Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (64) (entfernen)
Sprache
- Englisch (36)
- Deutsch (22)
- Mehrsprachig (6)
Schlagworte
- Rheology (14)
- Rheologie (6)
- Cement (5)
- Concrete (5)
- Betoninstandsetzung (4)
- Geopolymers (4)
- Instandsetzung (4)
- Self-compacting concrete (4)
- Alkali-activation (3)
- Beton (3)
Organisationseinheit der BAM
Paper des Monats
- ja (2)
A silica residue from waste treatment of chlorosilane production was used together with solid sodium aluminate to test its applicability for the production of one-part geopolymers. The blend was activated with water and cured at 70 °C. The degree of reaction and strength were determined after 1, 3, and 7 days. The reaction products were analyzed by XRD and SEM/EDX. Until the third day of curing the degree of reaction of the residue reached 51 % and the strength was 8.9 MPa. The reaction product was identified as geopolymer containing zeolite A. Thus, the results confirmed that the residue may be used in the production of geopolymers. However, after 3 days of curing no further progress of reaction was observed and the strength slightly decreased, which was attributed to changes in the structure of the geopolymeric gel. It was further observed that even harsh vacuum drying left some water (presumably zeolitic water and surface hydroxyl groups) in the geopolymer.
Trotz der zahlreichen Möglichkeiten zur Beeinflussung der Mörteleigenschaften durch Mischungsmodifikationen ist es nahezu unmöglich, einzelne Eigenschaften unabhängig von anderen zu verändern. Bei einer Mischungsoptimierung muss im Einzelfall immer entschieden werden, welcher der gewünschten Eigenschaften die höchste Priorität zukommt. Anhand von Parameterstudien wird im vorliegenden Artikel verdeutlicht, wie es für bestimmte Anwendungen sinnvoll sein kann, die Verschlechterung einzelner Eigenschaften zu akzeptieren, wenn dadurch eine für den speziellen Einsatzfall essenzielle Eigenschaft verbessert werden kann. Die komplexen Wechselwirkungen der einzelnen Bestandteile fuhren dazu, dass auch scheinbar widersprüchliche Kombinationen von Zusatzmitteln im Einzelfall erforderlich werden können. Zur Anpassung der meisten Mörteleigenschaften gibt es verschiedene Möglichkeiten der Zielerreichung mit jeweils unterschiedlichen Nebeneffekten. Frisch- und Festmörteleigenschaften sind dabei gleichermaßen zu beachten.
Derzeit erfolgt in mehreren Arbeitsgruppen unter Einbindung interessierter Kreise die Überarbeitung der 2001 erschienenen Richtlinie 'Schutz und Instandsetzung von Betonbauteilen' (Instandsetzungsrichtlinie) des Deutschen Ausschusses für Stahlbeton e.V. (DAfStb). Hierüber wird in dem nachfolgenden Beitrag berichtet, um der Fachwelt frühzeitig darzustellen, in welche Richtung die Fortschreibung des Regelwerkes geplant ist.
Die geplante neue Richtlinie wird nach derzeitigem Beratungsstand eine deutliche inhaltliche Erweiterung erfahren. Daher wird sie in 'Richtlinie für die Instandhaltung von Betonbauteilen' (Instandhaltungsrichtlinie) umbenannt und wird Festlegungen zu der grundsätzlichen Vorgehensweise bei der Instandhaltung unter Berücksichtigung der Komponenten Wartung, Inspektion, Instandsetzung und Verbesserung in Anlehnung an DIN 31051 enthalten. Da diese umfassenderen Aufgaben deutlich präziser beschrieben werden, konkretisieren sich auch die Anforderungen an die erforderliche Qualifikation des sachkundigen Planers, der zukünftig verstärkt die 'Restnutzungsdauer' bei seiner Planung beachten und in entsprechende Maßnahmen umsetzen muss.
Mit den Ergänzungen und Änderungen wird die Richtlinie an die aktuellen Entwicklungen und Regelungen im Betonbau angepasst. Gleichzeitig gewinnt die Planungsleistung erheblich an Bedeutung. Für Instandsetzungsprodukte gemäß DIN EN 1504 werden, die Beseitigung derzeit noch enthaltener Unklarheiten und technischer Defizite auf europäischer Ebene vorausgesetzt, Verwendbarkeitsmöglichkeiten aufgezeigt. Die Ausführung von Instandhaltungsmaßnahmen wird durch die Einführung von Überwachungsklassen mit zugehörigen Anforderungen an die durchzuführenden Prüfungen spezifiziert und damit konkretisiert.
