA, PVC, glass and wood demonstrates similar Compton contrast for all the substances, while the conventional absorption tomogram only reveals the two high order materials. Comparison to neutron tomography
reveals astonishing similarities except for the glass component (without hydrogen). Therefore, Compton CT offers the potential to replace neutron tomography, which requires much more efforts.
Vertebrate bones are made of a nanocomposite consisting of water, mineral and organics. Water helps bone material withstand mechanical stress and participates in sensation of external loads. Water diffusion across vertebrae of medaka (bone material lacking osteocytes) and zebrafish (bone material containing osteocytes) was compared using neutron tomography. Samples were measured both wet and following immersion in deuterated-water (D2O). By quantifying H+ exchange and mutual alignment with X-ray lCT scans, the amount of water expelled from complete vertebra was determined. The findings revealed that anosteocytic bone material is almost twice as amenable to D2O diffusion and H2O exchange, and that unexpectedly, far more water is retained in osteocytic zebrafish bone. Diffusion in osteocytic bones (only 33 % – 39 % water expelled) is therefore restricted as compared to anosteocytic bone (~ 60 % of water expelled), presumably because water flow is confined to the lacunar-canalicular network (LCN) open-pore system. Histology and Raman spectroscopy showed that anosteocytic bone contains less proteoglycans than osteocytic bone. These findings identify a previously unknown functional difference between the two bone materials. Therefore, this study proposes that osteocytic bone retains water, aided by non-collagenous proteins, which contribute to its poroelastic mechano-transduction of water flow confined inside the LCN porosity.
In-situ-Neutronenradiografie wird erfolgreich eingesetzt, um flüssiges Wasser in Niedertemperatur-PEM-Brennstoffzellen während des Betriebs zerstörungsfrei abzubilden und das sogenannte Wassermanagement eine der größten Herausforderungen der Entwicklung durch Anpassung der Materialeigenschaften zu optimieren. Dabei werden die besonderen Eigenschaften der Neutronen genutzt, die metallische Bauteile relativ leicht durchdringen, während selbst kleine Wassermengen durch ihre starke Streuung leicht nachweisbar sind. Die relativ langen Messzeiten für die Neutronentomografie werden durch den Betrieb der Zelle im angehaltenen Zustand realisierbar, sodass die dreidimensionale Wasserverteilung darstellbar wird.
Ein effektives Wassermanagement ist ein wichtiger Aspekt in der Entwicklung von Brennstoffzellen hinsichtlich Langzeitstabilität und Optimierung der Leistungsfähigkeit. Eine zentrale Rolle spielt dabei die Gasdiffusionslage, die für die gleichmäßige Verteilung der Reaktionsgase auf die elektrochemisch aktive Schicht (Katalysator) sorgen soll. In diesem Beitrag werden gemeinsame Forschungsaktivitäten des Helmholtz-Zentrums Berlin für Materialien und Energie (Entwicklung bildgebender Verfahren) sowie des Zentrums für Sonnenenergie- und Wasserstoff-Forschung (ZSW, Entwicklung von Brennstoffzellen) vorgestellt. Im Rahmen dieser Kooperation werden die Entstehung, die Verteilung und der Transport von flüssigem Wasser, kurz das Wassermanagement, unter Betriebsbedingungen untersucht. Mittels Synchrotronradiografie und -tomografie werden kleinste Wassercluster in der Gasdiffusionslage detektiert. Die gewonnenen Erkenntnisse dienen der Modifikation und einer gezielten Auswahl der eingesetzten Materialien.
Metastable austenitic stainless steel (304L) samples with a rectangular cross-section were plastically deformed in torsion during which they experienced multiaxial stresses that led to a complex martensitic phase distribution owing to the transformation induced plasticity effect. A three-dimensional characterization of the phase distributions in these cm-sized samples was carried out by wavelength-selective neutron tomography. It was found that quantitatively correct results are obtained as long as the samples do not exhibit any considerable preferential grain orientation. Optical microscopy, electron backscatter diffraction, and finite element modeling were used to verify and explain the results obtained by neutron tomography. Altogether, neutron tomography was shown to extend the range of microstructure characterization methods towards the meso- and macroscale.
Metastable austenitic stainless steel (304L) samples with a rectangular cross-section were plastically deformed in torsion during which they experienced multiaxial stresses that led to a complex martensitic phase distribution owing to the transformation induced plasticity effect. A three-dimensional characterization of the phase distributions in these cm-sized samples was carried out by wavelength-selective neutron tomography. It was found that quantitatively correct results are obtained as long as the samples do not exhibit any considerable preferential grain orientation. Optical microscopy, electron backscatter diffraction, and finite element modeling were used to verify and explain the results obtained by neutron tomography. Altogether, neutron tomography was shown to extend the range of microstructure characterization methods towards the meso- and macroscale.
