For higher operational temperatures and pressures required in petrochemical plants, the modified 13CrMoV9-10 steel was developed providing high resistance against creep and compressed hydrogen. Extreme care during the welding procedure is necessary for this steel, attributed to low toughness, high strength in as-welded state, and increased susceptibility to stress relief cracking (SRC) during post-weld heat treatment (PWHT). Previous research of SRC in creep-resistant steels discussed mainly thermal and metallurgical factors. Few previous findings addressed the influences of welding procedure on crack formation during PWHT considering real-life manufacturing conditions. These investigations focus on effects of welding heat control on stresses during welding and subsequent PWHT operations close to realistic restraint and heat dissipation conditions using a special 3D testing facility, which was presented in parts I and II of this contribution. Part III addresses investigations on residual stress evolution affecting crack formation and discusses the transferability of results from large-scale testing to laboratory-scale. Experiments with test set-ups at different scales under diverse rigidity conditions and an assessment of the residual stresses of the weld-specimens using X-ray (surface near) and neutron diffraction analysis (bulk) were performed. This study aims to provide a way of investigating the SRC behaviour considering component-specific residual stresses via small-scale testing concepts instead of expensive weld mock-ups.
Von der Anwendung ins Prüflabor: Maßstabsgetreues Bewerten von Spannungen in geschweißten Bauteilen
(2019)
Eigenspannungen sind von zentraler Bedeutung für die Performance geschweißter Bauteile. Die Bewertung schweißbedingter Beanspruchungen im Labormaßstab ist oft nicht zielführend. Reale Bauteilschweißungen weisen geometrisch und konstruktiv bedingt meist divergente Wärmeableitungs- und Einspannbedingungen auf. Dadurch lassen sich häufig nur eingeschränkt Aussagen über Eigenspannungshöhen, -verteilungen und die wesentlichen Einflussfaktoren treffen. Dies führt oftmals zur eher konservativen Konstruktionsauslegung und damit zu einer geringerenRessourcen- und Energieeffizienz. Dieser Beitrag widmet sich den Bestrebungen, reale Randbedingungen beim Bauteilschweißen in das Labor zu übertragen. Es werden die Möglichkeiten eines speziell für diesen Zweck an der BAM entwickelten Prüfsystems mit einer maximalen Tragkraft von 2 MN aufgezeigt. Durch die konstruktive Gestaltung der Anlage lassen sich in Schweißversuchen schweißbedingte Beanspruchungen nachbilden und die komplexen Einflüsse und Wechselwirkungen durch Schweißprozess, Bauteilgeometrie und -konstruktion sowie durch die eingesetzten Grund- und Zusatzwerkstoffe quantifizieren. Darüber hinaus können mittels Röntgenbeugung die resultierenden lokalen Eigenspannungen präzise und mit hoher Ortsauflösung bestimmt werden. Anhand von Beispielen wird die Nachbildung realer Produktionsbedingungen im Labor erörtert und gezeigt, wie die Spannungen beim Schweißen hochfester Baustähle von konstruktiven, werkstoff- und prozessseitigen Randbedingungen abhängen.
So wurde geklärt, wie erhöhte Arbeitstemperaturen zum signifikanten Anstieg der Beanspruchungen führen.