Errichtet aus Glas und Beton prägen heute unzählige Sakralbauten der 1950er- und 60er-Jahre unsere Stadtbilder. Nicht selten sind in diesen Kirchen erhebliche Schäden an den Betonglasfenstern zu verzeichnen. Diese fachgemäß zu erhalten, erfordert spezielles technisches und denkmalpflegerisches Know-how. An der Entwicklung geeigneter Instandsetzungsstrategien arbeitet derzeit ein interdisziplinäres Projektteam.
Wärmebehandlung und Autoklavierung von UHPC - Neue Perspektiven für die Betonfertigteilindustrie
(2011)
Das Gefüge von UHPC ist durch eine dicht gepackte und fehlstellenarme Matrix gekennzeichnet. Eine zusätzliche Optimierung ist durch eine Wärmebehandlung bzw. hydrothermale Nachbehandlung (Autoklavierung) unter einem Wasserdampfsättigungsdruck möglich. Die Wärmebehandlung von Beton ist ein in der Betonfertigteilindustrie geläufiges Verfahren, um die Erstarrungszeit zu verkürzen und höhere Frühfestigkeiten zu erreichen.
Although being a very promising area of concrete technology, computational modeling of fresh concrete flow is a comprehensive and time consuming task. The complexity and required computation time are additionally increased when simulating casting of heavily reinforced sections, where each single reinforcement bar has to be modeled. In order to improve the computation speed and to get closer to a practical tool for simulation of casting processes, an innovative approach to model reinforced sections is proposed here. The basic idea of this approach is to treat the reinforcement zone as a porous medium in which a concrete is propagating. In the present paper, the numerical implementation of this concept is described. A methodology allowing for the computation of the equivalent permeability of the steel bars network is suggested. Finally, this numerical technique efficiency is evaluated by a comparison with experimental results of model fluids casting in model formworks.
Reaction products and strength development of wastepaper sludge ash and the influence of alkalis
(2014)
Wastepaper sludge ash (WSA) from a newsprint paper mill was investigated for its mineralogical composition and its reaction products and strength development after activation with water and sodium and potassium hydroxide solutions. The results showed the WSA to consist of calcite, free lime, gehlenite, tricalcium aluminate, belite, talc, quartz and probably a glassy phase. The principle reaction product was monocarboaluminate (CO3–AFm) for the water- as well as for the alkali-activated WSA. Formation of monocarboaluminate and strength gain was more rapid for the alkali-activated WSA until 1 day of curing. However, afterwards reactions proceeded much slower when alkali solutions were used, leading to an about twice as high compressive strength for water-activated WSA mortars after 28 days of curing. The observed behavior is tentatively ascribed to a less uniform microstructure of the alkali-activated WSA. Significant differences between NaOH- and the KOH-activated WSA were not observed.
Üblicherweise werden Werkzeuge für den industriellen Einsatz aus hochlegierten Chromstählen hergestellt. Für den Einsatz in explosionsgefährdeten Bereichen werden oft Werkzeuge aus speziellen Nichteisen-Metalllegierungen (NE-Metall) verwendet. Für diese sogenannten funkenarmen Werkstoffe und deren mögliche Schlagpartner gibt es bisher keine umfassenden Untersuchungen mit Aussagen zur Zündwahrscheinlichkeit.
Die TRGS 723, Abschn. 5.15, fordert den Nachweis der Funkenfreiheit der verwendeten Werkstoffpaarung. Jedoch sind Werkzeuge keine Geräte oder Schutzsysteme im Sinne der Richtlinie 2014/34/EU. Deshalb ist es nicht möglich, Werkzeuge in Übereinstimmung mit dieser Richtlinie zu zertifizieren. Der Nachweis der Erfüllung dieser Anforderungen ist durch Zertifizierungen im sogenannten "gesetzlich nicht geregelten" Bereich möglich. Die BAM bietet diese Zertifizierung für "Funkenarme Werkzeuge" im Rahmen ihres Zertifizierungsprogrammes an.
Die bisherigen Ergebnisse der hier vorgestellten Untersuchung haben gezeigt, dass es keine funkenfreien, metallischen Werkzeuge (non-sparking Tools) gibt. Entscheidend ist im Hinblick auf die TRGS 723, ob zündfähige Funken entstehen oder nicht. Es ist immer die Frage, worauf die Werkzeuge im praktischen Anwendungsfall schlagen oder fallen gelassen werden können, d.h. aus welchem Material der mögliche Schlagpartner besteht. Dies können metallische Schlagpartner, aber auch Betonoberflächen sein. Unterschiedliche Kombinationen von Werkstoffen ergeben bei Schlagbeanspruchung im explosionsgefährdeten Bereich jeweils unterschiedliche Zündwahrscheinlichkeiten. Aber auch die Höhe der beim Einsatz der Werkzeuge möglichen kinetischen Schlagenergie und der Brenngas/Luft-Atmosphäre im betreffenden explosionsgefährdeten Bereich sind wichtige Einflussgrößen.
