Schlagworte
- Rheology (31)
- Repair mortar (12)
- Rheologie (11)
- Betoninstandsetzung (10)
- Cement (10)
- Concrete (10)
- Geopolymers (9)
- Self-compacting concrete (9)
- Instandsetzung (8)
- Instandsetzungsmörtel (8)
Organisationseinheit der BAM
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (59)
In paper recycling large amounts of waste sludge, containing organics as well as inorganic fillers of the recycled paper, are produced. A large fraction of these sludges is incinerated; the ashes generated in this process, often referred to as wastepaper sludge ash (WSA), have the potential to be used as binder material, either alone or as supplementary cementitious material. However, ashes from different paper mills differ in their Chemical and mineralogical composition, thus, the reaction products and the properties of the hardened binders may vary s i gn i fi cantley.
In the present study, a calcite-rich WSA was analyzed for reaction products and strength development. The WSA contained, besides calcite, hydraulic phases such as tricalcium aluminate (C3A) and belite (C2S), lime as well as inert phases. When activated with water, the WSA yielded a compressive strength of up to 12.3 MPa and the major hydration product was monocarboaluminate (C4A CO2 IIH2O or C4ACH11). Activation with 2M NaOH or 2M KOH solution caused a more rapid strength gain until one day of curing, but afterwards the strength development slowed down and the strength afiter 28 days was significantly lower than for the water-activated pastes. From TG analyses it is apparent that the higher strength of the alkaliactivated pastes after one day of curing was caused by a more rapid consumption of calcite and associated formation of C4ACH11. At later curing times the amount of calcite did not change substantially and consequently strength development almost ceased.
The results demonstrate the complex influence of alkaline conditions on the hydration of WSA and show that the reaction products, which determine the durability properties of the hardened pastes (and materials made from it), of the calcite-rich WSA differ from the products of other WS As, as discussed in the article.
Despite the numerous possibilities to influence the properties of repair mortars by modifications of the mixture proportioning, it is almost impossible to change an individual property without influencing other mortar properties. When optimising a mixture, it has to be decided for each individual case, which of the mortar properties needs to be treated with the highest priority. Most properties can be altered by several different measures, which may vary in effectiveness, side effects and cost efficiency. As the prevention of shrinkage induced constraining cracks is crucial for the durability and Service life of a concrete repair task, in the presented paper special attention is paid to the influences on the mortar’s shrinkage behaviour. On the basis of parameter studies it is shown, how it may be beneficial in certain cases to accept the worsening of some general properties if by this measure another property, which is essential for the individual application task, can be enhanced significantly. In general a tailor-made approach for the mixture proportioning seems beneficial but due to the complexity of the constituents’ interactions in repair mortars, it bears a high risk of unexpected malfunctions.
Main topics of the research project BEGLARES are the restoration of "dalle de verre" concrete Windows and the development of repair techniques and mortars. This project is executed in Cooperation between Glasmalerei Peters GmbH, the University of York and the BAM Federal Institute for Materials Research and Testing. It is funded by the Federal Ministry of Economics and Technology. The main mechanism of damages, the development of repair mortar and special test specimens are presented.
Hochfeste und ultrahochfeste Stahlfaserbetone eignen sich aufgrund ihrer Eigenschaften für den Einsatz bei extremen mechanischen Beanspruchungen. Das für diesen Einsatz erforderliche duktile Bruchverhalten unter Zugbeanspruchung wird ausschließlich durch die Zugabe von geeigneten Stahlfasern und deren Wirkung in der Zementsteinmatrix erreicht. Für eine gezielte stoffliche Optimierung des Systems sind fundierte Kenntnisse zur Wirkungsweise der Stahlfasern notwendig, die bei bisherigen Untersuchungen lediglich auf Basis von klassischen Messverfahren zerstörender Prüfungen gewonnen wurden. Durch das Einbeziehen von Methoden der zerstörungsfreien Materialcharakterisierung können das Bruchverhalten hochfester und ultrahochfester Stahlfaserbetone orts- und zeitaufgelöst untersucht und die einzelnen Phasen des Schädigungsprozesses identifiziert werden. Anhand der vorliegenden Ergebnisse von Zugversuchen eines ultrahochfesten Stahlfaserbetons wird der kombinierte Einsatz von Methoden der zerstörungsfreien Materialprüfung gezeigt und deren Anwendbarkeit in der Analyse des Bruchverhaltens diskutiert. Das Hauptaugenmerk liegt dabei auf der Charakterisierung der ausschlaggebenden Versagensmodi unter Zugbelastung durch die einzelnen Verfahren und dem Vergleich zu klassischen Messmethoden (z. B. Extensometer). Die Zugversuche wurden dazu parallel durch optische Verformungsanalyse mittels Bildkorrelation (DIC), Schallemissionsanalyse (SEA) und 3-D-Computertomografie (CT) begleitet.
