Polynuclear aluminium species (Al13 keggin cluster) find application in different areas like water purification [1], contaminant transport [2], and as pilling clays with high specific surface areas[3], due to their strong binding ability to aggregates and high positive charge.
In the present contribution, we report on the in situ investigation of the Al13 sulfate synthesis by synchrotron wide-angle X-ray scattering (WAXS). Al13 cluster were crystallized by precipitating hydrolyzed aluminum solutions by the addition of sodium sulfate. The measurements were performed using a custom-made acoustic levitator as sample holder. The study provides information about the intermediates during the crystallization process. From the data, a mechanism was derived indicating the influence of the crystallization process.
Polynuclear aluminium species (Al13 keggin cluster) find application in different areas like water purification, contaminant transport, and as pilling clays with high specific surface areas, due to their strong binding ability to aggregates and high positive charge.
In the present contribution, we report on the in situ investigation of the Al13 sulfate synthesis by synchrotron wide-angle X-ray scattering (WAXS). Al13 cluster were crystallized by precipitating hydrolyzed aluminum solutions by the addition of sodium sulfate. The measurements were performed using a custom-made acoustic levitator as sample holder. The study provides information about the intermediates during the crystallization process. From the data, a mechanism was derived indicating the influence of the crystallization process.
Combination of fast-XANES and SAXS for studying the formation mechanism of maghemite nanoparticles
(2015)
The mechanochemical synthesis of the zinc N-(phosphonomethyl)glycinate Zn(O₃PCH₂NH₂CH₂CO₂) H₂O is presented. The structure was solved from powder X-ray diffraction (PXRD) data. In the three-dimensional pillared structure, the Zn atoms are coordinated tetrahedrally. In situ investigations of the reaction process with synchrotron PXRD and Raman spectroscopy reveal a two-step process including the formation of an intermediate.
Detection of the electronic structure of iron-(III)-oxo oligomers forming in aqueous solutions
(2017)
The nature of the small iron-oxo oligomers in iron-(III) aqueous solutions has a determining effect on the chemical processes that govern the formation of nanoparticles in aqueous phase. Here we report on a liquid-Jet photoelectron-spectroscopy experiment for the investigation of the electronic structure of the occurring iron-oxo oligomers in FeCl3 aqueous solutions. The only iron species in the as-prepared 0.75 M solution are Fe3+ monomers. Addition of NaOH initiates Fe3+ hydrolysis which is followed by the formation of iron-oxo oligomers. At small enough NaOH concentrations, corresponding to approximately [OH]/[Fe] = 0.2–0.25 ratio, the iron oligomers can be stabilized for several hours without engaging in further aggregation. Here, we apply a combination of non-resonant as well as iron 2p and Oxygen 1s resonant photoelectron spectroscopy from a liquid microjet to detect the electronic structure of the occurring species. Specifically, the oxygen 1s partial electron yield X-ray absorption (PEY-XA) spectra are found to exhibit a peak well below the onset of liquid water and OH (aq) absorption. The iron 2p absorption gives rise to signal centered between the main absorption bands typical for aqueous Fe3+. Absorption bands in both PEY-XA spectra are found to correlate with an enhanced photoelectron Peak near 20 eV binding energy, which demonstrates the sensitivity of resonant photoelectron (RPE) spectroscopy to mixing between iron and ligand orbitals. These various signals from the iron-oxo oligomers exhibit Maximum intensity at [OH]/[Fe] = 0.25 ratio. For the same ratio, we observe changes in the pH as well as in complementary Raman spectra, which can be assigned to the Transition from monomeric to oligomeric species. At approximately [OH]/[Fe] = 0.3 we begin to observe particles larger than 1 nm in radius, detected by small-angle X-ray scattering.
Mechanochemistry is increasingly used for synthesizing various materials. Although this synthesis approach offers a fast and pure synthesis in high yields, there is a lack in understanding the mechanisms of milling reactions. The necessary data can only be obtained by in situ experiments, which were only recently established for milling reactions. Herein, we present a novel setup combining in situ synchrotron XRD and Raman spectroscopy. This combination allows to study milling processes comprehensively on the level of the molecular and crystalline structure and thus obtaining reliable data for mechanistic studies. The formation process of MOFs, metal phosphonates and model cocrystals could be studied in detail. The results prove that the presented method combination is applicable for a wide range of materials and will provide the necessary understanding to tune and optimize mechanochemically synthesized compounds.
Polynuclear cationic aluminum hydroxide phases are known intermediates in the formation of aluminum oxides or (oxide) ydroxides upon hydrolysis of aluminum salt solutions. In the presence of sulfate anions, these aluminum polyoxocations (Al13) can form crystalline Al13 sulfates with varying chemical composition.
The formation of these Al13 sulfates in aqueous solution has been poorly understood. Here, we investigate the early stage crystallization of Al13 clusters in a sulfate-containing solution, in situ and in real time. Dynamics associated with Al13 sulfate formation have been obtained for the first time, using Synchrotron X-ray diffraction (XRD) of solutions suspended by acoustic levitation. Time-resolved in situ data show that the cubic phase, Na [(AlO4)Al12(OH)24(H2O)12](SO4)4*10H2O, forms after only minutes. The Formation mechanism of Al13 sulfates was found to depend on the sulfate:aluminum (SO4:Al) ratio. Ex situ XRD of the product Al13 sulfates in solution shows that for SO4:Al ratio ≤ 1.5 two other crystalline phases form, and convert to the cubic phase upon washing and drying. In situ XRD for the same ratio shows transient formation of an intermediate during the crystallization process.
The production of formaldehyde on industrial scale requires huge amounts of energy due to the involvement of reforming processes in combination with the demand in the megaton scale. Hence, a direct route for the transformation of (bio)methane to formaldehyde would decrease costs and puts less pressure on the environment. Herein, we report on the use of zinc modified silicas as possible support materials for vanadium catalysts and the resulting consequences for the performance in the selective oxidation of methane to formaldehyde. After optimization of the Zn content and reaction conditions, a remarkably high space-time yield of 12.4 kgCH2O⋅kgcat − 1 ⋅h− 1 was achieved. As a result of the extensive characterization by means of UV–vis, Raman, XANES and NMR spectroscopy it was found that vanadium is in the vicinity of highly dispersed zinc atoms which promote the formation of active vanadium species as supposed by theoretical calculations. This work presents a further step of catalyst development towards direct industrial methane conversion which may help to overcome current limitations in the future.