The thermal gravimetric analysis (TG) is a common method for the examination of the carbonation progress of cement-based materials. Unfortunately, the thermal properties of some components complicate the evaluation of TG results. Various hydrate phases, like ettringite (AFt), C-S-H and AFm decompose almost simultaneously in the temperature range up to 200 °C. Additionally, physical bound water is released in the same temperature range. In the temperature range between 450 °C and 600 °C the decomposition of calcium hydroxide and amorphous or weakly bound carbonates takes place simultaneously. Carbonates, like calcite, from limestone powder or other additives may be already contained in the noncarbonated sample material. For this research an attempt was made to minimise the influence of these effects. Therefore, differential curves from DTG-results of non-carbonated areas and areas with various states of carbonation of the same sample material were calculated and evaluated. Concretes based on three different types of cement were produced and stored under accelerated carbonation conditions (1 % CO2 in air). The required sample material was obtained by cutting slices from various depth of previously CO2-treated specimen and subsequent grinding. During the sample preparation, a special attention was paid that no additional carbonation processes took place. As reference method for the determination of the carbonation depth the sprayed application of phenolphthalein solution was carried out. Microscopic analysis where examined to confirm the assumptions made previously. Furthermore, the observed effect of encapsulation of calcium hydroxide by carbonates caused by the accelerated carbonation conditions was examined more closely.
One-part geopolymers offer advantages over conventional geopolymers with regard to handling and storage of feedstocks. However, they often suffer from a low degree of reaction, a high amount of crystalline byproducts, and consequently low strength. In this study, one-part geopolymers were produced from rice husk ash (RHA) and sodium aluminate, and investigated by XRD, ATR-FTIR, SEM and compressive strength testing. The compressive strength of the material was 30 MPa, i.e. significantly higher than for comparable one-part geopolymers. This is attributed to an almost complete reaction of the RHA and the absence of crystalline byproducts (zeolites) in the hardened geopolymer.
Mit Veröffentlichung der europäischen Normenreihe EN 1504 in den Jahren 2004 bis 2008 mussten in Deutschland die bisherigen nationalen Regelungen für die Instandsetzung von standsicherheitsrelevanten Betonbauteilen angepasst werden. Im vorliegenden Entwurf der neuen Instandhaltungs-Richtlinie wurden die Hinweise zur Planung und Durchführung von Instandsetzungsmaßnahmen aus der Instandsetzungsrichtlinie des DAfStb von 2001 entsprechend überarbeitet und aufgrund neuer Erkenntnisse ergänzt. Außerdem wurde das Regelwerk um Gesichtspunkte der Instandhaltung erweitert, sodass die Aspekte Wartung, Inspektion und Verbesserung nun in Anlehnung an DIN 31051 berücksichtigt werden. Zudem wurden Regelungen aus der ZTV-ING sowie der ZTV-W übernommen. Im ersten Teil dieses Artikels geben wir einen Überblick über die Gliederung und wesentliche neue Inhalte wie die Ausweitung der Instandsetzungsprinzipien.
In einer Artikelserie stellen wir die neue Instandhaltungs-Richtlinie des Deutschen Ausschusses für Stahlbeton (DAfStb) vor. Im zweiten Teil geht es um Betonersatz- und Oberflächenschutzsysteme sowie Rissfüllstoffe. Es werden als Folge des EuGH-Urteils vom Oktober 2014 zukünftig keine Anforderungen an Bauprodukte mit dem Nachweis über allgemeine bauaufsichtliche Prüfzeugnisse gestellt. Stattdessen werden auf Basis der Anforderungen individueller Bauwerke notwendige Merkmale von Bauprodukten für die Instandsetzung definiert. Außerdem wird Teil 3 der neuen Instandhaltungs-Richtlinie "Ausführung der Instandsetzung und Überwachung" vorgestellt. Neu ist hier die Einführung von Überwachungsklassen, die sich aus der Art des instand zu setzenden Betonbauteils (standsicherheitsrelevant oder nicht) und der auszuführenden Arbeiten ergeben, zum Beispiel Instandsetzung oder Verstärkung. Am Ende dieses Artikels wird kurz der 4. Teil der neuen Instandhaltungs-Richtlinie erläutert.
Industrial wastes (bottom ash, crushed concrete fines, filter residue, paper ash and lignite fly ash) have potential for use in building materials, for instance as raw materials for clinker production, as supplementary cementitious materials (SCMs) or mineral additions in concrete. The properties of the products are dependent on the reactivity of the waste materials used, which can be classified as inert, latent hydraulic or pozzolanic. In this study, waste materials were first characterised. This was followed by theoretical considerations of the mentioned application options. Experiments were limited to evaluation of potential as SCMs and, for this purpose, activity index measurements and calorimetric and thermogravimetric analyses were performed. Finally, the synergetic effects of various waste materials were considered. Paper ash (calcium oxide source) and filter residue (amorphous silicon dioxide source) showed the best prospects for use as cementitious material components.
