Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (29) (entfernen)
Schlagworte
- Functional groups (3)
- Plasma modification (2)
- Plasma polymerization (2)
- Pulsed plasma (2)
- Pulsed plasma polymerization (2)
- Acrylic acid (1)
- Adhesion (1)
- Adhesion promoters (1)
- Adhesion-promoting interlayers (1)
- Allyl alcohol (1)
- Allylamine (1)
- Aluminium (1)
- Attenuated total reflectance-Fourier transorm infrared spectroscopy (1)
- Charcterization of homo- and copolymers (1)
- Chemical reduction of functional groups (1)
- Co-polymers (1)
- Cone calorimeter (1)
- Degradation (1)
- Doping with metal atoms (1)
- ESCA/XPS (1)
- Encapsulation of nanoparticles (1)
- Flame retardance (1)
- Fluorination kinetics (1)
- Gas phase fluorination of PE (1)
- Grafting (1)
- Heat release (1)
- Introduction of functional groups (1)
- Long-term stability (1)
- Metal-polymer composites (1)
- Metal-polymer systems (1)
- PET (1)
- Peel strength (1)
- Photoelectron spectroscopy (1)
- Plasma (1)
- Plasma bromination (1)
- Plasma surface treatment (1)
- Plasma treatment (1)
- Plasma-initiated copolymerization (1)
- Poly(ethylene terephthalate) (1)
- Poly(propylene) (PP) (1)
- Poly(tetrafluoroethylene) (1)
- Polyamides (1)
- Polymer surfaces (1)
- Polymer-metal composites (1)
- Polypropylene (1)
- Reactions at Polymer surfaces (1)
- Selective plasma process (1)
- Spacer (1)
- Surface modification (1)
- Surfaces (1)
- Weathering (1)
- X-ray (1)
- X-ray photoelectron spectroscopy (1)
Polymers synthesized with plasma techniques are very interesting materials for electronic, optic, and bio compatible applications. Thin films of plasma polymers shows a good adhesion to metals, glass, or other polymers. But the supramolecular structure, the durability, and the chemical and mechanical behavior of these polymers is poorly understood. Therefore dielectric investigations are carried out to study the dynamic behavior of the plasma polymers. As polymer system allyl alcohol/alkene is chosen to get polymers with a defined concentration of hydroxyl groups. The dielectric investigations shows several relaxation processes and a dependency of the dielectric parameters from the ratio of allyl alcohol in the polymer is observed. This results indicated that the alkene monomers were assembled continuous into the polymer matrix.
The chemical and morphological stabilities of polymer segments in the near-surface layer were investigated by spectroscopic methods such as X-ray photoelectron spectroscopy and near-edge X-ray absorption fine structure spectroscopy. Model studies were undertaken with LangmuirBlodgett films, self-assembled monolayers and oligomer films. For thin polymer layers (30 to 500 nm), the changes in molecular-weight distributions of some polymers were investigated systematically by size exclusion chromatography, matrix-assisted laser desorption/ionizationtime-of-flight mass spectrometry and thermal-field flow fractionation for oxygen- and helium-plasma exposures. The polymer surfaces were found to be relatively stable at exposure to an oxygen low-pressure plasma up to ca. 2 s. This is important information to get maximum adhesion to metals in composites. In correlation to their redox potentials, potassium, aluminium and chromium react with oxygen functional groups at the polymer/metal interface. In a dedicated study, chromium was found to attack aromatic rings and form different reaction products.
Technical waxes and paraffins were investigated using supercritical fluid chromatography (SFC), matrix-assisted laser-desorption/ionization mass spectrometry (MALDI-MS) and size-exclusion chromatography (SEC). SEC enables the simultaneous determination of molecular masses up to high values and molecular mass distributions. The resolution of homologous species, however, is poor. In this respect the use of SFC is advantageous. Proper resolution of homologues may be provided up to Mr~1200 without great difficulty. To compare these chromatographic results MALDI-MS was applied for the determination of molecular masses and mass distributions in technical waxes for the first time. Using reflectron mode excellent MALDI mass spectra could be achieved in the molecular mass range up to 1000 Da. The mean values of the molecular masses calculated by MALDI-MS were in sufficient agreement with those of SFC. In the linear mode of MALDI-MS molecular masses could be determined to nearly 3000 Da. Beyond this mass range SEC still remains the method of choice. Advantages and difficulties of the used methods are discussed in this paper.
Polyethylene foils, used as greenhouse foils stabilized with various types of sterically hindered amine light stabilizers (HALS), showed an extraordinary prolonged lifetime on exposure to natural or artificial weathering if a gas-phase fluorination under low-pressure conditions was applied. The fluorination was performed using F2/N2 mixtures and provided ca. 50 F/100 C (fluorination degree ap25%). The lifetimes of fluorinated PE foils on exposure to artificial or natural weathering were increased at least by a factor of 2-4 as measured in terms of tensile strength and elongation at break.
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
The hydrolytic degradation of technical poly(ethylene terephthalate) (PET) was investigated by means of different methods such as size-exclusion chromatography (SEC), viscometry, light-scattering, thin-layer chromatography, end-group titration, and matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS). The long-term degradation was simulated by exposing PET filament yarns to aqueous neutral conditions at 90°C for up to 18 weeks. By means of MALDI-MS and thin-layer chromatography, the formation of different oligomers was obtained during polymer degradation. As expected, an ester scission process was found generating acid terminated oligomers (H-[GT]m-OH) and T-[GT]m-OH and ethylene glycol terminated oligomers (H-[GT]m-G), where G is an ethylene glycol unit and T is a terephthalic acid unit. Additionally, the scission of the ester bonds during the chemical treatment led to a strong decrease in the number of cyclic oligomers ([GT]m). The occurrence of di-acid terminated species demonstrated a high degree of degradation.