Geopolymers are promising alkali activated materials with a wide range of possible applications like heat-resistant coatings and adhesives or concretes with lower C02 emissions than conventional Portland cement-based systems. Conventional ("two-part") geopolymers are synthesized by an activation of aluminosilicate feedstocks like metakaolin or blast furnace slags with highly alkaline solutions like sodium hydroxide solutions and/or water glass solutions.
A more recent approach are so called one-part geopolymers, where the alkaline activator is provided in solid form, so that only water has to be added to initiate the geopolymerisation reaction. The handling of alkaline solutions is avoided, which possesses several advantages compared to conventional geopolymers, in particular regarding safety and health issues, and, thus, it improves economic and social acceptance of these binders. However, the new formulations are less exhaustively studied and the knowledge about conventional geopolymers cannot simply be transferred to this new class of binders.
In urbanen Zentren schreitet die Versiegelung von Oberflächen voran. Ursache ist die stetige Zunahme moderner Infrastruktur. Straßen und Plätze heizen sich stärker auf und begünstigen die Entstehung von Hitzeinseln (Urban Heat Island Effect). Dies wirkt sich zunehmend negativ auf die Lebensqualität innerhalb dieser Städte aus. Einen möglichen Lösungsansatz zur Abschwächung dieses Effekts bietet die Entwicklung von Betonpflastersteinen mit erweiterten Leistungsmerkmalen. Der Einsatz von wasserspeichernden Materialien kann zur Verringerung der Oberflächentemperatur durch Ausnutzung von Verdunstungskälte einen Beitrag leisten. Die speziellen Anforderungen an die Pflastersteine bedürfen genauerer Untersuchungen, wobei diese über den Umfang der Standardprüfungen hinausgehen und eine entsprechende Anpassung der Messtechnik zum Nachweis der Wirksamkeit erforderlich machen. Da die selbstkühlenden Pflastersteine nach dem Prinzip der Verdunstung arbeiten, ist sowohl die Fähigkeit der Speicherung als auch die Fähigkeit zur kontinuierlichen Abgabe von Wasser nachzuweisen. Der kühlende Effekt in Bezug auf Oberfläche und Umgebung steht dabei im Vordergrund. Des Weiteren sind Untersuchungen unter verschiedenen klimatischen Bedingungen sowohl unter Laborbedingungen als auch im Freifeldversuch durchzuführen. Die Prüfung der Druckfestigkeit und der kapillaren Wasseraufnahme und des sind ebenfalls Bestandteil der umfangreichen Untersuchungen. Durch den Einsatz von thermischer Messtechnik sowie mechanischer Prüfungen und Untersuchungen zur Dauerhaftigkeit ist es möglich eine Charakterisierung der Pflastersteine vorzunehmen und deren prinzipielle Funktionalität nachzuweisen. In diesem Beitrag werden die verschiedenen Möglichkeiten und die daraus resultierenden Ergebnisse vorgestellt und so Schlüsse zur Funktion und Anwendbarkeit von derartig modifizierten Betonpflastersteinen gezogen.
