Filtern
Erscheinungsjahr
Dokumenttyp
Schlagworte
Eine neue Generation von alterungsbeständigen Plasmapolymeren mit definierter chemischer Struktur
(2000)
Several possibilities exist to produce a modified polymer surface with a high density of only one sort of functional group such as: (i) the plasma grafting of unfragmented monomer molecules and their polymerization forms OH, NH2, COOH groups, etc. in concentrations of approximately 25 groups per 100 C atoms; (ii) selective plasma bromination provides 1025 CBr groups; (iii) the plasma oxidation of polymer surfaces in an O2 plasma followed by the chemical reduction of all O-containing groups to OH groups by diborane, vitride (Na complex) or LiAlH4 yields 914 OH groups per 100 carbon atoms; and (iv) the grafting of spacers with different endgroups onto OH or CBr groups produces 710 spacer molecules/100 C. This work was focused on the formation of thin plasma deposited polymer layers with a maximum of (homo)functional groups and with a minimum of chemical irregularities using the pulsed plasma technique. The monomers were allylalcohol, allylamine, acrylonitrile and acrylic acid. The further intent was to study the interactions of functional groups (OH, COOH, NH2) and deposited metals (Cr, Al, Ti). It was expected that more basic (NH2), weakly basic or neutral (OH) or more acidic (COOH) groups would show different interactions and chemical reactions with metal atoms.
The X-ray-induced sample damage during mono XPS analysis of an oxygen-plasma-oxidized and subsequently wet-chemically reduced poly(propylene) film was investigated as a showcase for plasma-modified or plasma-deposited samples. By doing this, the degradation index approach as introduced by Beamson and Briggs in the Scienta ESCA300 high-resolution XPS database of organic polymers has been adopted. As to be expected, the sample degrades by loosing oxygen as revealed by observation of decreasing O/C and COR/Csum ratios. However, the X-ray degradation indices are definitely higher than those of conventional reference polymers. Moreover, the COR/Csum degradation index is significantly higher in comparison with one obtained for the O/C ratio. In that context, there is no difference between the plasma sample and a conventional poly(vinyl alcohol) polymer. It is concluded that for reliable quantitative surface chemical analysis, the quality of spectra in terms of acquisition times must be optimized aimed to a minimization of X-ray degradation. Finally, it is proposed to describe the photon flux of an X-ray gun in an XPS experiment, which defines the degradation rate at the end, by using the sample current simply measured with a carefully grounded sputter-cleaned reference silver sample.
The chemical and morphological stabilities of polymer segments in the near-surface layer were investigated by spectroscopic methods such as X-ray photoelectron spectroscopy and near-edge X-ray absorption fine structure spectroscopy. Model studies were undertaken with LangmuirBlodgett films, self-assembled monolayers and oligomer films. For thin polymer layers (30 to 500 nm), the changes in molecular-weight distributions of some polymers were investigated systematically by size exclusion chromatography, matrix-assisted laser desorption/ionizationtime-of-flight mass spectrometry and thermal-field flow fractionation for oxygen- and helium-plasma exposures. The polymer surfaces were found to be relatively stable at exposure to an oxygen low-pressure plasma up to ca. 2 s. This is important information to get maximum adhesion to metals in composites. In correlation to their redox potentials, potassium, aluminium and chromium react with oxygen functional groups at the polymer/metal interface. In a dedicated study, chromium was found to attack aromatic rings and form different reaction products.