In modernen Schweißkonstruktionen des Stahl- und Ingenieurbaus werden zunehmend hochfeste Feinkornbaustähle eingesetzt. Grundsätzlich sind während der schweißtechnischen Verarbeitung hochfester Stahlgüten aufgrund ihres speziellen Gefüges und wegen ihres vergleichweise hohen Streckgrenzenverhältnisses engere Verfahrensgrenzen einzuhalten, als bei Stählen mit niedrigerer Festigkeit. Die Sicherheit von hochfesten Schweißverbindungen erfordert präzise Kenntnisse über die Höhe und Verteilung der schweißbedingten Beanspruchungen, da sie die erreichbare Tragfähigkeit unmittelbar beeinflussen. In den Untersuchungen wurde der Einfluss der Wärmeführung in Form der Zwischenlagentemperatur und Streckenenergie auf die Eigenspannungsausbildung und Gesamtbeanspruchung in hochfesten Schweißverbindungen ermittelt. Zur Berücksichtigung einer äußeren Bauteilsteifigkeit wurden die Proben in Nahtquerrichtung unter einem definierten Einspanngrad in einer speziellen Prüfanlage (CTW-Test) mehrlagig geschweißt. Es zeigte sich beispielsweise, dass insbesondere die Zwischenlagentemperatur einen direkten Einfluss auf die globalen Reaktionsspannungen hat. Ferner bedingt die Erhöhung der Wärmeführung ein deutliches Anheben der Zugeigenspannungen im Bereich des Schweißgutes.
Große Materialstärken und komplexe Strukturen bewirken eine erhebliche Schrumpfbehinderung der Schweißnaht.
Die aus dem Schweißprozess resultierenden multiaxialen Belastungen tragen maßgeblich zur Gesamteigenbeanspruchung einer Schweißkonstruktion bei und lassen sich nur unter realen Fertigungsbedingungen analysieren.
Zur wirklichkeitsnahen Simulation der komplexen Steifigkeitsverhältnisse realer Bauteile wurden hierzu in einer speziellen 3D-Prüfanlage UP-Mehrlagenschweißungen am warmfesten Stahl 13CrMoV9-10 durchgeführt. Während der schweißtechnischen Fertigung sowie der Abkühlung auf Raumtemperatur wurden die Proben an der freien Ausdehnung und Schrumpfung gehindert. Der Einfluss der Wärmeführung, d.h. Streckenenergie (E) und Vorwärm-/Zwischenlagentemperatur (T(Pli>), auf die resultierende Bauteilbeanspruchung wurde durch in-situ Messungen der Reaktionskräfte (Fy) und Biegemomente (Mx) während des Schweißens und der anschließenden Wasserstoffarmglühung untersucht. Sowohl die Reaktionskräfte als auch die Biegemomente steigen mit zunehmender Vorwärmtemperatur an und somit erhöht sich die Beanspruchung des Wurzelbereiches. Während die Vorwärm-/Zwischenlagentemperatur einen signifikanten Einfluss auf die resultierenden Reaktionskräfte hat, ist der Einfluss auf die Biegemomente nach Abkühlung auf Raumtemperatur vernachlässigbar. Eine Erhöhung der Streckenenergie wirkt sich nur geringfügig auf die Höhe der Endreaktionskraft aus, beeinflusst aber signifikant das resultierende Biegemoment nach erfolgter Abkühlung auf Raumtemperatur.
A 20 mm thick heat resistant 13CrMoV9-10 steel was welded using a multi-pass submerged arc tandem setup on a 3-D testing facility designed to prevent shrinkage both during the welding and the subsequent cooling to room temperature. The effects of variations in pre-heating and interpass temperatures on the local stresses were monitored by in situ measurement of reaction forces and bending moments during welding and the subsequent dehydrogenation heat treatment. The austenite to bainite transformation and its effects on the overall loads were monitored through the use of a high sampling rate. Increasing the pre-heating and interpass temperatures led to a rise in reaction forces and bending moments. The bending moments originated from the eccentric force transmission over the backing, with a concomitant risk of fracture, especially in the critical root zone. Although the pre-heating and interpass temperatures had a strong effect on the reaction forces, their effect on the bending moments upon cooling to room temperature was negligible.