Entwicklung eines PCC-Leichtmörtels zur Instandsetzung einer denkmalgeschützten Sichtbetonfassade
(2015)
Der Schutz und Erhalt der Originalsubstanz stehen im Mittelpunkt jeglicher denkmalpflegerischer Instandhaltungsmaßnahmen. Das äußere Erscheinungsbild spielt hierbei - im Gegensatz zur klassischen Betoninstandsetzung - eine größere Rolle. Nichtsdestotrotz dürfen die technischen Belange auch hier nicht außer Acht gelassen werden. Die Ermittlung des Ist- und Sollzustands stellt die Grundlage einer dauerhaften Instandsetzung dar. Der vorliegende Beitrag zeigt Schäden und Schadensursachen an einem denkmalgeschützten Gebäude in Leichtbetonbauweise auf. Das Bauwerk wurde hinsichtlich seines Schädigungsgrads, -umfangs und der maßgeblichen Schadensursachen untersucht. Im Rahmen dieser Untersuchungen wurden gehäuft Risse, Abplatzungen und Bewehrungskorrosion festgestellt. Die durch eine Brettschalung strukturierte Sichtbetonfassade soll im Zuge der Instandsetzungsmaßnahme möglichst originalgetreu wiederhergestellt werden.
Bei der Auswahl von geeigneten Instandsetzungsmethoden und -produkten konnte aufgrund fehlender Normen und Richtlinien für die Instandsetzung von denkmalgeschützten Leichtbetonbauten nicht auf bereits existierende Produkte und Methoden zurückgegriffen werden. Daher wurde in Anlehnung an die Richtlinie "Schutz und Instandsetzung von Betonbauteilen" (RL SIB) des DAfStB eine polymermodifizierte Betonergänzungsmasse mit leichter Gesteinskörnung entwickelt. Ausgehend von der Hauptschadensursache, der karbonatisierungsinduzierten Bewehrungskorrosion, wurden erforderliche Eigenschaften der Betonergänzungsmasse in enger Absprache mit der zuständigen Denkmalschutzbehörde und dem involvierten Fachplaner abgestimmt. Neben den grundlegenden mechanischen Eigenschaften spielen in diesem Anwendungsfall spezielle Eigenschaften wie z.B. farbliehe Anpassung der Betonergänzungsmasse, Möglichkeit der Oberflächenstrukturierung, Zeitfenster der Verarbeitbarkeit sowie die Modellierbarkeit eine wichtige Rolle. Der entwickelte PCC-Leichtmörtel berücksichtigt dabei auch den Einfluss einer geringen Schwind- und Quellneigung der Betonergänzungsmasse um Delaminierung infolge unterschiedlicher Längenänderungen zu vermeiden und somit eine dauerhafte Instandsetzung zu gewährleisten. Weiterhin wurde das Verbundverhalten des entwickelten PCCL Leichtmörtels für unterschiedliche Schichtaufbauten untersucht.
Die Herausforderung einer anspruchsvollen Natursteininstandsetzung liegt in der richtigen Zusammensatzung der Steinersatzmassen. Dabei müssen vielerlei, teilweise gegenläufige Interessen miteinander vereinbart werden: Mechanische und bauphysikalische Belange müssen genauso beachtet werden wie denkmalpflegerische und gestalterische Aspekte. Auf die konkreten Anforderungen und Voraussetzungen einer Restaurierungsaufgabe reagieren zu können, ist die Grundvoraussetzung für ein gutes Gelingen. Hilfreich sind hier Mischungen, die modular aufgebaut sind und sich individuell und flexibel an die Erfordernisse anpassen lassen.
Reinforced concrete buildings are frequently damaged by cracks, spalling and corroded
reinforcement bars. The present article focuses on the damage analysis of one of the first
buildings in Berlin that was constructed using reinforced lightweight concrete, which makes it
historically important. The compressive strength, carbonation depth, location and diameter of
reinforcement bars as well as moisture and salt profiles were determined. The carbonationinduced corrosion of the reinforcement bars represented the main damage of the building.
Certified repair mortars with lightweight aggregates (LWA) do not exist on the German
market. Therefore, an appropriate repair mortar was developed in accordance with DIN EN
1504 and the German guideline for the repair and protection of concrete structures (RL-SIB).
