Hydrolytic degradation and functional stability of a segmented shape memory poly(ester urethane)
(2009)
In order to understand the effects of water and hydrolytic ageing on semi-crystalline poly(ester urethane) and its shape memory functionality, water immersion experiments at elevated temperature have been performed on a model substance and various parameters were monitored: change of the melting/crystallisation temperatures, substantial increase in crystallinity, temperature dependence of the water diffusion coefficient and solubility, hydrogen-bonding index and phase mixing by peak deconvolution of the FT-IR carbonyl region and day-to-day tensile and thermo-mechanical cyclic tensile tests. A rising fraction of freezable water agglomerates in the polymer was found for specimens cooled from the immersion temperature. The degradation process could be divided into three phases: an induction phase, a phase of continuous degradation and a phase of accelerated degradation. Shape recovery remains fairly constant during phase one and decreases slowly during phase two. The increase in crystallinity in phase two is accompanied by an increase in shape fixing ability.
The German Federal Institute for Materials Research and Testing (BAM) has established a testing guideline to assess the suitability of geosynthetic or geocomposite drain (GCD) elements for final landfill cover systems. In an earlier paper the uniform procedure according to the BAM guideline for determining long-term water flow capacity was described, and the structural stability of drain cores under creep was investigated. The extrapolation of creep curves is permissible only when it can be shown, over the extrapolated period (at least 100 years), that oxidative aging does not invoke any relevant changes in the polyolefin material. This can be shown by measuring antioxidant depletion and mechanical degradation of the drain cores and filter/protection geotextiles in oven aging and water immersion tests. In this paper the results of such aging studies on three different GCD products are reported. Degradation of the tensile strength of HALS-stabilized polypropylene needle-punched nonwoven geotextiles (PP NWGTs) starts right from the beginning of the oven aging. This has to be taken into account for lifetime predictions based on residual tensile strength. The rate of oxidative degradation of NWGTs decreases significantly with increasing mass per area. Therefore the expected service life sets a limit on acceptable geotextile grammage. Antioxidant depletion in the drain cores, which are made of relatively thick PP strands or HDPE ribs, is about an order of magnitude slower than in filter and protection NWGTs, which are made of thin fibers. Service life values in excess of 100 years may be obtained for the products when the geotextiles and drain cores are properly stabilized and designed.