Aufgrund des hohen Wirkungsgrades und der vielfältigen Einsatzmöglichkeiten können Brennstoffzellen einen wichtigen Beitrag zur zukünftigen Energieversorgung leisten. Für die Optimierung der Brennstoffzellentechnik ist es erforderlich, die während des Zellbetriebs ablaufenden Prozesse zu verstehen und exakt zu charakterisieren. Ein ausbalanciertes Wassermanagement ist die Grundlage für die optimale Leistungsfähigkeit einer wasserstoffbetriebenen Zelle. Das während des Betriebs entstehende Wasser muss die Membran ausreichend befeuchten, um deren Protonenleitfähigkeit aufrechtzuerhalten. Andererseits behindern zu große Wasseransammlungen in der Zelle die Gaszufuhr durch die porösen Materialien sowie in den Kanälen der Gasverteilerstrukturen. Alterungsphänomene einzelner Zellkomponenten können die Verteilung der Wasseransammlungen und somit das Wassermanagement empfindlich stören und so die Leistungsfähigkeit der Brennstoffzelle herabsetzen. Zur Analyse der Wasserverteilung werden zerstörungsfreie, bildgebende Methoden, wie die Ex-situ-Neutronentomografie und die In-situ-Synchrotronradiografie, eingesetzt. Diese Methoden können während des Brennstoffzellenbetriebs mit weiteren Messverfahren, beispielsweise der ortsaufgelösten Stromdichtemessung, kombiniert werden. Auf diese Weise werden einzelne Komponenten, wie zum Beispiel die Gasdiffusionsschichten, charakterisiert.
Auf Grund des hohen Wirkungsgrades und der vielfältigen Einsatzmöglichkeiten stellen Brennstoffzellen sowie Brennstoffzellenverbünde eine vielversprechende Energiequelle dar. Daher ist es wichtig, die Prozesse während des Betriebs einer Brennstoffzelle exakt charakterisieren zu können, um diese im nächsten Schritt zu optimieren.
So ist ein ausbalanciertes Wassermanagement in einer mit Wasserstoff betriebenen Zelle ausschlaggebend für ihre Leistungsfähigkeit. Für eine dauerhafte Leistungsfähigkeit muss das entstehende Wasser die Membran feucht halten, um so die Protonenleitfähigkeit aufrecht zu erhalten. Zu viel Wasser kann jedoch die Gaszufuhr durch die porösen Materialien in Richtung Membran verhindern.
Alterungsphänomene der einzelnen Komponenten können dieses sensible Wassermanagement stören und so die Leistungsfähigkeit einer Brennstoffzelle
herabsetzen. Zum tieferen Verständnis der Wasserverteilung werden zerstörungsfreie Methoden, wie zum Beispiel die ex situ Neutronentomografie oder die in situ Synchrotronradiografie eingesetzt. Letztere Methode kann während des Brennstoffzellenbetriebs in Kombination mit weiteren Messmethoden, wie der ortsaufgelösten Stromdichtemessung, eingesetzt werden. So können einzelne Brennstoffzellenkomponenten, wie die Gasdiffusionsschichten, charakterisiert werden.
Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam). The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature Ms since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging.
Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam).
The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature M s since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging.
Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic
stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial
resolution of 100 µm.
This paper gives a brief overview on3D imaging of magnetic domains with shearing grating neutron tomography. We investigated the three-dimensional distribution of magnetic domain walls in the bulk of a wedge-shaped FeSi single crystal. The width of the magnetic domains wasanalyzed at different locations within the crystal. Magnetic domains close to the tip of the wedge are much smaller than in the bulk. Furthermore, the three-dimensional shape of individual domains wasinvestigated. We discuss prospects and limitations of the applied measurement technique.
Magnetic domains have been the subject of much scientific investigation since their theoretical existence was first postulated by P.-E. Weiss over a century ago. Up to now, the three-dimensional (3D) domain structure of bulk magnets has never been observed owing to the lack of appropriate experimental methods. Domain analysis in bulk matter thus remains one of the most challenging tasks in research on magnetic materials. All current domain observation methods are limited to studying surface domains or thin magnetic films. As the properties of magnetic materials are strongly affected by their domain structure, the development of a technique capable of investigating the shape, size and distribution of individual domains in three dimensions is of great importance. Here, we show that the novel technique of Talbot-Lau neutron tomography with inverted geometry enables direct imaging of the 3D network of magnetic domains within the bulk of FeSi crystals.