On the one hand, historic preservation requirements, such as: colour of the mortar,
possibilities of surface patterning, maximum preservation of the original substance and
reversibility of any Intervention must be met. On the other hand, technical requirements of the
relevant Standards must be achieved. The developed mix was designed to resist the identified
causes of deterioration. Thermal strains within the repair mortar and between the repair
mortar and the Substrate influence the crack formation and thus the durability. Therefore,
special attention was paid to the bonding and shrinking behaviour of the concrete repair
System. By using polymers, both hardened mortar properties and durability were influenced
positively.
Die Funktionalität und Dauerhaftigkeit von Instandsetzungs- und Verstärkungssystemen an Bauwerken hängt in einem hohen Maß von der Beschaffenheit der Bauteiloberfläche ab. Als aussagekräftiger Parameter bei der Instandsetzung dient hierbei die Rauigkeit oder Rautiefe. Die Bestimmung der Rautiefe wird im Baubereich seit vielen Jahrzehnten unter Verwendung des Sandflächenverfahrens durchgeführt. Dieses volumetrische Messverfahren hat sich als robust und sehr praktikabel erwiesen. Es ist vergleichsweise einfach und ohne größeren Kostenaufwand umsetzbar. Dennoch weist es einige Schwächen in der Anwendung auf. Der größte Mangel ist die Beschränkung auf horizontale, trockene Oberflächen. Sowohl auf vertikalen, geneigten oder gekrümmten Oberflächen als auch „über Kopf1 lässt sich dieses Verfahren nicht anwenden. Bedingt durch verschiedene nationale Normen und unterschiedliche Anwendungsbereiche, weichen sowohl die zu verwendenden Prüfmittel als auch die zu ermittelnden Kenngrößen stark voneinander ab. Dies macht eine genaue Kenntnis über die verschiedenen Vorschriften und deren Inhalte notwendig. Ein weiterer Nachteil ist die, durch das Verfahren bedingte, starke Streuung über den „Prüfereinfluss“ in den zu erzielenden Ergebnissen. Untersuchungen zur Wiederholgenauigkeit ergaben Schwankungen von bis zu 20 Prozent in Abhängigkeit von Prüfer und Prüfvorschrift. An der BAM wurde deshalb ein automatisiertes Messsystem entwickelt,
До 1970-х годов производители бетона и ЖБИ определяли свой продукт исключительно как долговечный строительный материал. В последующие годы инженеры-строители ввели такие термины как устойчивость и экспозиция. Современные бетонные технологии учитывают, что определенные строительные материалы (в частности, бетоны) обладают высокой устойчивостью к замораживанию-оттаиванию и расслоению.
This contribution presents the results of structural and compressive strength investigations on cured andhigh-temperature treated silica-based one-part geopolymer-zeolite composites. The specimens weresynthesized from two different silica sources, sodium aluminate and water. The phase content as well asthe compressive strength of the cured composites varied depending on the starting mix-design and thesilica feedstock. Besides geopolymeric gel, A-type zeolites and hydrosodalites were the major reactionproducts. One of the silica feedstocks yielded significantly higher compressive strength (19 MPa), whilethe other one appears to cause less variation in phase content. Strength testing indicated an improvementon heating up to
200–400 °C (28 MPa) followed by a moderate decrease up to 700 °C. Above 700 °C the sys-tems underwent new phase formation and shrinkage (volume decrease) deformations. After exposureat 1000 °C the different mixes consisted of a mix of several stuffed silica phases, almost pure hexago-nal nepheline or amorphous phase. Depending on the mix-design, the onset temperature of the hightemperature phase transformations varied.
