As soon as cement is mixed with water, the hydration reaction starts to set of. The progression of the hydration process is governed by the amount and the availability of water and its possibility to access the unhydrated cement grain surfaces. For a total hydration cement theoretically requires water amounting approximately 0.38 of its own mass. Nevertheless, due to the cement’s highly hygroscopic nature, already the moisture in the ambient air can cause first hydration reactions to set in upon the cement grain surfaces. Such pre-hydration processes have an effect on the cement's properties. Dpending on the specific conditions during the storage the significance of the impact on certain properties can vary.
If cement is consumed soon after production and is transported only short distances in a silo wagon to its final destination for immediate use without further stock transfer, the effects are rather negligible. However, if cement is delivered in bags, transported over long distances, shifted serval times and stored for longer time periods until it is finally consumend, these effects can be quite severe. Due to the actual logistical situation with comparably few cement plants, large delivery distances and partially less developed infrastructures, the latter scenario pictures the situation for the most cases in Africa quite well.
In order to verify the relevance of the pre-hydation for practical application, a series of tests was conducted at the German Federal Institute for Materials Research and Testing (BAM). The influence of the cement storage on gresh and hardened concrete properties was investigated for different concrete and mortar types. The investigations show that the impact of the storage conditions is more pronounced for specialized concretes with high sophisticated optimized mixture compositions containing admixtures. Nevertheless, the effects also occur for ordinary concrete and should not be ignored.
Superplasticizers (SPs) have been employed in concrete technology for decades to improve the workability of concrete in its fresh state. The addition of SPs in cement-based systems affects the early properties. Although the interaction of the cement particles with various SPs has been extensively researched, there still exists limited research on the interaction of SPs with supplementary cementitious materials such as rice husk ash (RHA). This paper investigates the rheological properties and early hydration kinetics of RHA-blended systems with three types of SPs, a polycarboxylate ether (PCE) and two lignosulphonates (LS-acc and LS-ret). In rheological properties, the addition of SP causes an initial improvement of workability as the yield stress is significantly reduced. The pastes with PCE and LS-acc show a slight increase of yield stress over time whereas pastes with LS-ret tend to lower the yield stress slightly over time, further improving the workability. Without SP, pastes with RHA show a lower yield stress but an increase in plastic viscosity as cement is further replaced with RHA. The addition of the LS SPs is observed to lower the plastic viscosity but remains constant with further replacement of cement with RHA. This indicates that LS SPs further adsorbs on RHA particles and hydration products produced causing dispersion of the particles
within the system. In early hydration kinetics, pastes with PCE retard hydration and the degree of retardation is further increased with LS SPs. In the presence of RHA, the retardation of LS SP systems is significantly reduced. The pastes with PCE show more ettringite in the SEM micrographs, but is observed to be shorter needles. This indicates an initial good workability for PCE. However, C-S-H and CH were observed to be low in quantity, whereby the pastes with LS show more nucleation sites for C-S-H and CH. The ettringite needles in the LS systems were similar in quantity and more elongated in some cases but not abundant as in the PCE systems.