Hochfeste und ultrahochfeste Stahlfaserbetone eignen sich aufgrund ihrer Eigenschaften für den Einsatz bei extremen mechanischen Beanspruchungen. Das für diesen Einsatz erforderliche duktile Bruchverhalten unter Zugbeanspruchung wird ausschließlich durch die Zugabe von geeigneten Stahlfasern und deren Wirkung in der Zementsteinmatrix erreicht. Für eine gezielte stoffliche Optimierung des Systems sind fundierte Kenntnisse zur Wirkungsweise der Stahlfasern notwendig, die bei bisherigen Untersuchungen lediglich auf Basis von klassischen Messverfahren zerstörender Prüfungen gewonnen wurden. Durch das Einbeziehen von Methoden der zerstörungsfreien Materialcharakterisierung können das Bruchverhalten hochfester und ultrahochfester Stahlfaserbetone orts- und zeitaufgelöst untersucht und die einzelnen Phasen des Schädigungsprozesses identifiziert werden. Anhand der vorliegenden Ergebnisse von Zugversuchen eines ultrahochfesten Stahlfaserbetons wird der kombinierte Einsatz von Methoden der zerstörungsfreien Materialprüfung gezeigt und deren Anwendbarkeit in der Analyse des Bruchverhaltens diskutiert. Das Hauptaugenmerk liegt dabei auf der Charakterisierung der ausschlaggebenden Versagensmodi unter Zugbelastung durch die einzelnen Verfahren und dem Vergleich zu klassischen Messmethoden (z. B. Extensometer). Die Zugversuche wurden dazu parallel durch optische Verformungsanalyse mittels Bildkorrelation (DIC), Schallemissionsanalyse (SEA) und 3-D-Computertomografie (CT) begleitet.
Die Herausforderung einer anspruchsvollen Natursteininstandsetzung liegt in der richtigen Zusammensatzung der Steinersatzmassen. Dabei müssen vielerlei, teilweise gegenläufige Interessen miteinander vereinbart werden: Mechanische und bauphysikalische Belange müssen genauso beachtet werden wie denkmalpflegerische und gestalterische Aspekte. Auf die konkreten Anforderungen und Voraussetzungen einer Restaurierungsaufgabe reagieren zu können, ist die Grundvoraussetzung für ein gutes Gelingen. Hilfreich sind hier Mischungen, die modular aufgebaut sind und sich individuell und flexibel an die Erfordernisse anpassen lassen.
This contribution presents the results of structural and compressive strength investigations on cured andhigh-temperature treated silica-based one-part geopolymer-zeolite composites. The specimens weresynthesized from two different silica sources, sodium aluminate and water. The phase content as well asthe compressive strength of the cured composites varied depending on the starting mix-design and thesilica feedstock. Besides geopolymeric gel, A-type zeolites and hydrosodalites were the major reactionproducts. One of the silica feedstocks yielded significantly higher compressive strength (19 MPa), whilethe other one appears to cause less variation in phase content. Strength testing indicated an improvementon heating up to
200–400 °C (28 MPa) followed by a moderate decrease up to 700 °C. Above 700 °C the sys-tems underwent new phase formation and shrinkage (volume decrease) deformations. After exposureat 1000 °C the different mixes consisted of a mix of several stuffed silica phases, almost pure hexago-nal nepheline or amorphous phase. Depending on the mix-design, the onset temperature of the hightemperature phase transformations varied.
One-part alkali-activated (geopolymer) mortars based on three different silica-rich starting materials and sodium aluminate, with and without ground granulated blast furnace slag (GGBFS) addition, were tested regarding sulfuric acid resistance according to DIN 19573:2016-03 (70 days at pH = 1). Corresponding pastes were characterized by XRD, SEM, chemical analysis, 29Si MAS NMR and 1H-29Si CPMAS NMR after water storage and after acid exposure. The mortars exhibited a high resistance against sulfuric acid attack, with the best ones conforming to the requirements of DIN 19573:2016-03. The analytical results showed that this was due to precipitation of silica gel at the acid-mortar interface, which formed a mechanically stable layer that protected the subjacent mortar and thus inhibited further degradation. The addition of GGBFS decreased the acid resistance via formation of expansive calcium sulfate phases.
While calcined clays in general have been credited with a great potential to mitigate CO2 emissions related to cement production and consumption, calcined brick clays are currently understudied in this regard. In the present work, two brick clays, a low-grade kaolinitic clay, and a mixed clay composed of 50% brick clay and 50% low-grade kaolinitic clay were studied regarding transformations on calcination, and strength and durability performance as well as pore structure of mortars made with the blended cements. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the low-grade kaolinitic clay. However, the mixed clay performed very similar to the low-grade kaolinitic clay, which points to a viable option for optimal use of brick clays in cementitious systems. The carbonation resistance of the blended cement mortars was generally worse than that of the plain Portland cement mortar, as expected, but the former exhibited a significantly improved chloride penetration resistance. The latter improvement was due to pore structure refinement in the blended cement mortars, compared to the Portland cement mortar.