The main objective of this work is to determine chloride migration coefficients for alkali activated fly ash-based mortars. The effect of various mixture composition is studied. The identified values will be used in simulations of chloride transport in the alkali-activated composites, mainly to determine a critical time span of exposition to chlorides causing corrosion of reinforcement. Rapid chloride migration experiments (RCM) are performed on cylindrical specimens, 100 mm diameter, 50 mm height. Low voltage electric field (10–30 V DC) is applied as a driving force for the accelerated chloride penetration. The chloride front in the sample is identified according to NT Build 492 standard after given time of penetration (depending on the electrical current ~ 3 hours) on a fracture surface using silver nitrate solution.
Further, accelerated diffusion experiments are performed in order to verify the migration coefficients obtained using RCM. The total chloride content is determined, and chloride profiles obtained on powder ground from separate layers of the specimen.
Alkali-activated slag materials are known for their high Chloride penetration resistance. This makes them potentially applicable as repair systems for damaged steel-reinforced concrete structures, which are exposed to chloride attack. For this purpose, the influence of the activator composition, i.e. the SiO2 and Na2O concentration of the alkaline solution on a) the compressive strength, b) shrinkage and mass change and c) the resistance against chloride penetration of four alkali-activated slag mortars (AASM) were studied. An ordinary Portland cement-based mortar was used as the reference sample. Increasing SiO2 and Na2O concentrations increased the strength, shrinkage and mass loss of the AASMs. The resistance of the mortars against chloride penetration was evaluated using the non-steady-state migration coefficient Dnssm obtained from NT BUILD 492. The results indicate that the Dnssm is related to differences in the pore solution of the AASMs rather than to differences in their microstructure. An upcoming study of the authors is going to evaluate this hypothesis by the accelerated chloride penetration (diffusion) test.
Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads
(2018)
The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed.
One-part alkali-activated (geopolymer) mortars based on three different silica-rich starting materials and sodium aluminate, with and without ground granulated blast furnace slag (GGBFS) addition, were tested regarding sulfuric acid resistance according to DIN 19573:2016-03 (70 days at pH = 1). Corresponding pastes were characterized by XRD, SEM, chemical analysis, 29Si MAS NMR and 1H-29Si CPMAS NMR after water storage and after acid exposure. The mortars exhibited a high resistance against sulfuric acid attack, with the best ones conforming to the requirements of DIN 19573:2016-03. The analytical results showed that this was due to precipitation of silica gel at the acid-mortar interface, which formed a mechanically stable layer that protected the subjacent mortar and thus inhibited further degradation. The addition of GGBFS decreased the acid resistance via formation of expansive calcium sulfate phases.
While calcined clays in general have been credited with a great potential to mitigate CO2 emissions related to cement production and consumption, calcined brick clays are currently understudied in this regard. In the present work, two brick clays, a low-grade kaolinitic clay, and a mixed clay composed of 50% brick clay and 50% low-grade kaolinitic clay were studied regarding transformations on calcination, and strength and durability performance as well as pore structure of mortars made with the blended cements. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the low-grade kaolinitic clay. However, the mixed clay performed very similar to the low-grade kaolinitic clay, which points to a viable option for optimal use of brick clays in cementitious systems. The carbonation resistance of the blended cement mortars was generally worse than that of the plain Portland cement mortar, as expected, but the former exhibited a significantly improved chloride penetration resistance. The latter improvement was due to pore structure refinement in the blended cement mortars, compared to the Portland cement mortar.
Alkali-activated materials are ideal for the repair of concrete structures in harsh environmental conditions due to their high durability in chemically aggressive environments. However, slag-based mortars, in particular, are prone to shrinkage and associated cracks. In this respect, the application of steel fibres is one solution to reduce the formation of shrinkage induced cracks and to improve post cracking behaviour of these mortars. This study investigated the influence of two different types of steel fibres on the tensile properties of two alkali-activated mortars. Direct tensile tests and single fibre pull-outs were performed to analyse the determining failure modes both on macro and micro scale. Mechanical testing was accompanied by non-destructive testing methods such as digital image correlation and acoustic emission for a detailed analysis of the fracture process.