In einer speziellen 3D-Prüfanlage zur wirklichkeitsnahen Simulation von komplexen Verhältnissen an Großproben wurden UP-Mehrlagenschweißungen am warmfesten Stahl 13CrMoV9-10 durchgeführt. Während der schweißtechnischen Fertigung und der Abkühlung auf Raumtemperatur wurden die Proben an der freien Ausdehnung und Schrumpfung gehindert. Die daraus resultierenden Reaktionsspannungen führten während der Wärmenachbehandlung zu Relaxationsrissen in der Wärmeeinflusszone. Das Spannungsarmglühen wurde bei einer Temperatur von 705°C und einer Haltezeit von 8 h durchgeführt. Während der Aufheiz- und Abkühlphasen wurde die thermische Ausdehnung der Probe über die 3D-Prüfanlage kompensiert und damit das Spannungsniveau bis zum Erreichen der maximalen Glühtemperatur aufrechterhalten. Nach Erreichen der Glühtemperatur konnte die Probe relaxieren. Der Einsatz der Schallemissionsmessung ermöglichte es die Entstehung von Spannungsrelaxationsrisse, erstmalig online, nachzuweisen. Durch Synchronisierung der Schallemissionsereignisse mit den Messdaten der 3D – Prüfanlage wurde der kritische Temperaturbereich für das Auftreten von Spannungsrelaxationsrissen bestimmt. Die Rissinitiierung findet im Temperaturbereich zwischen 350°C - 500°C statt. Aussagen über das Risswachstum können auf Grund der ungünstigen Versuchsbedingungen, mit Emission von Störgeräuchen, nicht getroffen werden.
The article "Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part I - Effect of heat control on welding stresses and stress relief cracking" was originally published in the journal "Welding in the world" Online First without Open Access. After publication in volume 64, issue 5, page 807-817 the authors decided to opt for Open Choice and to make the article an Open Access publication. Therefore, the copyright of the article has been changed to The Author(s) 2020 and the article is forthwith distributed under the terms of the Creative Commons Attribution Attribution 4. 0 International License.
The article "Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part II - Mechanisms of stress relief cracking during post weld heat treatment" was originally published in the journal "Welding in the world" Online First without Open Access. After publication in volume 64, issue 5, page 819-829 the authors decided to opt for Open Choice and to make the article an Open Access publication. Therefore, the copyright of the article has been changed to The Author(s) 2020 and the article is forthwith distributed under the terms of the Creative Commons Attribution Attribution 4. 0 International License.
The avoidance of failures during the fabrication or operation of petrochemical reactors made of creep-resistant, low-alloy steels as 13CrMoV9-10 requires still research despite over 60 years of international investigations in the field of stress relief cracking. The quality of modern base materials and filler metals leads to the fact that previously known crack causes, such as impurities of S or P, recede into the background. Rather, the causes are increasingly to be found in the fabrication process. Investigations on the influence of heat control on the stresses in welded components and thus on the stress relief cracking sensitivity under realistic manufacturing conditions are not yet available. This work is subdivided in two parts. Part 1 of this study focused on the effect of heat control during submerged arc welding on the stresses. For this purpose, a testing facility was applied, which allows to observe the forces and moments accumulating during welding or heat treatment in a component-like specimen under shrinkage restraint. The stress acting in the specimen increases with higher preheat/interpass temperatures and higher heat input. During the heat treatment, the stresses are relieved. Nevertheless, cracks are formed already during heating. The total crack length correlates with the heat input.
Welding of 13CrMoV9-10 vanadium steel requires care due to an increased susceptibility to stress relief cracking during post weld heat treatment. Previous research into the crack formation in creep-resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gathered regarding the crack formation during post weld heat treatment considering real-life restraint conditions. This work is subdivided in two parts. Part I showed that an increasing heat input during submerged arc welding under restraint led to an increasing stress level in the joint prior to the post weld heat treatment. The magnitude of stress relief cracking observed in the heat-affected zone after the post weld heat treatment is affected by the heat input. In Part II of this work, the cracks and the associated microstructure which occurred under restraint were studied. The application of a Special acoustic emission analysis indicated that the cracks formed in a temperature range between 300 and 500 °C during the post weld heat treatment. The toughness in the heat-affected zone of the restrained welds was affected by the welding heat input.
Microstructural analyses of all specimens revealed accelerated aging due to precipitation of carbides during post weld heat treatment under restraint.