European and Germany regulations demand an elaborate waste management to save natural resources, reduce waste volumes deposited at landfills and enhance sustainable development by recycling of various residues. Research into the use of these materials in the construction sector and other fields is a positive step forward in achieving these objectives. BAM shares its latest findings.
Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles.
The most common method for determination of the carbonation depth is the sprayed application of indicator solutions, Phenolphthalein in particular. Since the aerosols of Phenolphthalein are suspected to be carcinogenic, efforts have been intensified to use alternative indicators for the determination of carbonation depth. The subject and aim of this research paper are to examine indicator solutions from Alizarin Yellow R, Thymol Blue and a Mixed Indicator. These indicator solutions are commercially available and are not suspected to be carcinogenic.
For the purpose of this research, samples previously stored under accelerated carbonation conditions (1% CO2) were examined by thermogravimetric analysis (TGA) and examination of the pH value. Additionally, the electrolytic back-titration for determination of total CO2 amount was carried out comparatively to TGA.
The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose.
Grouted connections are intensively used in offshore rigs, platforms as well as jacket and monopile offshore wind turbine structures. Being located in remote offshore conditions, these connections can experience considerable adverse loading during their lifetimes. Degradation was reported inside similar connections, which were installed in the last three decades. Grouting in the offshore sites may often be proven difficult, which eventually leads to reduced load-bearing capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs. In this study, scaled grouted connections were manufactured using a novel mould, whose integrity were monitored using digital image correlation (DIC). The connections were loaded under static load to visualize the main failure pattern using distributed fibre optic sensors and acoustic emission (AE) analysis. Grouted connections were then repaired using a cementitious injectable grout. The effectiveness of the grout injection was monitored using dye penetration technique. Finally, specimens are reloaded to identify the potential of such repair for grouted connections.
Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock
(2021)
Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions.
Die Bestimmung der Rauheit von Bauteiloberflächen stellt eine wichtige Messaufgabe im Bauwesen dar. Vor allem bei der Betoninstandsetzung, im Straßenbau und bei der Herstellung von Stahlbeton-Halbfertigteilen ist die Rauheit – gemessen als Rautiefe – eine wichtige Kenngröße. Zurzeit werden Messungen der Rautiefe mittels volumetrischer Verfahren (Sandflächenverfahren) durchgeführt. Diese bereits seit mehreren Jahrzehnten angewandten Verfahren sind jedoch auf horizontale bzw. wenig geneigte und trockene Oberflächen beschränkt. Darüber hinaus hängen die erzielten Ergebnisse sehr stark von der angewandten Prüfvorschrift, den darin vorgeschriebenen Prüfmitteln und Geräten und dem jeweiligen Anwender ab.
Als Alternative zu den volumetrischen Verfahren wurde an der Bundesanstalt für Materialforschung und -prüfung (BAM) ein automatisiertes, laserbasiertes Messverfahren entwickelt, mit dem Rautiefen von Bauteiloberflächen in Anlehnung an bereits standardisierte Verfahren bestimmt werden können. Der vorliegende Beitrag befasst sich zunächst mit den konventionellen Prüfverfahren, beschreibt die wichtigsten Zusammenhänge und zeigt die Grenzen dieser Methoden auf. Im zweiten Teil wird das an der BAM entwickeltes Messsystem, als zielführendes Alternativverfahren für die konventionellen Methoden, vorgestellt und dessen Leistungsfähigkeit näher beschrieben.
The present work addresses powder bed binder jetting additive manufacturing by selective magnesium phosphate cement activation. Despite the potential of this technology to aid the digitalization of the construction industry, the effect of processing parameters on the mechanical performance of printed materials has not yet been studied to generate a guideline for the further development of the technology. Statistical methodologies were used to screen the effect of four printing process parameters (printing speed, layer thickness, raster angle, and build direction on flexural and compressive strength). As the exploited technology works with constant fluid pressure, the physical interpretation of the effect of each factor can be considered taking into account the interactions between the binder materials in the powder bed. Analysis of variance (ANOVA) indicated that printing speed and layer thickness significantly affect mechanical performances. Furthermore, the layout of samples for the printing process is preferable to be parallel the printhead movement. An anisotropic behavior was observed, and the samples subjected to compressive forces parallel to the layer plane possessed lower strength values. This effect can be interpreted as a result of a weak area of low density in between layers, leading to a pronounced delamination under compression. Even though the strength of the printed material is not suitable for a structural concrete, it can be marginally improved by design of experiment and optimized for non-structural applications, such as for porous artificial stone. Design of experiment coupled with ANOVA methods can be used in the future to support the development of novel material mixtures, thus expanding the fields of application of this novel additive manufacturing technology.