In the last several decades, the rural exodus has led to an increasing number of inhabitants in the urban areas. The increased building and infrastructural construction caused the transformation of the landscape and to an increased land sealing in these areas. Consequently, the increased land sealing influences the air temperatures in the cities, since houses, streets and squares heat up continuously. As a result, the city and metropolitan areas became significantly warmer than their surroundings - the effect is known as Urban Heat Island (UHI). These changes have a negative impact for the quality of life. To deal with the negative effects of UHI, a high level of technical and financial effort is necessary. The costs caused by the UHI effects are in the range of several billion US dollars worldwide per year. The recent studies on UHI showed that the established methods like parks and green spaces or bright coatings for roof areas will soon not be able to effectively cope with the UHI effect in urban areas. Therefore there is a need for additional methods to mitigate UHI effect in the cities. The streets, sidewalks and squares represent approximately 30% to 40% of the inner cities areas. If these areas are designed functionally, they can have a significant impact on the UHI. This contribution focuses on development of a concrete paving stone with self-cooling properties. For the cooling effect the evaporative cooling is used. The paving stone is able to store large quantities of water and deliver during appropriate environmental conditions. This paper deals with the results of the long-term experiments on the test-fields under different climatic conditions. To interpret the test-field-results, laboratory tests were carried out as well. The paper presents and discuss the obtained results, and points out the difficulties occurred.
Untergrundprüfung: Rautiefe, Oberflächenfeuchte und Haftzugfestigkeit, Durchführung und Auswertung
(2015)
Untergrundprüfung: Rautiefe, Oberflächenfeuchte und Haftzugfestigkeit, Durchführung und Auswertung
(2015)
European and Germany regulations demand an elaborate waste management to save natural resources, reduce waste volumes deposited at landfills and enhance sustainable development by recycling of various residues. Research into the use of these materials in the construction sector and other fields is a positive step forward in achieving these objectives. BAM shares its latest findings.
Two brick clays (rich in 2:1 clay minerals) and a low-grade kaolinitic clay were studied regarding their transformations during calcination and their performance in blended cement mortars. The mortars with calcined clays exhibited decreased workability (slump flow), but this effect could be mitigated by employment of a conventional superplasticizer; however, compressive strength of the hardened mortar was lowered in some cases. While the kaolinitic clay generally yielded the highest strength, the performance of a brick clay could be increased by grinding to higher fineness and by mixing it with the kaolinitic clay.
Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles.
In Deutschland fallen jährlich 20 Millionen Tonnen Altpapier an. 75 % davon werden dem Recyclingprozess zugeführt. Dabei bleiben Prozessrückstände wie Deinkingschlämme, Sortierrückstände und Faserreststoffe übrig. Zusammengefasst als Papierschlamm verwerten die Recycler diesen Reststoff thermisch in dezentralen Heizkraftwerken. Die dabei anfallende Papierasche hat mit den Anteilen der Hauptoxide von 59 M.-% CaO, 22 M.-% SiO2 und 13 M.-% Al2O3 eine ähnliche chemische Zusammensetzung wie Portlandzement, wobei sich die Mineralphasen unterscheiden. Durch eine Aktivierung der Papierasche können jedoch hydraulisch aktive Phasen wie Mayenit (C7A12) und Belit (C2S) erzeugt werden. Die Mineralphase Mayenit reagiert schnell mit Wasser zu Calciumaluminathydraten, wodurch der Bindemittelleim schnell ansteift. Die festigkeitsbildenden Calciumsilicathydrate (CSH) in Bindemittelleimen entstehen bei einer späteren Reaktion von Belit mit Wasser.