We investigated hydrogen embrittlement and blistering in electrochemically hydrogen-charged technical iron samples at room temperature. Hydrogen-stimulated cracks and blisters and the corresponding hydrogen distributions were observed by neutron tomography. Cold neutrons were provided by the research reactor BER II to picture the sample with a spatial resolution in the reconstructed three-dimensional model of ~25 µm. We made the unique observation that cracks were filled with molecular hydrogen and that cracks were surrounded by a 50 µm wide zone with a high hydrogen concentration. The zone contains up to ten times more hydrogen than the bulk material. The hydrogen enriched zone can be ascribed to a region of increased local defect density. Hydrogen also accumulated at the sample surface having the highest concentration at blistered areas. The surfaces of the brittle fractured cracks showed micropores visualized by scanning electron microscopy. The micropores were located at grain boundaries and were surrounded by stress fields detected by electron backscattered diffraction. The cracks clearly originated from the micropores.
The neutron imaging instrument CONRAD was operated as a part of the user program of the research reactor BER‐II at Helmholtz‐Zentrum Berlin (HZB) from 2005 to 2020. The Instrument was designed to use the neutron flux from the cold source of the reactor, transported by a curved neutron guide. The pure cold neutron spectrum provided a great advantage in the use of different neutron optical components such as focusing lenses and guides, solid‐state polarizers, Monochromators and phase gratings. The flexible setup of the instrument allowed for implementation of new methods including wavelength‐selective, dark‐field, phase‐contrast and imaging with polarized neutrons. In summary, these developments helped to attract a large number of scientists and industrial customers, who were introduced to neutron imaging and subsequently contributed to the Expansion of the neutron imaging community.
This study was carried out to investigate the neutron transmission signal as a function of sample temperature during a welding process. A theoretical description that includes the Debye-Waller factor was used to describe the temperature influence on the neutron crosssections. Neutron imaging using a monochromatic beam helps to observe transmission variations related to the material temperature. In-situ neutron imaging of welding experiments show the distribution of the temperature in bulk steel samples. The performed finite element modelling of expected temperature distributions shows good agreement with the obtained experimental data.
A systematic study has been carried out to investigate the neutron transmission signal as a function of sample temperature. In particular, the experimentally determined wavelength-dependent neutron attenuation spectra for a martensitic steel at temperatures ranging from 21 to 700°C are compared with simulated data. A theoretical description that includes the Debye–Waller factor in order to describe the temperature influence on the neutron cross sections was implemented in the nxsPlotter software and used for the simulations. The analysis of the attenuation coefficients at varying temperatures shows that the missing contributions due to elastic and inelastic scattering can be clearly distinguished: while the elastically scattered intensities decrease with higher temperatures, the inelastically scattered intensities increase, and the two can be separated from each other by analysing unique sharp features in the form of Bragg edges. This study presents the first systematic approach to quantify this effect and can serve as a basis , for example, to correct measurements taken during in situ heat treatments, in many cases being a prerequisite for obtaining quantifiable results.
Spectral neutron tomography
(2021)
Combined three-dimensional (3D) mapping of (micro-)structures with elemental and crystalline phase variations is of significant importance for the characterization of materials. Neutron wavelength selective imaging is a spectral imaging technique that exploits unique contrast differences e.g. for mapping dissimilar elemental, isotope, or phase compositions, and has the particular advantage of being applicable to sample volumes on the meso- and macroscale. While being mostly applied as radiography (2D) so far, we herein report that the extension to tomography allows for the display of the full spectral information for every voxel and in 3D. The development is supported by example data from a continuous as well as a pulsed neutron source. As a practical example, we collected 4D data sets (3D + spectral) of plastically deformed metastable stainless steel and herein demonstrate an improved quantification strategy for crystalline phase fractions. These exemplary results illustrate that localized phase transformations can be quantified even in complex geometries within centimeter-sized samples, and we will discuss the limits and future prospects of the technique that is not limited to crystalline materials.
Die Aufklärung spezifischer Fragestellungen zur Funktionalität von PEM(polymer electrolyte membrane)- und DMFC(Direct Methanol)-Brennstoffzellen bedarf der 3D-Abbildung der spezifischen Komponenten mit unterschiedlichen Strahlungsarten: des Wassergehalts in den Flow Fields mit Neutronen, der Katalysator-Alterung in der MEA (membrane electrode assembly) mit Synchrotronstrahlung und der freien (reaktiven) Katalysator-Oberfläche von Nano-Partikeln mit TEM-Elektronen-Tomografie. Diese Messungen im Bereich der mm- bis nm-Skala unterliegen dabei erheblichen Restriktionen: einer ortsabhängigen Verschmierung der Neutronenradiogramme, Manipulatorinstabilitäten der Synchrotronmessungen sowie einer Kombination von Limited-View-Datensätzen, wenigen Projektionswinkeln und teilweiser Nichtdurchstrahlbarkeit in der Elektronen-CT. Die Vorteile eines fortentwickelten Directt-Algorithmus für die Bewältigung dieser Randbedingungen gegenüber gefilterten Rückprojektionen werden aufgezeigt.