Selbstverdichtender Beton verhält sich unter Temperatureinfluss anders als Normalbeton, da die Rheologie neben der fortschreitenden Hydratation zusätzlich durch die von der Zeit und dem Hydratationsfortschritt abhängige Adsorption von Fließmitteln beeinflusst wird. Anhand rheometrischer Betonversuche an SVB unterschiedlicher Entwurfskonzepte mit variierter anionischer Ladungsdichte im Fließmittel wird verdeutlicht, dass mehlkornreiche SVB bei niedrigen Temperaturen sehr robust sind, während bei hohen Temperaturen mehlkornärmere Entwürfe zu bevorzugen sind. Darüber hinaus wird gezeigt, wie sich unterschiedliche Fließmittelmodifikationen in bestimmten Temperaturbereichen verhalten. Anhand des Wasser-Feststoff-Verhältnisses und des Adsorptionsverhaltens von Fließmitteln werden die maßgeblichen Prozesse erläutert und Möglichkeiten für die Entwicklung robuster Mischungen für individuelle Temperaturbereiche aufgeführt.--------------------------------------------------------------------------------------------------------------------------------------------------------------
Regarding the temperature dependent performance, self-compacting concrete (SCC) distinguishes from normal concrete, since its rheology does not only depend upon the hydration itself but supplementary upon the adsorption of superplasticizers, which is affected by the time and the hydration progress. Based on rheometric concrete investigations with different SCC mixture compositions and varied anionic charge densities of the superplasticizers, it is shown that SCC, which is rich in powder components, shows robust performance at low temperatures, while compositions with lower powder contents are favourable at high temperatures. Furthermore, the performance of different superplasticizer modifications at different temperature ranges is demonstrated. The relevant processes are explained by means of the water to powder ratio as well as the adsorption behaviour of superplasticizers, and options for the development of robust mixture compositions for individual temperature ranges are itemised.
Self-compacting concrete (SCC) differs substantially from normal concrete as regards the quantity of superplasticiser dosage. The functionality of superplasticisers, based on the polycarboxylate ether (PCE) superplasticiser customary with SCC, is nowadays very well understood at construction material research level. However, knowledge concerning pertinent correlations does not always permeate practice to an equal extent. PCEs are extremely polymorphic as opposed to earlier superplasticiser groups, which still possess a considerable proportion of the superplasticiser market. The geometry of polymers can be adjusted individually to performance characteristics required for certain uses. Yet, in selecting a superplasticiser for its specified rheological properties, a very strong influence can equally be exerted simultaneously on the subsequent hydration process. The charge density of the PCE employed also plays a key role in connection with both rheology and early hydration.
Grouts have numerous applications in construction industry such as joint sealing, structural repair, and connections in precast elements. They are particularly favoured in rehabilitation of structures due to penetrability and convenience of application. Grouts for repair applications typically require high-performance properties such as rapid strength development and superior shrinkage characteristics. Sometimes industrial by-products referred as supplementary cementitious materials (SCM) are used with neat cement due to their capabilities to provide binding properties at delayed stage. Micro silica, fly ash and metakaolin are such SCMs, those can modify and improve properties of cement products. This study aims at investigating long-term mass loss and linear shrinkage along with long-term compressive and flexural strength for grouts produced from ultrafine cement and SCMs. A series of mixtures were formulated to observe the effect of SCMs on these grout properties. Properties were determined after 365 days of curing at 23oC and 55% relative humidity. The effect of SCMs on the properties are characterised by statistical models. Response surfaces were constructed to quantify these properties in relation to SCMs replacement. The results suggested that shrinkage was reduced by metakaolin, while micro silica and fly ash had positive effects on compressive and flexural strength, respectively.
While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio‐based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil‐based.
The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfet ta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly.
Polysaccharides are incorporated into cement based Systems in order to modify the rheological properties. Typically, cellulose ethers, sphingan gums, guar gum or starch ethers are applied. Depending upon their chemistry, molecular architecture, and adsorption tendency, polysaccharides interact differently with the entire cementitious system. Some stabilising agents like diutan gum mainly affect the cementitious paste; other stabilising agents like starch tend to interact with the sand fraction and even with the coarse aggregates. Cellulose and guar gum shows more diverse performances.
Typically stabilising admixtures like polysaccharides are used, when sophisticated rheological properties are adjusted. Therefore, polysaccharides are often used in combination with superplasticisers, which are added to reduce the yield stress of concrete. This can cause interactions, particularly when the stabilising Agent shows a strong tendency to adsorb on particle surfaces. Adsorptive stabilising agents may reduce the amount of adsorbed superplasticisers, thus affecting both viscosity and yield stress, while non-adsorptive stabilising agents mainly affect the plastic viscosity independently of the superplasticiser. Due to the strong influence of superplasticisers on the yield stress, influences of the stabilising agent on the yield stress retreat into the background, so that their major effect is an increase of the plastic viscosity.
The paper provides a comprehensive overview of how different polysaccharide superplasticisers affect cementitious flowable systems and points out the challenges of the combined use of polysaccharides and superplasticisers. Based on rheometric experiments and observations of the hydration process, time dependent effects on the workability as well as of the hydration of cement are presented and discussed.
In this work, engineered recycled mineral admixtures were obtained from four different industrial residues: basic oxygen furnace slag, iron ore tailings, quartz mining tailings and quartzite mining tailings.
The grinding performance was evaluated in two different programs and the characterization included chemical and mineralogical composition, particle morphology, and physical properties. Performance evaluations were carried out in blended pastes and mortars, including flow properties, hydration kinetics, soundness, pozzolanic activity, and compressive strength. Coarser-than-cement admixtures allowed better flow performance, greater dimensional stability and more economical production, while finer-thancementn admixtures improved mechanical performance by both filler effect and cementing activity.
Nachdem vor ca. 20 Jahren in Japan die Entwicklung der selbstverdichtenden Betone begann, dauerte es weitere 10 Jahre, bis diese Entwicklung auch Europa erreichte. Obwohl im Fertigteilsektor bereits deutlich mehr SVB zum Einsatz kommt als im Transportbetonbereich, bleiben die Produktionsmengen hinter dem zurück, was die Potenziale und Chancen dieser Technologie eigentlich erwarten ließen. Eine Ursache für die geringe Marktverbreitung sind die stark schwankenden und teilweise nur schwer beherrschbaren Frischbetoneigenschaften dieser Betone.
Im Hinblick auf die Konformitätsbewertung der Druckfestigkeit von Beton wird es in der für 2014 geplanten Fassung der EN 206 signifikante Änderungen geben. Neben den bisher bekannten Verfahren werden auch sogenannte Kontrollkartensysteme als Konformitätsnachweis zugelassen. Dabei können beliebige Kontrollkartensysteme verwendet werden, sofern nachgewiesen werden kann, dass der maximale Durchschlupf (Average Outgoing Quality Limit, AOQL) 5 % beträgt. Im informativen Normenanhang werden zwei grundlegende Verfahren, das sogenannte Shewhart-Verfahren sowie das CUSUM-Verfahren (Cumulative Sum) beschrieben, welche beide die Forderung an das AOQL erfüllen.
Kontrollkartensysteme sind eigentlich Werkzeuge zur Prozesssteuerung. Sie können effektiv dabei helfen, die Produktion technisch, ökonomisch und ökologisch zu optimieren. Allerdings sind Kontrollkarten deutlich komplexer in der Anwendung als die bisher normativ erfassten Methoden. Der vorliegende Beitrag stellt die neuen Verfahren und deren Besonderheiten anhand von Beispielen vor. Darüber hinaus werden der Zusatznutzen bei sachgerechter Anwendung im Vergleich und Vor- und Nachteile zu den bisherigen Verfahren dargestellt und diskutiert.--------------------------------------------------------------------------------------
With regard to the conformity assessment of the compressive strength of concrete, there will be significant changes in the EN 206, which is scheduled for publication in 2014. So called control chart systems will be approved supplementary to the existing methods. Any control chart can be used as long as the system can grant an average outgoing quality limit (AOQL) of 5 %. The informative appendix of the standard presents two fundamental control chart methods, the so called Shewhart method and the CUSUM method (cumulative sum), both of which fulfill the required AOQL.
Control card systems are actually tools for process control. They can effectively help to optimise production processes technically, economically, and ecologically. However, control charts are much more complex to use than the methods known from the recently applied standard. This paper presents these new methods and their characteristics using examples. Furthermore, the additional benefit of these systems is illustrated and advantages and disadvantages are discussed in comparison to existing methods.
Numerical simulations of concrete castings are complex and time consuming. In order to decrease simulation time and to simplify simulation procedure, an innovative modelling approach, which treats reinforced sections in a formwork as porous media, was proposed. In the previous studies, this numerical model was proved suitable to simulate casting of model yield-stress fluids through reinforced elements. This article focuses on the experimental validation of the proposed model at the concrete scale. For this purpose, a large-scale laboratory casting of a highly reinforced beam is performed. The casting process is numerically simulated and the numerical results are compared to the experimental measurements.
In Produktionspausen können in Betonwerken nennenswerte Lagerungsintervalle entstehen. Auf Baustellen und in den Instandsetzungen werden Zement- und Trockenmörtelsäcke teilweise über längere Zeiträume gelagert. Auch im Zusammenhang mit Zementimporten und zunehmend filigran abgestimmten Betonrezepturen die bereits bei kleinen Änderungen der Ausgangsstoffe sensibel reagieren, nimmt die Relevanz der Zementlagerung zu. Aus diesem Grund wurde der Einfluss der Zementlagerung auf die Eigenschaften von Betonen in einer Versuchsreihe an der Bundesanstalt für Materialforschung und -prüfung (BAM) ermittelt.
Repair is an indispensable part of the maintenance of structures over their lifetimes. Structural grouting is a widely used remediation technique for concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. A structural grout system should be injectable in narrow spaces and hence include ingredients with finer particles. Ultrafine cements are ideal for these type of demanding grouts due to their superior properties compared to that of the less expensive, but coarser ordinary Portland cement (OPC). Supplementary cementitious materials (SCMs) are often used to replace OPC clinker based binder in order to modify certain properties and to reduce costs. The most commonly used SCMs are fly ash (FA), and ground granulated blast furnace slag (GGBS). For various special applications microsilica (MS), and metakaolin (MK) are also used. Identifying the optimum replacement contents of OPC by SCMs are a challenge during the design of such grouts. The aim of this experimental study is to investigate the effect of the selected SCMs (FA, MS and MK) on the slump flow, time of efflux, viscosity, shrinkage, and compressive and flexural strength of ultrafine cement based grouts with constant water-binder ratio and superplasticizer content. The test program was formulated using Box-Behnken design principles. Maximum percentages of replacement with ultrafine cement was 6% by volume of cement for MS and 16% for FA, and MK. The results suggest that most investigated grouts have the potential to be used for structural applications. The appropriate quadratic models are then formulated through statistical tools and presented as response surfaces. The trends indicate that fly ash improves the rheological properties, whereas microsilica and metakaolin positively affect shrinkage and mechanical properties to some extent. Based on the influence of SCMs and priorities among the properties, Decision Matrix Analysis (DMA) is carried out to select the most suitable ones among the SCMs. The analysis suggests that microsilica and fly ash are more suitable as SCMs than metakaolin without affecting the properties.
Rising temperatures worldwide pose an increasing challenge for safe and healthy living conditions. Particularly inner cities have been affected by these environmental changes because of the materials used to build houses, streets and infrastructure. The most common building material is concrete. It shows a specific heat capacity, while the heat conductivity for Standard concrete is low. Thus, the use of concrete generates a high capacity of heat storage. In addition, extensive soil sealing also contributes to the temperature rise of inner city areas compared to
their surroundings. To mitigate this so-called urban heat island effect, a self-cooling concrete paver was developed. This paver is able to store water. The evaporation of the water at elevated temperatures provides a cooling effect. This paper focuses on determination of this new paver’s capability to cool the surface and the surrounding. The new paver’s cooling Qualities were analysed in a series of laboratory tests. To prove the results outside of laboratory conditions, two fields (12 m × 8 m) with self-cooling and reference pavers were installed in Spain.
This paper presents and discusses the results of the tests. Correlation between reduced surface temperature of the self-cooling concrete pavers and the air temperature is examined.
Im Rahmen des europäischen Forschungsprojekts Microcon wurden wirtschaftliche und ökologische Ansätze zur Verwendung von Feinstfüllstoffen so genannten Microfillern in Bauprodukten, die auf zementgebundenen Systemen basieren, untersucht. Hauptzielsetzung war die Entwicklung von modifizierten Bindemitteln und Zusätzen für die Transportbeton- und Fertigteilindustrie bis hin zur Marktreife. Eine der Neuentwicklungen war eine leicht handhabbare Werktrockenmischung für selbstverdichtenden Beton (SVB), die alle Schlüsselkomponenten bis auf das Bindemittel und die grobe Gesteinskörnung enthält und eine hohe Robustheit in der Anwendung gewährleistet.
Stabilising admixtures are commonly used additives in repair mortars and grouts. Beyond this, such type of admixture is increasingly used in concrete and other cementitious materials. In particular when fresh mortar or concrete properties have to be adjusted reliably, stabilising agents can be beneficially used to improve workability and robustness of the mixture. The mode of operation of these admixtures varies, rather affecting either the liquid phase or the solid particles in the dispersion, both causing strong interactions with the mortar or concrete system, and significant changes in their rheological behaviour. Furthermore, these are strongly affected by the environmental temperature during the casting process. In the paper the effect of temperature on the performance of stabilising agents in cementitious systems is presented and how performance changes affect fresh and hardening mortar or concrete properties. Particular attention is placed on interactions between stabilising agents and superplasticizers. Results are discussed with special focus on self-compacting concrete.