Zur Aktivierung dient eine hydrothermale Calcinierung. Dabei wird Papierasche mit einer Aktivatorlösung (Wasser oder KOH) gemischt und bei 200 °C hydrothermal behandelt, wobei sich Hydratphasen ausbilden. Diese Zwischenprodukte dehydratisieren durch eine anschließende Calcinierung zu reaktiven Calciumsilicaten und Calciumaluminaten. Wie sich die Parameter des Aktivierungsprozesses auf die Mineralphasen auswirken, war Fokus der Untersuchungen. Mit thermogravimetrischen Analysen der Zwischenprodukte konnten die Reaktionsprodukte nach dem hydrothermalen Prozessschritt bestimmt werden. Den größten Einfluss auf den Mineralphasenbestand hat hierbei die Alkalität der Aktivatorlösung. Im zweiten Prozessschritt, der Calcinierung, ist die Temperatur der wesentliche Faktor für die Ausbildung reaktiver Phasen. Die Ergebnisse kalorimetrischer Untersuchungen an Leimen aus den calcinierten Proben dienten der Auswahl der optimalen Calcinierungstemperatur. Die gesamte Reaktionswärme war für die Proben, welche bei einer Calcinierungstemperatur zwischen 700-800 °C hergestellt wurden, am höchsten.
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
The most common method for determination of the carbonation depth is the sprayed application of indicator solutions, Phenolphthalein in particular. Since the aerosols of Phenolphthalein are suspected to be carcinogenic, efforts have been intensified to use alternative indicators for the determination of carbonation depth. The subject and aim of this research paper are to examine indicator solutions from Alizarin Yellow R, Thymol Blue and a Mixed Indicator. These indicator solutions are commercially available and are not suspected to be carcinogenic.
For the purpose of this research, samples previously stored under accelerated carbonation conditions (1% CO2) were examined by thermogravimetric analysis (TGA) and examination of the pH value. Additionally, the electrolytic back-titration for determination of total CO2 amount was carried out comparatively to TGA.
Global energy consumption will increase in the future necessitating both fossil fuels and renewable energy choices - especially wind energy. Such high energy demand requires installation of offshore energy structures, rigs, platforms and towers, which are susceptible to adverse environmental conditions along with maintenances. Due to their large size and remote locations, cylindrical grouted joints are often adopted between substructure and foundation in these offshore platforms and wind structures such as monopiles. However, these connections are composite structures with exterior sleeve, interior pile and infill mortar. Degradation and settlements were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites were proven difficult to obtain ideal load bearing capacity. In-situ loading conditions were also found to be affecting the failure mechanism inside such connections. This study aims at characterizing the nature of cracks generated in these grouted connections under both static and cyclic loading. Scaled grouted joints were manufactured using a novel reusable mold, and connections were loaded to failure to visualize the main failure patterns. An assessment between failure under these two types of load is drawn along with comparison to previously available literature.
The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose.
The aim of an ongoing research project is to develop a design approach for typical offshore driven piles (e.g. Jacket piles) based on the application of injections by compaction grouting directly at the pile shaft. The paper aims to present the results of laboratory and in-situ tests, which reveal the efficiency and the promising potential of the optimised foundation concept for a more economic dimensioning of pile foundations and to increase their bearing capacity in non-cohesive soil at any moment after installation.
Stone deterioration is the result of a complex interaction of external physical, chemical and biological forces with the mineralogical-petrophysical properties of the stone. With a better understanding of how these properties are linked to material behavior and durability, more effective measures for stone conservation can be developed. Studying these interactions in tuff is particularly complex due to the naturally high heterogeneity of tuff rocks.
The first aim of a current research project is to combine the results of recent and older studies on tuff deterioration. Furthermore, the literature overview is complemented by our own investigation of Weibern and Ettringen tuff, with a focus on pore structure characteristics.
Grouted connections are intensively used in offshore rigs, platforms as well as jacket and monopile offshore wind turbine structures. Being located in remote offshore conditions, these connections can experience considerable adverse loading during their lifetimes. Degradation was reported inside similar connections, which were installed in the last three decades. Grouting in the offshore sites may often be proven difficult, which eventually leads to reduced load-bearing capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs. In this study, scaled grouted connections were manufactured using a novel mould, whose integrity were monitored using digital image correlation (DIC). The connections were loaded under static load to visualize the main failure pattern using distributed fibre optic sensors and acoustic emission (AE) analysis. Grouted connections were then repaired using a cementitious injectable grout. The effectiveness of the grout injection was monitored using dye penetration technique. Finally, specimens are reloaded to identify the potential of such repair for grouted connections.
Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt.