- Plasma modification (5)
- Functional groups (3)
- Introduction of functional groups (3)
- Peel strength (3)
- Pulsed plasma (3)
- Pulsed plasma polymerization (3)
- Acrylic acid (2)
- Allyl alcohol (2)
- Allylamine (2)
- Aluminium (2)
Polymer surfaces were modified in low-pressure glow discharge plasmas for introduction of monotype functional groups of different type and density. For this purpose three ways are selected, (i) oxygen plasma treatment followed by wet-chemical reduction of O functional groups to OH groups, (ii) plasma bromination for introducing C - Br groups and (iii) coating by deposition of thin plasma (co-) polymerized layers of functional groups-bearing monomers with OH, NH2, COOH, epoxy etc. functionalities. Subsequently, these groups were used as anchoring points for chemical grafting of spacer molecules, oligomers, prepolymers, fluorescent labels, ionic and nucleic acid residues, employing different chemical routes. The yield in monosort functional groups at polymer surfaces ranged from 1014 (process i), 2040 (process ii) and 1831 groups per 100 C atoms (process iii) as measured by XPS after derivatization. The consumption of functional groups amounted to 4090% of all functionalities present at the surface and depended on the dimensions of grafted molecules. For infinitely variably tuning the number of functional groups process iii was performed as copolymerization of a functional group-carrying comonomer with a non-functionalized (chain-extending) comonomer.
Communication: Fire retardant coatings are deposited on polyamide-66 using plasma polymerisation. Chemical composition and thickness of deposits are adjusted varying the plasma treatment based on hexamethydisiloxane mixed with oxygen. The fire retardancy performances are evaluated using a cone calorimeter. The correlation between fire retardancy and thickness as well as chemical composition is discussed.
Polymer surfaces can be finished with functional groups upon exposure to a plasma. Species of the plasma gas are attached at surface carbon atoms, forming functional groups of different composition. To produce a modified polymer surface with a high density and homogeneity of hydroxyl groups only, the oxygen-plasma-formed oxygen functional groups were chemically reduced by diborane and LiAlH4 with yields of 10 to 11 OH groups per 100 carbon atoms in the 3 to 5 nm near-surface layer as detected by X-ray photoelectron spectroscopy (XPS). The identification of hydroxyl groups was performed by means of attenuated total reflectanceFourier transform infrared spectroscopy and XPS.
Polymeroberflächenfunktionalisierungen im gepulsten Plasma mit nachfolgender chemischer Behandlung
(2000)
The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further.
In contrast to other plasma modification processes of polymer surfaces, the bromination is very selective and shows a high yield in C—Br groups. The most convenient bromination process was found using bromoform, which was thus preferred to elemental bromine, allyl bromide, vinyl bromide or tert-butylbromide. The bromoform process give yields in C—Br up to 40 C—Br or more, with only 2-3% co-introduction of O-functionalities whereas allyl bromide results in yields of about 20 C—Br and more, but in more than 10% oxygen-containing by-products. C—Br groups serve as anchoring points for grafting of molecules, oligomers and pre-polymers of diole or diamine character.